FORD ESF-M2G156-A2-2014 ADHESIVE EPOXY ONE PART THIXOTROPIC TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2014 12 08 N Status No replacement named L. Sinclair, NA 2003 01 23 Revised Para 3.0 inserted ; Para 3.1, 3.2, 3.3, 3.7, 3.8, 4 deleted 1990 07 11 DE00E00107002060 Released Page 1 of 2 Copyright 2014, Ford G

2、lobal Technologies, Inc. ADHESIVE, EPOXY, ONE PART, THIXOTROPIC ESF-M2G156-A2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a one-part thixotropic epoxy adhesive. 2. APPLICATION This specification was released originally for a material used where adhesion of ny

3、lon to steel is required, such as bonding the rotor coil to the pole pieces in the alternator rotor. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A).

4、3.4 THIXOTROPY AND CURE TIME Test Method: Support a piece of 55 x 71/100 mm mesh flyscreen so that the center area is open. Placing the screen over the open end of a 1/2 L can is a satisfactory method. Cut a 25 mm diameter hole in the center of a piece of 3 mm thick material. This may be a metal or

5、non-metal. Place 3 mm plate on top of flyscreen. Fill the hole in the plate with resin until it is slightly over full. Scrape off excess resin and remove the plate by lifting it straight up. This should leave a 3 mm thick by 25 mm diameter wafer of approximately 4 g. Place the resin and flyscreen in

6、 an air circulating oven which is at 150 +/- 2 C for 30 minutes. The flyscreen should be supported so it is away from the bottom of the oven. After cure, remove from the oven and allow to cool. The resin may pass through the screen slightly, but must not drop off. Check hardness of cured epoxy (Rock

7、well “M“ 70 min). 3.5 SHEAR STRENGTH (ASTM D 1002) 3.5.1 Steel to Steel, min 18.0 MPa Test Specimen Preparation and Procedure: CRLC steel test coupon 25 x 100 x 1.5 mm. If material exhibits any surface oxidation acid etch (10 % HCL) until visibly clean. Vapor degrease and wipe surface with acetone.

8、Apply 0.25 mm wet film of adhesive 6 mm overlap. Cure as above under 4.4 N load. Test at 1.3 mm/minute. ENGINEERING MATERIAL SPECIFICATION ESF-M2G156-A2 Page 2 of 2 Copyright 2014, Ford Global Technologies, Inc. 3.5.2 Nylon to Steel, min 2.1 MPa Same as above but bond nylon Type 66 tensile bar to st

9、eel coupon in place of steel to steel. 3.6 SHELF LIFE Material must meet requirements of para, 3.2 (WSS-M99P1111-A), 3.4, 3.5, and be able to be dispensed as well as it was when originally received after 6 months at 15.5 - 27 C. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 SAFETY This material represents a potential health hazard. Manufacturing Engineering should notify the Safety Department of its presence in the plant.