FORD WRS-M2F211-A1-2014 FABRIC VINYL COATED (PVC) EXPANDED WITH BIO-BASED AND RECYCLED CONTENT (PCR PIR) TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 3 2014 11 24 N Status No replacement named D. Murtonen, NA 2013 06 05 Revised Updated 2.0 and 2.1 L. Schmalz, NA 2012 09 07 Released S. Stanciu, NA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 3

2、 FABRIC, VINYL COATED (PVC) EXPANDED, WITH BIO-BASED AND WRS-M2F211-A1 RECYCLED CONTENT (PCR/PIR) NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a laminate consisting of a vinyl film, an expanded PVC layer, and fabric backing. The backing fabric is made with 100

3、% recycled (PCR) yarn. The PVC layer has 20% minimum bio-based and recycled (PIR) content. 2. APPLICATION The specification was released originally as a flexible skin for side facing and seat back applications and other soft trim applications. 2.1 LIMITATIONS This material has not been approved for

4、use on A surface seating applications. For IP topper applications, full passenger air bag deployment testing needs to be completed. 3. REQUIREMENTS In addition to the requirements listed herein, this material shall meet all requirements of the WSS-M8P3-E1/E2/E3, Performance, Flexible Polymeric Film,

5、 Interior Quality material performance specification. Laminated material must meet the lamination requirement per WSS-M8P3-E3 performance specification. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements for Pro

6、duction Materials (WSS-M99P1111-A). 3.1.1 The PVC layer must contain a minimum of 20% recycled content as defined by WRS-M99P42-A2. 3.2 APPEARANCE (FLTM BI 109-01) The color, pattern, gloss level and finish shall match the approved Corporate Design master sample or shall be as specified on the engin

7、eering drawing 3.3 SUPPORTED FABRIC 3.3.1 Composition (ASTM D276) Fabric 100% Polyester knit fabric (100% PCR) Yarn Size 165 denier ENGINEERING MATERIAL SPECIFICATION WRS-M2F211-A1 Copyright 2014, Ford Global Technologies, LLC Page 2 of 3 3.3.2 Weight 119-152 g/m2 (ASTM D751, Sample Method) 3.3.3 Br

8、eaking Strength (ASTM D5034, Grab Method) WMD 250 N min AMD 200 N min 3.4 VINYL COATED FABRIC 3.4.1 Weight (ASTM D751, Sample Method) Total (Vinyl and supported fabric) 740-930 g/m2 3.4.2 Breaking Strength (ASTM D751, Grab Method) WMD 445 N min AMD 445 N min 3.4.3 Tear Strength (ASTM D751, Trapezoid

9、 Tear) WMD 100 N min AMD 200 N min 3.4.4 Seam Strength (FLTM BN 119-01) WMD 350 N min AMD 450 N min 3.4.5 Dimensional Stability (SAE J883, 15 minutes at 100 C) WMD 3.0% max AMD 3.0 % max 3.5 RESISTANCE TO FADE (For IP Applications Only) (FLTM BO 116-01, ISO 105-A02/AATCC Evaluation Procedure 1) 3609

10、 kJ/m2 Exposure Rating 4 After exposure, the material shall show no change in color tone (hue) or gloss and shall be equal to or better than the sample approved by Materials Engineering. Any surface bloom/chalking should be easily removed with water. In addition, it must remain flexible and exhibit

11、no cracking when bent around a 6.4 mm mandrel (face side out) after exposure. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. ENGI

12、NEERING MATERIAL SPECIFICATION WRS-M2F211-A1 Copyright 2014, Ford Global Technologies, LLC Page 3 of 3 5. SUMMARY OF REVISIONS 2013 02 08 Updated Application description Revised Limitations to remove IP Panels and added Air Bag deployment test needs Added Resistance to Fade for IP Applications 2013 06 05 Updated Application and Limitation paragraph