FORD ESB-M6J123-C-2012 PRIMER SURFACER MICROCELLULAR URETHANE ELASTOMER TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 03 2012 05 14 N Status No usage or replacement N. Benipal, NA 2008 04 21 Revised Revised 4; Format Update 1982 02 10 Released CZM1-DR592195-1 RJD Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 3 PR

2、IMER SURFACER, MICROCELLULAR ESB-M6J123-C URETHANE ELASTOMER NOT TO BE USED FOR NEW DESIGN 1. SCOPE The materials defined by this specification are primer surfacers for use on molded urethane elastomer parts (microcellular or dense). 2. APPLICATION This specification was released originally for mate

3、rials used as primers on molded elastomeric substrates such as bumpers, ornaments or other exterior parts. Two types of primers are defined as follows: Type I Conductive Primer - Recommended when the enamel color coat is applied with electrostatic spray equipment. Type II Non-Conductive Primer 3. RE

4、QUIREMENTS (Requirements are for both Types I and II unless specifically stated otherwise.) 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 PHYSICAL PROPERTIES 3

5、.2.1 Viscosity (FLTM BI 111-01) The enamel viscosity value by color shall be established at I.S.I.R. Tolerance on subsequent batches shall be +/- 6 s #2 Ford Cup or +/- 3 s #4 Ford Cup. 3.2.2 Solids, min 19% (FLTM BI 102-01) The solids content is to be run on unreduced paint if its viscosity is lowe

6、r than 26 s #4 Ford Cup at 26 +/- 1 C. If the paints viscosity is higher, adjust the paint viscosity to 26 s #4 Ford Cup at 26 +/- 1 C with a solvent blend agreed to by the manufacturer and user. 3.2.3 Stability (FLTM BI 102-03) The material shall not liver or jell upon standing and must be free fro

7、m settling which is not dispersed by normal agitation. The viscosity of the material shall not increase more than 10 s. ENGINEERING MATERIAL SPECIFICATION ESB-M6J123-C Copyright 2012, Ford Global Technologies, LLC Page 2 of 3 3.3 PREPARATION OF TEST PANELS Prepare according to the following procedur

8、e: 3.3.1 Panels Use microcellular urethane panels of any convenient size, representative of production material. A smooth surface with no pits or blow holes is required. Solvent wipe panels clean before applying primer. 3.3.2 Primer Reduce to 13 - 22 s #4 Ford Cup using solvent recommended by suppli

9、er. Spray 21 - 30 m dry film thickness. Bake the panels to obtain a surface temperature of 121 C for 5 min or 107 C for 20 min. Do not sand. 3.3.3 Color Coat Apply ESB-M2J121-A Elastomeric Enamel (46 m min) and bake approximately 40 min at 121 C to obtain a surface temperature of 116 C for 25 min. 3

10、.4 APPEARANCE 3.4.1 Color As specified on the (FLTM BI 109-01) engineering release The primed test plaques as prepared in para 3.3 shall match the master color panels on file at B&CE. 3.4.2 Leveling The primer film shall level with a minimum of orange peel. The surface of the material under test sha

11、ll be equal to or better than current approved production material for smoothness when applied and baked under identical conditions. 3.4.3 Holdout There shall be no evidence of dulling or strike-in when enamel color coat is applied over unsanded primer. 3.5 FILM PROPERTIES 3.5.1 Adhesion (FLTM BI 10

12、6-01) Both primer adhesion to substrate and enamel adhesion to primer shall be satisfactory, with no chipping. 3.5.2 Electrical Conductivity (Type I only), min 125 (Ransburg Electro-Coating Corp. Model 236 Sprayability Meter or Equivalent) ENGINEERING MATERIAL SPECIFICATION ESB-M6J123-C Copyright 20

13、12, Ford Global Technologies, LLC Page 3 of 3 3.6 RESISTANCE PROPERTIES Primer with topcoat must meet all requirements of ESB-M2J121-A - Elastomeric Enamel - Exterior specification. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the require

14、ments of this specification. 4.1 FLASH POINT Below 26 C (ASTM D 92) 4.2 FLAMMABILITY This material represents a potential fire hazard. The Manufacturing Engineering Department shall notify both the Plant Security and the Safety Units of its presence in the Plant to assure that proper fire precaution

15、s are provided. The location in which it is used or stored shall be included in the notifications. 4.3 APPLICABLE SPECIFICATIONS Substrate ESB-M2D263 Primer ESB-M6J123 Enamels ESB-M2J121 and ESB-M2J218-A1/A2 4.4 This specification replaces and supersedes ESB-M6J123-A. When ESB-M6J123-A is shown on other documents, the requirements of this specification apply.