FORD ESB-M3G59-A-2012 TAPE WATERPROOF - PRESSURE SENSITIVE - WHITE TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD ESB-M3G58-A).pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 22 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.17, 4 1984 03 29 Revised Remove Thread Count CA01-CR524083 1963 06 21 Released AS1 No. 945 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 3 TAPE, WAT

2、ERPROOF - PRESSURE SENSITIVE BLACK ESB-M3G58-A TAPE, WATERPROOF - PRESSURE SENSITIVE WHITE ESB-M3G59-A 1. SCOPE The materials defined by these specifications are waterproof, pressure sensitive, cloth tapes. 2 APPLICATION Specification ESB-M3G58-A was released originally for tape used as a waterproof

3、 protective covering for large openings on inner door panels. Specification ESB-M3G59-A was released originally for tape used as a waterproof exterior protective covering along tacking strips on models equipped with light colored convertible tops. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUC

4、TION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 COLOR ESB-M3G58-A Black ESB-M3G59-A White 3.4 BACKING Waterproof fabric 3.5 BREAKING STRENGTH (ASTM D 1000, 508 mm/min rate of pull) 3.5.1 Dry 6.1 N/

5、mm width 3.5.2 Wet 6.1 N/mm width Test Method: Immerse specimens in distilled water at 23 +/- 2 C for 6 h. Remove, blot off excess water and pull immediately. 3.6 UNWIND PULL, max 613 N/m width Test Method: Place core of tape around a fixture which will allow it to revolve. Attach the free end of th

6、e tape to a 44.5 N maximum limit spring scale. Pull the tape from its roll at the rate of 305 mm/min. Measure and record the unwind pull as a direct scale reading. ENGINEERING MATERIAL SPECIFICATIONESB-M3G58-AESB-M3G59-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Pa

7、ge 2 of 3 3.7 ADHESION TO BACKING, min (ASTM D 1000, 305 mm/min rate of pull) ESB-M3G58-A 274 N/m width ESB-M3G59-A 164 N/m width 3.8 ADHESION TO STEEL, min 274 N/m width (ASTM D 1000) 3.9 ADHESIVE SOLUBILITY The adhesive shall be soluble in M-14J167 Special Spirits and M-14J147 Petroleum Light Naph

8、tha. 3.10 MOISTURE VAPOR TRANSMISSION RATE, max 5.6 g (FLTM BU 001-01) 3.11 WATER PENETRATION RATE, max 30 g (FLTM BU 001-02) 3.12 ACCELERATED AGING (Storage Stability) The adhesive shall show no signs of separating from its backing, nor loss in adhesion or tack. It shall not become a pasty or strin

9、gy mass. The backing shall not become brittle. Test Method: Apply 3 strips of tape side by side with the adhesive in contact with a glass plate 100 mm square. Lay three additional strips directly on top of each strip with the adhesive side of each strip in contact with the backing side of the under

10、piece. Press each layer of tape down smoothly by hand or by a roller. Place the plate with the test specimens in a relative humidity of 95 - 100 percent at temperature of 38 +/- 1 C for six days. After the exposure period, remove the specimens from the high humidity, allow to cool for 4 h at 23 +/-

11、2 C, and then examine layer by layer to determine the extent of adhesive deterioration. 3.13 FINISHED TAPE The tape shall be wound evenly on rolls so that the surface of the roll shall be free from depressions. The tape shall have no liner over the adhesive and shall unroll evenly and uniformly with

12、out unraveling. The adhesive material shall not separate from the backing so as to leave bare spots or show offsetting of the adhesive from one layer to another when the tape is unwound. When unwound from the roll, the tape shall remain reasonably flat with no tendency to curl transversely. The tape

13、 shall adhere snugly to work without wrinkling, curling, or buckling. The edges of the tape shall be straight, true and unbroken so as to provide sharp distinct boundaries to finished areas. The tape shall be wound on standard 75 mm cores. 3.14 WATERFASTNESS OF DYE Shall be waterfast Test Method: Vi

14、gorously shake a 100 mm strip of tape in 200 ml of distilled water at 23 +/- 2 C. Allow to stand in the water at 23 +/- 2 C for 6 h. Any discoloration of the water will be cause for rejection. ENGINEERING MATERIAL SPECIFICATIONESB-M3G58-AESB-M3G59-APrinted copies are uncontrolled Copyright 2005, For

15、d Global Technologies, LLC Page 3 of 3 3.15 MIGRATION STAINING None (FLTM BU 105-01, 72 h) 3.16 FUNCTIONAL APPROVAL Materials being evaluated for initial approval to this specification shall be subjected to a production trial. Functional trial results should be available to design and materials engineering prior to material approval and release.