FORD SK-M99G9505-A-1994 DEADENER POLYURETHANE MOLDED《模制聚氨酯隔音材料》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Release No. Released1994 12 16 Revised and Retyped, was 10 pages1973 09 24 A/CX 9904 KP #1 ReleasedWP 3948-a Page 1 of 5 PU-MOLDED PART FOR SOUND ABSORPTION SK-M99G9505-A1. SCOPEThe mate rial defined by this specification is a

2、 flame resistant moldedpolyether base polyurethane foam with closed skin on the entire surface.2. APPLICATIONThis m aterial is used as a sound absorption pad in the engine compartmentand is adhered with adhesive ac cording to S-M2G4610-A to the underneath ofthe hood and/or other applications as spec

3、ified on the E ngineering Drawing.3. REQUIREMENTSNot e: The material shall be conditioned for a minimum of 24 h at 23 +/-2 C and 50 +/ - 5 % relative humidity prior to test and tested under thesame conditions.3.1 COLORGrey or as specified on the Engineering Drawing.3.2 THICKNESS(ASTM D 1564)Between

4、10 mm and 38 mm according to the Engineering Drawing.3.3 DENSITY 40 - 70 kg/m3(ISO 1855, with surface skin)3.4 TENSILE STRENGTH(ISO 1798)3.4.1 Original, min 80 kN/m23.4.4.1 Elongation at Break, min 100 %3.4.2 After Humidity Ageing(ISO 2440, 3 h 105 C)Maximum - 30 %, based on measured original value.

5、ENGINEERING MATERIAL SPECIFICATIONSK-M99G9505-AWP 3948-b Page 2 of 5 3.4.3 After Heat Ageing(ISO 2440, 22 h, 140 C)Maximum - 30 %, based on measured original value.3.5 ADHESION OF SKIN TO FOAM, min 4 N/25 cmTest Method:1) Cut into the skin of the material under test an area of 25 x250 mm with a razo

6、r blade.2) Cover the area with tape accor ding to SK-M3G9500-A and press downfirmly.3) Remove t he tape from test piece in a tensile testing machine atan angle of 180 deg and a test speed of approx 500 mm/minute.3.6 RESISTANCE OF SKIN TO VARIOUS TEST REAGENTSThe coating shall not dissolve or exhibit

7、 tackiness when rubbedlig htly for 15 seconds with a cotton cloth soaked with each of thefo llowing test reagents. Use a separate specimen for each testreagent.1) Petrol, Premium grade2) Oil No 1, ASTM D 4713) Ford Longlife coolant(50 % mixture in water)4) Toluene3.7 FLAMMABILITY S elf-extinguishing

8、(FLTM EU-BN 24-1, 15 s)3.8 ADHESION TO PAINTED METALThere shall be no loss of adhesion, no evidence of skin or foamdeterioration when tested as follows.Test Method A:1) Cut from material under test specimens 200 x 200 mm (thicknessacc ording to Engineering Drawing) and bond firmly with adhesiveaccor

9、din g to S-M2G4610-A to body steel panel 300 x 300 x 1 mm,prepared according to FLTM EU-BI 3-2.2) After 24 hours at room tempera ture expose test assemblies 4 timesto the following environmental test cycle:16 h at 38 +/- 1 C and 98 +/- 2 % relative humidity8 h at 70 +/- 2 C3) Cool to r oom temperatu

10、re and test according to FLTM EU-BN 55-6,Load “B“ at room temperature.ENGINEERING MATERIAL SPECIFICATIONSK-M99G9505-AWP 3948-b Page 3 of 5 Test Method B:1) Prepare t est specimens as outlined under clause 1 of Method “A“above.2) After 24 hours conditioning at room temperature expose assembliesfor 14

11、 da ys at 70 +/- 2 C in a mechanically convected air-dryoven.3) After cooling to room temperature expose assemblies for 4 hoursat - 40 +/- 1 C and while still in cold box test accord ing to FLTMEU-BV 55-6, Load “B“.3.9 ADHESION AT ELEVATED TEMPERATURESNo loss of adhesion or deterioration of skin.Tes

12、t Method:1) Prepa re test specimens as outlined under clause 3.8, Method “A“,paragraph 1.2) After 24 hours conditioning at room temperature suspend assembliesin inve rted position in a mechanically coveted air-dry ovenmaintained at 90 +/- 2 C for 14 days.3.10 SOUND ABSORPTION(ASTM C 384)According to

13、 attached diagrams.3.11 ODORThe material shall be free from objectionable or irritating odor bothas received and after storage.3.12 SUPPLIERS RESPONSIBILITYAll materials supplied to this specification must be equivalent inal l characteristics to the material upon which approval wasoriginally granted

14、.Pri or to making any change in the properties, composition,constr uction, color, processing or labeling of the materialorig inally approved under this specification, whether or not suchchange s affect the materials ability to meet the specificationrequir ements, the Supplier shall notify Purchasing

15、, Toxicology andthe affected Materials Engineering activity of the proposed changesand obtain the written approval of the Materials Engineeringactivity. Test data, t est samples and a new code identification areto be submitted with the request.ENGINEERING MATERIAL SPECIFICATIONSK-M99G9505-AWP 3948-b

16、 Page 4 of 5 Substance restrictions imposed by law, regulations or Ford, apply tothe materials addressed by this document. The restrictions aredefined in Engineering Materials Specification WSS-M99P9999-A1.4. APPROVAL OF MATERIALSMat erials defined by this specification must have prior approval by t

17、heresp onsible Materials Engineering activity. Suppliers desiring approvalof thei r materials shall first obtain an expression of interest from theaffec ted Purchasing, Design and Materials Engineering activity. Uponrequest, the Supplier shall submit to the affected Materials Engineeringactivity a c

18、ompleted copy of their laboratory test reports, signed by aqualified and authorized representative of the test faci lity, demonstratingful l compliance with all the requirements of this specification (testresults, not nominal values), the material designation a nd code number, andtes t specimens for

19、 Ford evaluation. Fords engineering approval of amateri al will be based on its performance to this specification and on anassessment of suitability for intended processes and/or applications. Uponapprov al, the material will be added to the Engineering Material ApprovedSource List.5. GENERAL INFORM

20、ATIONThe information given below is provided for clarification and assistancein meeting the requirements of this specification.5.1 HEIGHT AT STORAGEAs recommended by supplier.5.2 STORAGE STABILITY(From date of receipt at Ford Motor Company)Minimum 12 months when stored between 5 C and 28 C.ENGINEERING MATERIAL SPECIFICATIONSK-M99G9505-AWP 3948-b Page 5 of 5 COEFFICIENT OF ABSORPTIONABSORPTION SKO EFFIECIENTASTM C 384 Hz