FORD SK-M1J9561-A-2010 DECORATIVE PAINT AIR DRYING BLACK TO BE USED WITH FORD WSS-M99P1111-A 《黑色晾干式装饰漆 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 07 27 Re-Activated Material will still be used in South Africa on J97 and T6 vehicles L. Sinclair, NA2010 03 16 INACTIVE No replacement named L. Sinclair, NA 1980 01 21 Released SM/EQ 8611 TP Printed copies are uncontrolled Copyright 2010

2、, Ford Global Technologies, LLC Page 1 of 5 DECORATIVE PAINT, AIR DRYING, BLACK SK-M1J9561-A 1. SCOPE The material defined by this specification is a semigloss black, air drying paint suitable for application on automotive finishes. 2. APPLICATION The material is used as specified by the responsible

3、 Engineering System for decorative painting of interior and restricted exterior body areas non-visible or partially visible e.g wheel house, lower flange of rocker panel. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Comp

4、anys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.1 COMPOSITION 3.1.1 Vehicle Physical drying synthetic resins, if necessary in combination with nitrocellulose and suitable plasticizers. 3.1.2 Toxicity Contents of toxic components, e.g. benzene, chlorinated hydrocarbons, lead c

5、ompounds etc., shall conform to the safety regulations currently prevailing in the plant and/or country where the material shall be used. The use of cadmium is prohibited. 3.2 PHYSICAL PROPERTIES 3.2.1 Non-Volatile (FLTM BI 102-01) According to initial sample report +/- 1.0%. 3.2.2 Package Viscosity

6、 (FLTM BI 111-01) According to initial sample report +/- 5 s FC-4, 25 C but minimum 90 s FC-4, 25 C. ENGINEERING MATERIAL SPECIFICATIONSK-M1J9561-A Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 2 of 5 3.2.3 Density (ASTM D 1475) According to initial sample report

7、 +/- 0.02 3.2.4 Flash Point The flash point shall conform to the safety regulations applicable to the plant and/or country where the material shall be used. 3.2.5 Compatibility The material must be of such compatibility that it can be reduced with S-M14J19-A (nitro thinner). 3.2.6 Hiding Power Dry (

8、FLTM EU-BI 001-05) Reducer S-M14J19-A Viscosity 20 s FC-4/25 C Complete visual hiding over substrate at a maximum dry film thickness of 10 micrometre. 3.2.7 Shelf Stability During a storage of 3 months at room temperature the material as received shall not gel or liver upon standing and must be free

9、 from settling which cannot be dispersed by normal agitation. The viscosity of the material shall not increase in excess of 40 seconds when tested according to FLTM EU-BI 2-3. 3.3 PREPARATION OF TEST PANELS (FLTM BI 103-02, section Bb) 3.3.1 Stone Peck Protective SK-M99J9587-A/B (If applicable) Afte

10、r electrocoat bake one half of the test panels to be treated as follows: Application of stone peck resistant material SK-M99J9587-A/B to a dry film thickness of approximately 100 +/- 10 micrometer by suitable spray method. After a flash off time of 1 minute spray a full hiding coat (approximately 20

11、 micrometer of SK-M6J9556-A or approved equivalent, spray primer of current production. After 3 minutes flash off time bake according to material specification requirements; further process of top coat application according to FLTM BI 103-02, Method Bb. ENGINEERING MATERIAL SPECIFICATIONSK-M1J9561-A

12、 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 3 of 5 3.3.2 Baking Enamels to be used 3.3.2.1 S-M32J100-E a) Lightest and darkest solid color of each manufacturer supplying to the plant where SK-M1J9561-A is intended for use. b) Lightest and darkest metallic colo

13、r of manufacturer supplying to the plant where SK-M1J9561-A is intended for use. 3.3.2.2 S-M32J110-A/111-A/9553-A Silver metallic base coat and clear top coat of that manufacturer supplying to the plant where SK-M1J9561-A is intended for use. 3.3.2.3 Baking conditions for baking enamels according to

14、 3.3.2.1 and 3.3.2.2. For all tests bake according to Material Specification. For gravelometer test prepare one additional panel which has been additionally overbaked for 10 minutes at 140 C metal temperature. 3.3.3 Application of SK-M1J9561-A 1 hour after enamel baked panels are treated as follows:

15、 Dilute SK-M1J9561-A with S-M14J19-A to spray viscosity (20 s FC-4/25 C or as recommended by vendor). Apply material under test to a dry film thickness of 15 20 micrometer, using pneumatic spray equipment. 3.4 AGEING OF TEST PANELS Prior to testing panels, they have to be aged as follows. 3.4.1 Pane

16、ls for resistance to wax and dewax materials: 6 hours at room temperature 3.4.2 Additional test panel for abrasion resistance 10 minutes at 100 C metal temperature. 3.4.3 All other panels: 7 days at room temperature ENGINEERING MATERIAL SPECIFICATIONSK-M1J9561-A Printed copies are uncontrolled Copyr

17、ight 2010, Ford Global Technologies, LLC Page 4 of 5 3.5 APPEARANCE 3.5.1 Color and Gloss (FLTM BI 109-01/BI 110-01) Shall match approved master sample. 3.6 FILM PROPERTIES 3.6.1 Drying Dust free after 2 minutes Dry to handle after 10 minutes 3.6.2 Adhesion No chipping (FLTM BI 106-01, Method B) 3.6

18、.3 Scratch Resistance Test The test shall be conducted similar to the crockmeter test FLTM BN 107-01. Clamp a ball bearing ball (steel) of 10 mm diameter (Ford part number 154.5435) with the prescribed dry cotton fabric under the cylindrical wooden or plastic pin so that the ball is covered smoothly

19、 by the cotton fabric and fixed simultaneously. The specimen shall be placed under the prepared pin. The pin shall be moved 1 time one direction across the test specimen at the rate of approx 100 mm per second. No scratch mark permitted Prior to each test the cotton fabric shall be replaced. 3.6.4 P

20、encil Hardness, min H (FLTM BI 151-01) To be performed on the half of the test panel without SK-M99J9587-A/B Remove pencil graphite with a soft rubber prior to estimation. 3.6.5 Quality The material shall air dry to a serviceable film showing no craters or pinholes. The material shall have reasonabl

21、e tolerance for cleaning procedures. 3.7 RESISTANCE PROPERTIES 3.7.1 Water Resistance 240 h (FLTM BI 104-01) No blistering, softening or dulling. ENGINEERING MATERIAL SPECIFICATIONSK-M1J9561-A Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, LLC Page 5 of 5 3.7.2 Chipping re

22、sistance, max Rating 3 (FLTM EU BI 007-01) Test panels according to 3.3.2.3, 3.4.2 and 3.4.3. 3.7.3 Resistance to Water and Soap Spotting (FLTM BI 113-01) No change of color and/or gloss. 3.7.4 Resistance to Acid Spotting (FLTM BI 113-02) No change of color and/or gloss. 3.7.5 Resistance to Applicab

23、le Wax and Dewax Materials Application of wax preservative after 6 hours ageing at room temperature and the removal of the preservative after a further 72 hours by any current dewax compound shall have no deleterious effect upon the quality or appearance of the paint film. 3.7.6 Weathering Resistanc

24、e Test panels shall show a minimum degree of fading, chalking, dulling or color change. No increase of brittleness nor loss of adhesion is permitted and the test panel shall be completely free from evidence of cracking, checking, blistering, peeling or rusting after exposure as follows: Florida Expo

25、sure (Miami Area) 12 months at 5 facing south. Evaluation of this test for information only. 3.7.7 Temperature Cycling Test Test panels prepared according to section 3.3 shall be subjected 3 times to the following cycle. 3 h at + 80 +/- 2 C 1 h at room temperature 3 h at - 40 +/- 2 C 1 h at room temperature 16 h + 38 +/- 2 C, 98 +/- 2% relative humidity After last cycle leave test panels at room temperature for 3 to 4 hours prior to evaluation. No cracking or other surface deterioration caused by the material under test. Adhesion must fulfill requirements of section 3.6.2.