FORD ESB-M9H3-A-2006 FABRIC WOVEN BACKING FOR VINYL COATING - OSNABURG TO BE USED WITH FORD WSS-M99P1111-A (Shown on ESB-M9H1-A)《乙烯基涂层的粗袋布(OSNABURG)机织底衬织物 与标准FORD WSS-M99P1111-A.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 11 06 Revised ESB-M9H1-B, 2-B, 3-B, 4-B Inserted 3.0; Deleted 3.1, 3.9, 3.9.1, 3.9.2, 3.9.3, 3.11 & 4 R. Lord1978 11 22 Revised Metricated and Retyped CAHI-RD572066181 1963 07 26 Released ESB-M9H1-5A ASI-1004 Printed copies are uncontroll

2、ed Copyright 2006, Ford Global Technologies, LLC Page 1 of 3 FABRIC, WOVEN BACKING FOR VINYL COATING DRILL ESB-M9H1-A FABRIC, WOVEN BACKING FOR VINYL COATING OSNABURG ESB-M9H3-A 1. SCOPE These specifications were released initially for woven fabrics, cleaned, free from waste, and of good commercial

3、quality. 2. APPLICATION These materials were released originally as backing in the manufacture of vinyl coated fabrics and other trim applications as specified on engineering drawings. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must confo

4、rm to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 WIDTH As specified on the Purchase Order. In all cases, this figure shall be a minimum inside selvage dimension. 3.3 WEAVE Shall be the same as the sample approved for production by the Textile Engineering Sectio

5、n, BEPE Materials Engineering Department. 3.4 SIZING (FLTM AN 003-01) Shall not exceed the maximum indicated in the attached chart. 3.5 INJURIOUS ELEMENTS, max (ASTM D 377) Copper 0.001% Manganese 0.0005% In addition, chemicals such as caustic soda shall be completely removed so that discoloration d

6、oes not occur as the vinyl coated fabric passes through the processing ovens. ENGINEERING MATERIAL SPECIFICATIONESB-M9H1-A ESB-M9H3-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 3 3.6 DYE FASTNESS Shall impart no noticeable color to water. Test Method: Pla

7、ce 8 oz (237 ml) of distilled water (23 +/- 2 C) in a white paper cup. Saturate a 2 x 2 in (51 x 51 mm) dyed fabric test specimen in the water. Withdraw the specimen and squeeze it by hand so that the water drips back into the cup. Observe water in cup for noticeable color change. 3.7 DETAILED PROPE

8、RTIES See attached chart 3.8 SELVAGE Shall be of uniform and equal width on both edges of the fabric. The selvages shall be so made that the tension shall be the same as, and shall lie flat with the body of the cloth. Baggy goods and curling selvages shall be cause for rejection. 3.10 BONDING ASSEMB

9、LY In addition to the requirements listed above, bonding grade materials shall meet the following added requirements. 3.10.1 Material Acceptability The criterion for material acceptability shall be the assemblys job performance. This means that the materials composition and formulation must form a s

10、atisfactory bond to itself, as an overlay, and/or as an underlay when bonded separately and with the remaining approved components in the assembly and when bonded under approved production conditions. ENGINEERING MATERIAL SPECIFICATIONESB-M9H1-A ESB-M9H3-A Printed copies are uncontrolled Copyright 2

11、006, Ford Global Technologies, LLC Page 3 of 3 Yarn Size Yarn Count, min (ASTM D 1910) Tensile Strength (ASTM D 1682 Grab Method) Minimum “ESB“ No. Warp Fill Nominal Yield yd/lb (m/kg) Width in (mm) Weight FLTM BN 6-1/2 Oz/yd2(kg/m2) Minimum Ends Per in. (10 mm) Picks Per in. (10 mm) Lb (N) W F M9H1

12、-A 17 cc (35 tex) 14 cc (42 tex) 1.85 (3.74) 59 (1500) 4.2 (0.142) 68 (27) 37 (15) 76 (338) 42 (187) M9H3-A 16 cc (37 tex) 99 cc (66 tex) 2.35 (4.74) 59 (1500) 3.3 (0.112) 32 (13) 26 (10) 38 (169) 38 (169) *Note: The above yarn size, nominal yield and yarn count requirements may be used as a guide f

13、or procuring fabrics employed in the vinyl coating process. However, the remaining requirements are critical and must be fully met. All yarns are single ply. “SB“ No. Shrinkage (FLTM BN 105-01) % Trapezoid Tear Strength (ASTM D 5733) lb (N) Stretch & Set* (SAE J855) Stretch % Minimum or Range Set %

14、Maximum Sizing (FLTM AN 103-01) % Max. Warp Fill Warp Fill Warp Fill Warp Fill M9H1-A 6.0 6.5 5.5 (24) 5.0 (22) 2.0 4.5 3.0 7.0 1.0 M9H3-A 5.0 5.0 5.0 (22) 6.0 (27) 2 - 7 7 - 13 2.5 7.5 1.5 *Note: The above shrinkage, and stretch and set requirements may be used as a guide for procuring fabrics employed in the vinyl coating process. However, the remaining requirements are critical and must be fully met.