FORD ESB-M99J228-C-2005 CATALYST ACID ACRYLIC REPAIR ENAMELS (50 50 BLEND MONOBUTYL MALEATE MONOBUTYL PHOSPHATE) TO BE USED WITH FORD WSS-M99P1111-A 《丙烯酸系树脂修复瓷漆用酸性催化剂(马来酸一丁酯 磷酸一丁.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 09 13 Revised Inserted 3.0; deleted 3.7, 3.8, 3.9, 3.10, 3.11 and 4 1995 03 01 Revised Inactivated ESB-M99J228-A & ESB-M99J228-B 1963 11 05 Released AS1-1142 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Pa

2、ge 1 of 2 CATALYST, ACID-ACRYLIC REPAIR ENAMELS (50/50 BLEND, ESB-M99J228-C MONOBUTYL MALEATE/MONOBUTYL PHOSPHATE) 1. SCOPE The material defined by this specification is an acid catalyst solution. 2. APPLICATION This specification was released originally for material used to convert standard high ba

3、ke acrylic solution and non-aqueous dispersion (NAD) enamels to low bake enamels for repairing passenger and commercial vehicles. 3. REQUIREMENTS 3.1 SPECIFIC GRAVITY, 15.6/15.6 C 0.895 - 0.955 (ASTM D 891) 3.2 ACID NUMBER 155 - 240 (ASTM D 1467) 3.3 FLASH POINT, C, min 21 (ASTM D 56) 3.4 COMPOSITIO

4、N (Percent by Weight) Normal butyl alcohol 53 Xylo 9 Monobutyl maleate 27 Monobutyl phosphate 11 3.5 QUANTITY REQUIRED FOR CONVERSION 3 (% By Volume) 3.6 PERFORMANCE Appearance, gloss, hardness and intercoat adhesion of a catalyzed enamel applied over a high bake uncatalyzed enamel shall be satisfac

5、tory. Test Method: Determine performance of catalyst in ESB-M32J100 Acrylic Enamel, ESB-M50J100 NAD Enamel or both as applicable. Prepare 2 panels of uncatalyzed enamel (ZWFAXXA White, preferred) per FLTM BI 103-02, Method C. Scuff sand one-half of each panel, lengthwise. Two samples of the unreduce

6、d enamel are catalyzed per para 3.5, one with the catalyst under test and one with a previously approved batch of catalyst for control. Reduce each sample to spraying viscosity and apply 31 38 micrometers over one-half of a panel, crosswise, so that the catalyzed enamel is applied over the scuffed a

7、nd unscuffed portions of the high bake enamel (bake 20 minutes at 83 C). Test for appearance and gloss versus the uncatalyzed portion of the panel, hardness (approximately 20 Sward) and intercoat adhesion. The catalyst under test shall be equal to the control in all cases. ENGINEERING MATERIAL SPECI

8、FICATIONESB-M99J228-CPrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 FLAMMABILITY AND/OR TOXICITY This mate

9、rial represents a potential fire and/or health hazard. The Manufacturing Engineering Department shall notify both the Plant Security and the Safety Units of its presence in the Plant to assure that proper fire and/or health precautions are provided. The location in which it is used or stored shall be included in the notifications.