FORD ESF-M11P5-A-2013 ADHESIVES INTERIOR APPLIQUE TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2013 12 11 N Status No replacement named L. Sinclair, NA 2007 06 26 Revised Inserted 3.0 1965 01 05 Released F6-1474 Controlled document at www.MATS Copyright 2013, Ford Global Technologies, LLC Page 1 of 2 ADHESIVES, INTERIOR APPLIQUE ESF-M1

2、1P5-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines the performance of a pressure sensitive adhesive as applied to interior appliques. 2. APPLICATION This specification was released originally for material used for interior automotive decorative trim panels, to be applied to inst

3、rument cluster housings. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 BOND AND STRIPPING STRENGTH - INITIAL (ASTM D 903, except 90 peel on a 0

4、.5 in (13 mm) wide strip) The applique, as received, shall have a minimum bond strength of 2 lb (8.9 N) to initiate separation and a minimum continuing stripping strength of 1 lb (4.5 N), after being bonded to its substrate or test panel, and allowed to cure at room temperature for 72 h. The test pa

5、nel shall have a painted for vacuum metalized surface, or be an “as molded“ plastic. The applique shall show no evidence of lifting after application and prior to bond test. 3.2 BOND AND STRIPPING STRENGTH - CONDITIONED (ASTM D 903, except 90 peel on a 0.5 in (13 mm) wide strip) The applique, after

6、application per para 3.1, shall have a minimum bond strength of 2.5 lb (11.2 N) to initiate separation and a minimum continuing stripping strength of 1 lb (4.5 N), after completing the following cycle of environmental conditions. . 24 h at 82 +/- 1 C. . 3 h at 23 +/- 1 C. . 24 h at -29 +/- 1 C. . 3

7、h at 23 +/- 2 C. . 4 h at 38 +/- 3 C in 20 - 25% relative humidity. . 4 h at 23 +/- 2 C in 90 - 95% relative humidity. . 24 h in salt spray (ASTM B 117). ENGINEERING MATERIAL SPECIFICATION ESF-M11P5-A Copyright 2013, Ford Global Technologies, LLC Page 2 of 2 The applique shall show no evidence of lifting after application or at any time in the cycle, prior to bond test. 3.3 QUALITY The adhesive shall have no adverse effect upon the substrate such as crazing, softening, or discoloration.