1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 08 12 N-STATUS No known use. No Replacement Named C. Mracna, NA 2004 06 29 Revised Para 3.0 inserted; para 3.3 & 4 deleted 1979 02 19 Released IR-834834-P121 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Pa

2、ge 1 of 3 OIL SEAL, SILICONE RUBBER - INCREASED TEAR ESP-M2D96-C STRENGTH - IMPROVED REVERSION RESISTANCE NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a silicone rubber suitable for high temperature service conditions, possessing increased tear strength and im

3、proved reversion resistance. 2. APPLICATION This specification was released originally for material used as a rotating shaft oil seal in automotive automatic transmissions. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Co

4、mpanys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 SLAB STOCK PROPERTIES (ASTM D 3182) All seals and test samples, except slabs for tear resistance, shall be prelubed as follows: Material shall be immersed in ASTM No. 3 oil with no more than 2% rust inhibitor to be added. Th

5、e time and temperature is to be optional for each vendor to meet the limits of the specification. 3.1.1 Original Properties Tensile Strength, min 4.5 MPa (ASTM D 412, Die “C“) Elongation, min 100% Hardness - Durometer “A“ 70 - 80 (ASTM D 2240) Tear Strength, min 18 kN/m of (ASTM D 624, Die “B“, unlu

6、bricated thickness slab material) 3.1.2 Heat Aged (ASTM D 865, 70 h at 177 +/- 3 C, aluminum block) Tensile Strength Change, max -20% Elongation Change, max -45% Hardness Change, max +12 ENGINEERING MATERIAL SPECIFICATIONESP-M2D96-C Printed copies are uncontrolled Copyright 2009, Ford Global Technol

7、ogies, LLC Page 2 of 3 Bend Test No cracks when bent flat against itself 3.1.3 Immersion in ASTM No. 1 Oil (ASTM D 471, 70 h at 163 +/- 3 C, Method “A“, aluminum block) Tensile Strength Change, max -15% Elongation Change, max -15% Volume Change -5 to +1% (To be determined on typical seals in additio

8、n to slab stock from same batch of material for establishment of limits per para 3.2.1) Hardness - Durometer “A“ Change, max -5 Bend Test No cracks when bent flat against itself 3.1.4 Immersion in ASTM No. 3 Oil (ASTM D 471, 70 h at 163 +/- 3 C, Method “A“, aluminum block) Tensile Strength Change, m

9、ax -30% Elongation Change, max -25% Volume Change, max +35% (To be determined on typical seals in addition to slab stock from same batch of material for establishment of limits per para 3.2.2) Hardness - Durometer “A“ Change, max -25 Bend Test No cracks when bent flat against itself 3.1.5 Immersion

10、in Ford Approved Automatic Transmission Fluids, ESW-M2C33-F and/or ESP-M2C138-CJ. (ASTM D 471, 70 h at 163 +/- 3 C, Method “A“, aluminum block) Tensile Strength Change, max -70% Tensile Strength, min 2.1 MPa Elongation Change, max -25% Volume Change, max +35% Hardness - Durometer “A“ Change, max -30

11、 Bend Test No cracks when bent flat against itself ENGINEERING MATERIAL SPECIFICATIONESP-M2D96-C Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, LLC Page 3 of 3 3.1.6 Cold Test at -40 C Shall not crack (FLTM BP 106-03) on flexing Condition samples prior to cold test per the

12、 following method: Immerse samples in ASTM No. 1 oil at 163 +/- 3 C for 70 h. Remove samples from ASTM No. 1 oil, place in “bent loop“ test fixture and condition in cold chamber at -40 +/- 1 C for 5 h prior to flexing. 3.1.7 Reversion Test No reversion (as determined by smear test) after aging 240 h

13、 at 163 +/- 3 C in each factory fill qualified automatic transmission fluid ESW-M2C33-F and ESP-M2C138-CJ (ASTM D 471, para. 6.1, aluminum block). Smear test shall consist of sliding an aged compound across a section of white cardboard under approximately 18 N (4 lb) thumb force. Color smear shall b

14、e no greater than that produced by sliding of unaged compound across an identical section of white cardboard under the same, 18 N (4 lb), thumb force. Reversion resistance to be determined on actual seals in addition to slab stock. 3.2 SEAL PROPERTIES (Material control) 3.2.1 Immersion in ASTM No. 1

15、 Oil (ASTM D 471, 70 h at 163 +/- 3 C, Method “A“, aluminum block) Volume Change Within +/- 2.5% points of the percent change obtained on actual seals during original qualification under para. 3.1.3. The percent change to which these limits are applied for control purposes shall be established from

16、the qualification test results by agreement between purchaser and supplier. The weight of seal stock for volume change determination shall be 0.4 g minimum. In some instances this will require several small seal samples to be used as the test specimen. Bend Test No cracks when bent flat against itse

17、lf 3.2.2 Immersion in ASTM No. 3 Oil (ASTM D 471, 70 h at 163 +/- 3 C, Method “A“, aluminum block) Volume Change Within +/- 3.5% points of the percent change obtained on actual seals during original qualification under para. 3.1.4. The percent change to which these limits are applied for control purposes shall be established from the qualification test results by agreement between purchaser and supplier. Bend Test No cracks when bent flat against itself