FORD ESE-M13P6-B2-2013 RESIN BONDED FLUOROCARBON COATING HIGH PERFORMANCE TO BE USED WITH FORD WSS-M99P1111-A (Shown on FORD ESE-M13P6-B1).pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 4 2013 10 25 N-Status N-Status for B1 and B2. No Replacement Named A. Wedepohl 2008 08 28 Revised Revised 2, Deleted 3.9, 3.10 Inserted 3.0 C. McComb, FNA 1978 10 04 ESE-M13P6-B1 use 1/2 in (13 mm) scratch and use tape from Method “B“) M

2、ust not flake, chip, or transfer film to tape. 3.5 CURE TEST AND SOLVENT RESISTANCE No softening of the coating or evidence of color rubbing off when a cloth dipped in MEK is rubbed twice over the surface of the coating. ENGINEERING MATERIAL SPECIFICATION ESE-M13P6-B1/B2 Copyright 2013, Ford Global

3、Technologies, LLC Page 2 of 3 3.6 PANEL TESTING Tests shall be conducted on coated panels of low carbon steel (ESE-M1A140-A) conforming to para 3.1 through 3.5. 3.6.1 Salt Spray 500 h (ASTM B 117) Panels must meet a rating of no lower than #7 per ASTM D 1654, Schedule No. 2. 3.6.2 Coefficient of Fri

4、ction, max 0.12 (FLTM BQ 13-1) Static i.e. using coated test specimen and omitting oils, test run at room temperature until coating wear is indicated by kinetic coefficient of friction reaching 0.30. 3.8 FINISHED PART Parts must meet para 3.1 through 3.5, other requirements when required shall be sp

5、ecified on the engineering drawings or engineering specification for parts with this coating (as configuration permits). 3.8.1 Salt Spray 300 h (ASTM B 117) (Approval - ISIR) 96 h (Lot certification per Q-101) Parts must meet a rating of no lower than #7 per ASTM D 1654, Schedule No.2. The above req

6、uirements for both thickness and salt spray apply only to significant surfaces. The specified coating thickness shall be required only on such surfaces of parts other than threads or holes, as can be touched by a sphere 0.5 in (13 mm) in diameter, unless otherwise noted on drawings. On other surface

7、s such as those of holes, recesses, threads, etc., where a controlled deposit cannot be obtained under normal coating conditions, the above requirements do not apply. Acceptance or rejection of parts submitted to this specification will be based on thickness and salt spray results on significant sur

8、faces. ENGINEERING MATERIAL SPECIFICATION ESE-M13P6-B1/B2 Copyright 2013, Ford Global Technologies, LLC Page 3 of 3 5. GENERAL INFORMATION The material data included herein is for information only and is not a requirement for the supplier. 5.1 OPERATING TEMPERATURE, C ESE-M13P6-B1 ESE-M13P6-B2 Conti

9、nuous 149 204 Intermittent 177 260 5.2 SELECTION OF COATING ESE-M13P6-B1: This coating is recommended for applications requiring low friction and good resistance to sliding wear. Also, where corrosion resistance is of primary concern along with possible identification of parts by color coding. Coating available either by spraying or dipping. ESE-M13P6-B2: This coating is recommended for applications requiring low friction and optimum resistance to sliding and abrasive wear. This coating is available in black only and applied only by spray.