FORD ESE-M2C160-A-2009 LUBRICANT SOLID FILM - SOLVENT CARRIED TO BE USED WITH FORD WSS-M99P1111-A 《溶剂承载型固态膜式润滑剂 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 10 26 N-STATUS No known use. No Replacement Named D. DiGregorio, NA 2004 05 19 Revised Para 3.0 inserted; para 3.8 & 4 deleted 1980 05 01 Released CE3K-DR742543-E Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, L

2、LC Page 1 of 1 LUBRICANT, SOLID FILM - SOLVENT CARRIED ESE-M2C160-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a solid film lubricant consisting of molybdenum disulfide in a solvent carrier which dries by reaction with air. It is intended for reduction of fr

3、iction of metal-to-metal contact. Additionally, coating of parts by molybdenum disulfide provides resistance to corrosion. 2. APPLICATION This specification was released originally for material used to coat linkage parts of carburetors, or other metal parts which require lubrication but cannot be pr

4、otected from dust or water. 3. REQUIREMENTS (When applied to sheet steel surfaces) 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 FILM CHARACTERISTICS Shall for

5、m a continuous, homogeneous coating of uniform thickness, free of cracks, blisters and foreign material. 3.2 APPLICATION CHARACTERISTICS Shall be suitable for application, after agitation, by brushing, spraying or dipping at all room temperatures. 3.3 TOXICITY Shall not contain chlorinated solvents

6、or other compounds of known high toxicity under normal conditions of usage. 3.4 COLOR Dull charcoal gray to black 3.5 FILM THICKNESS, min 0.002 mm 3.6 DRYING TIME Non-tacky in 15 minutes 3.7 SOLIDS, BY WEIGHT, min 7% (98% of particles less than 1 micron diameter) 3.7.1 Molybdenum Disulfide (MoS2), by 5% weight, min 3.7.2 Graphite, by weight, min 2%