FORD ESF-M4D511-A-2006 POLYAMIDE (PA) 66 PLASTICIZED - HIGH TEMPERATURE RESISTANT MOLDING COMPOUND TO BE USED WITH FORD WSS-M99P1111-A (Use WSK-M4D648-A)《增塑聚酰胺66耐高温成型料 与标准FORD W.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2006 04 28 N-STATUS Replaced by WSK-M4D648-A A. Reaume/M. Masserant 2005 05 31 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.7, 3.8 & 4 1985 08 27 Released 888002-300 Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Pa

2、ge 1 of 2 POLYAMIDE (PA) 66, PLASTICIZED, HIGH TEMPERATURE ESF-M4D511-A RESISTANT MOLDING COMPOUND NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a heat stabilized, plasticized type 66 polyamide (nylon) molding compound. 2. APPLICATION This specification was rel

3、eased originally for material used for speedometer cables. NOTICE: This material absorbs and retains moisture. Part design and tolerances must accommodate changes in part dimensions and physical properties due to moisture absorption or loss in the service/assembly environment. Information on this ma

4、terial with respect to moisture should be obtained from the responsible PEO Materials Engineering Department. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P

5、1111-A). 3.3 CONDITIONING AND TEST CONDITIONS All test values indicated herein are based on material and specimens with moisture content not exceeding 0.3% (test according to ISO R 960, Method B/ASTM D 789). All test materials immediately after processing have to be sealed in containers that are imp

6、ermeable to water vapor. If the moisture content exceeds 0.3%, condition the material for a minimum of 16 h at 40 - 50 C at a reduced pressure below 133 kPa. Conduct tests in a controlled atmosphere of 23 +/- 2 C and 50 +/- 5% relative humidity. Individual specimens shall not be removed from closed

7、containers until immediately before testing. 3.4 HEAT STABILIZER ADDITIVE Ford Motor Company, at its option, may conduct following heat stabilizer additive test on material/parts supplied to this specification. The stabilizer must be present. Test Method: Ash 1 g sample in a covered porcelain crucib

8、le (size 17H is suitable) using a muffle furnace at a temperature of 500 - 520 C. Be certain temperature does not exceed 530 C. Overheating will volatilize the stabilizer. Allow the crucible to cool to room temperature and then add 1 - 2 cc of 5 molar hydrochloric acid, swishing to wash sides of cru

9、cible with acid. Evaporate to dryness, preferably on a steam bath or by very gentle heating with a low flame. Do not overheat. ENGINEERING MATERIAL SPECIFICATIONESF-M4D511-A Printed copies are uncontrolled Copyright 2006, Ford Global Technologies, LLC Page 2 of 2 Dissolve the stabilizer by warming i

10、n 3 - 4 drops of distilled water. Note: Greenish yellow color may occur at this point, which indicates the presence of a heat stabilizer. If the color does not occur, proceed as follows. Withdraw by means of a capillary tube and place on a piece of #40 Whatman filter paper. Add directly 2 - 3 drops

11、of a 5% solution of benzoin oxime in absolute ethanol (color complexing agent). Hold the filter paper over concentrated ammonium hydroxide for 2 min. A faint greenish yellow color indicates the presence of a heat stabilizer. It is imperative to use controls of stabilized and non-stabilized nylons, b

12、ecause color is weak and can be interpreted incorrectly. It is also very important to avoid any possibility of contamination. 3.5 MOLDING COMPOUND 3.5.1 Melting Point 250 - 265 C (ASTM D 789)3.6 MOLDED TEST SPECIMEN 3.6.1 Preparation of Test Specimens Unless otherwise specified all tests shall be ca

13、rried out on injection molded test specimens. The specimens shall be prepared according to ISO 294/ASTM D 1897. No annealing allowed. 3.6.2 Density 1.08 - 1.10 g/cm3(ASTM D 792)3.6.3 Tensile Strength, min 40 MPa (ASTM D 638, Type I specimen, 3.2 mm thick, 50 mm/min test speed) 3.6.3.1 Elongation, ul

14、timate, min 200% 3.6.4 Impact Strength, Izod, min 180 J/m (ASTM D 256, 3.2 mm thick specimen) 3.6.5 Heat Deflection Temperature, min (ASTM D 648, 127 x 12.7 x 6.4 mm specimens) 3.6.5.1 At 0.45 MPa 150 C 3.6.5.2 At 1.82 MPa 50 C 3.6.6 Heat Stability (ASTM D 3045, 84 h at 204 +/- 2 C) Tensile Strength, min 30 MPa (Test Method according to para 3.6.3) 3.6.7 Flexural Modulus, max 1.2 GPa (ASTM D 790, Method I, Procedure A, 6.4 mm thick specimen, 100 mm span)