FORD WRS-M1H1196-A22-2015 FABRIC BARBED PATTERN WOVEN 25% RECYCLED PIR PCR CONTENT BACKCOATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2015 04 02 Released D. Murtonen, NA Controlled document at www.MATS Copyright 2015, Ford Global Technologies, LLC Page 1 of 2 FABRIC, BARBED PATTERN, WOVEN, WRS-M1H1196-A22 25% RECYCLED PIR/PCR CONTENT, BACKCOATED 1. SCOPE The material

2、 defined is a flat woven polyester face fabric. Material conforming to WRS-M1H1196-A22 contains a minimum of 25% PIR/PCR (postindustrial/post-consumer) recycled yarn. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for P558 2016 MY seat insert.

3、The fabric was originally approved as trilaminated with foam and backing fabric/scrim. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). Materials with

4、 recycled content as defined by WRS-M99P42-A2 (Textile Materials, Identification of Recycled Content) should be used whenever technically feasible. 3.1.1 WRS-M1H1196-A22. This specification must contain 25% minimum recycled content as defined by WRS-M99P42-A2/latest. The remaining portion of the mat

5、erial can come from virgin sources. 3.1.2 In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-B1/B2/B3/B4/latest as applicable. 3.1.3 Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-D1/latest, Performance, Veh

6、icle Interior Environmental Quality Material/Component Requirements. Data must be included in material submission package. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count (ASTM D3775) Ends/cm 335 / 10 cm Picks/cm 220 / 10 cm 3.2.2 Fabric Weight (FLTM BN 106-01) Face fabric 320 g/m2 ( +/- 5%) Backcoat 50

7、g/m2. (+10/-5 g/m) Total Weight 370 g/m2 ENGINEERING MATERIAL SPECIFICATION WRS-M1H1196-A22 Copyright 2015, Ford Global Technologies, LLC Page 2 of 2 3.3 COMPOSITION (ASTM D629) Fabric 100% polyester Backcoating Acrylic Resin 3.4 YARN CONSTRUCTION (ASTM D1244) Warp (A) 501 Dtex x1 (polyester, false

8、twist) Warp (B) 330 Dtex x1 (polyester, false twist Weft (A) 501 Dtex x1, (polyester, false twist) Weft (B) 550 Dtex x2 (polyester flat yarn made) Weft (C) 501 Dtex x1 (polyester, twisted 350 tpm) 100% Recycled yarn 3.5 METHOD OF DYEING Solution dyed 3.6 FINISHED OPERATIONS Washing, Drying, Top resi

9、n, Backcoating 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 Purchase departments will ensure that the material defined in t

10、his specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. The fabric must also meet the requirements of WSS-M8P18-B1/B2/B3/B4/latest. 4.3 Global strategy for this fabric is to use tri-laminate/foam & scrim construction in all regions