FORD ESE-M99J289-A-2012 LABEL VINYL PRESSURE SENSITIVE TO BE USED WITH FORD WSS-M99P1111-A 《乙烯基压敏材料制成的标签 与福特WSS-M99P1111-A 一起使用》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev 03 2012 02 16 N Status No replacement named N. Benipal, NA 2006 03 08 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.11, 4 1976 01 12 Released Controlled document at www.MATS Copyright 2012, Ford Global Technologies, LLC Page 1 of 2 LABEL, VIN

2、YL, PRESSURE SENSITIVE ESE-M99J289-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a pressure sensitive flexible vinyl film for interior use. 2. APPLICATION This specification was released originally for label material applied to the sun visor to provide four-w

3、heel drive and transmission shift information. The film is applied to the vinyl sun visor surface by removing the paper backing and pressing firmly into place. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. 3.0 STANDARD REQUIREMENTS FOR PRO

4、DUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 THICKNESS - WITHOUT RELEASE PAPER 0.090 - 0.125 mm (ASTM D 1000) or as specified on engineering drawing 3.4 APPEARANCE Shall be free from streaks,

5、 blisters, wrinkles, ragged edges and any other surface imperfections which will make them unsuitable for the intended usage. The design and color shall be as specified on the engineering drawing. 3.5 TENSILE STRENGTH, min 1 kN/m (ASTM D 1000) 3.6 PREPARATION OF LABELS ON TEST PANELS Except where ot

6、herwise noted, tests shall be conducted on vinyl coated fabric test panels. With firm hand pressure, apply a 25 x 75 mm strip of label to a test panel of suitable size. The applied label must be free of all wrinkles and trapped air bubbles. The label film shall be applied at 23 +/- 3 C and condition

7、ed for 48 h at a relative humidity of 50 +/- 5% at 23 +/- 3 C. 3.7 ADHESION, min 0.22 kN/m (ASTM D 1000, Method A, 180 peel) ENGINEERING MATERIAL SPECIFICATION ESE-M99J289-A Copyright 2012, Ford Global Technologies, LLC Page 2 of 2 3.8 THERMAL CYCLE TEST Label shall exhibit no wrinkling, cracking, c

8、olor change or curling of edges after the specified 4 cycles of testing. At the end of the 4 cycles, adhesion must meet the requirements stated below. 3.8.1 Adhesion, min 0.07 kN/m Test Method: Prepare test panels per para 3.6. Expose the panels for 1 h at 100 +/- 3 C, then cool to -29 +/- 3 C for 1

9、 h. Repeat for a minimum of 4 cycles. 3.9 HUMIDITY RESISTANCE No wrinkling, cracking, color change, curling of edges or loss in readability. 3.9.1 Adhesion, min 0.075 kN/m Test Method: Prepare test panels per para 3.6. Place test panels in humidity cabinet maintained at 98 +/- 2% relative humidity a

10、nd 38 +/- 3 C for 400 h. 3.10 WEATHERING RESISTANCE (FLTM BO 101-01, 400 h minimum) Prepare test samples per para 3.6. The label shall show a minimum degree of fading, chalking or dulling. No increase of brittleness and shall be completely free from evidence of cracking, checking, blistering or peeling. 3.10.1 Adhesion, min 0.075 kN/m