FORD WRS-M1H1229-A-2013 FABRIC OMNI PATTERN FLAT WOVEN 43% PIR PCR UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 2 2013 08 30 Revised Revised recycled % from 45 to 43 M.Dumitrescu, NA 2012 07 13 Revised Revised sect 3.2.2 M.Dumitrescu,NA 2012 03 28 Activated M. Dumitrescu, NA Controlled document at www.MATS Copyright 2013 Ford Global Technologies,

2、Inc. Page 1 of 2 FABRIC, OMNI PATTERN, FLAT WOVEN WRS-M1H1229-A 43% PIR/PCR UNLAMINATED 1. SCOPE The material defined by this specification is a woven dobby polyester face fabric. The fabric is made with 43% PIR/PCR (Post industrial/post consumer) recycled yarn. 2. APPLICATION This specification was

3、 released originally for material used as an interior trim fabric for 2013 Fusion seat bolster and /or insert for Europe and China production. The fabric was approved as backcoated and trilaminated with foam and backing fabric/scrim. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS

4、 Material suppliers and part producers must conform to the Companys Standard Requirements for Production Materials (WSS-M99P1111-A). 3.1.1 Recycled Content This specification must contain 43% recycled content as defined by WRS-M99P42-A2, Textile Materials, Identification of Recycled Content. The rem

5、aining portion of the material can come from virgin sources. 3.1.2 In addition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. The fabric must be backcoated. 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 9

6、05 ends/10 cm Weft 283 picks/10 cm 3.2.2 Fabric Weight, +/-10 % tolerance, (FLTM BN 106-01) Face fabric 320 g/m2 Backcoat 55 g/m2 Total weight 375 g/m2 ENGINEERING MATERIAL SPECIFICATION WRS-M1H1229-A Copyright 2013, Ford Global Technologies, Inc. Page 2 of 2 3.3 COMPOSITION (ASTM D 629) Tolerance a

7、s specified in WSS-M8P18-A1/A4 Fabric 100% Polyester Backcoating Acrylic Backing fabric/scrim 100% Polyester, Circ knit 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 167 dtex (textured polyester yarn) x 1 Weft 167 dtex (100% recycled textured polyester yarn) x 2 3.5 METHOD OF DYEING Piece dye/Solution dy

8、e 3.6 FINISHING OPERATIONS Set make, wash,dye, coating, brushed (optional) 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications 4.1 Purc

9、hase departments will ensure that the material defined in this specification and shipped to any one assembly plant will be produced by one supplier only. 4.2 Global strategy to use Tri-Laminate construction in all regions. 4.3 If yarn is locally sourced it must meet the above fabric construction, composition and yarn construction. The fabric must also meet the requirements of WSS-M8P18-A1/A2/A3/A4. 5. SUMMARY OF REVISIONS 2013 08 30 Revised recycled content from 45 to 43%. 2012 07 13 Revised Face fabric weight from 270 to 320 g/m2