FORD ESW-M4P5-A-2008 ANODIZE ALUMINUM - SULPHURIC ACID TYPE TO BE USED WITH FORD WSS-M99P1111-A 《经阳极化处理的铝用硫酸型清理剂 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 11 06 N-STATUS No Replacement A. Wedepohl, FNA 2003 08 27 Revised Para 3.0 inserted 1964 03 10 Released CPS-438009 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, Inc. Page 1 of 1 ANODIZE, ALUMINUM - SULPHURIC AC

2、ID TYPE ESW-M4P5-A NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines an electrolytic, sulphuric acid surface treatment for aluminum alloy parts, especially automatic transmission parts. 2. APPLICATION This specification was released originally for a surface hardening conversion coati

3、ng to increase wear resistance and avoid embedding of particles in bearing or sliding surfaces. Corrosion resistance is not the primary aim of this treatment although some resistance to corrosion is obtained. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and p

4、art producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 The method used shall be an electrolytic treatment in a sulphuric acid solution, with the part forming the anode. Other details of procedure are not limited by this specification, any meth

5、od being acceptable which will produce a satisfactorily hardened wear resistance surface equivalent to, or better than, that of the approved standard sample. A recommended procedure is outlined in Process Standard PL-52-02, Anodizing Aluminum, Sulphuric Acid Method. 3.2 COATING The coating shall be continuous and uninterrupted on all significant surfaces.