FORD WSB-M99P6-B-2005 PERFORMANCE REQUIREMENTS DECORATIVE WINDOWS TO BE USED WITH FORD WSS-M99P1111-A 《装饰窗的性能要求 与标准FORD WSS-M99P1111-A一起使用 使用WSS-M99P6-C1 C2》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 01 11 N-STATUS Replaced by WSS-M99P6-C1/C2; inserted 3.0; deleted 3.1, 3.2, 3.3, 3.15, 3.16 and 4 M. Mehandru 2002 02 25 Revised Updated and renumbered, no technical change 1991 08 19 NB00I10043054114 Released RDM, LWM Printed copies are

2、uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 2 PERFORMANCE REQUIREMENTS, DECORATIVE WINDOWS WSB-M99P6-B NOT TO BE USED FOR NEW DESIGN 1. SCOPE This specification defines the performance requirements of decorative windows. Two types are defined, as follows: Type I Decoration a

3、pplied between the layers of laminated glass. Type II Decoration applied to expose surface of either tempered or laminated glass. 2. APPLICATION These performance requirements were released originally for styling effects requiring decorative quarter window. Decorative materials utilized to attain th

4、e desired effects may include paints, ceramics, metal inserts or other materials either alone or in combination. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M

5、99P1111-A). 3.4 APPEARANCE Shall match the Ford Motor Company master sample. 3.5 ADHESION Type I No delamination of the glass-polyvinyl butyral bond is permitted after exposure to any resistance test. 3.6 HARDNESS (Type II Only) The decorative material shall be sufficiently hard at time of packing t

6、o withstand normal handling and shipping without marring. 3.7 ABRASION RESISTANCE (Type II Only) The decorative material shall exhibit no more abrasion or dulling than that shown on the master sample approved by Body Materials Engineering and kept on file at the Glass Division, per Test Number 18 AN

7、SI Standard Z26.1, 1977, January 26, 1977, as supplemented by Z26.1a, July 3, 1980, and incorporated by reference in FMVSS 205, February 23, 1984, except that the wheel must be refaced with a new 600 grit paper disc prior to abrading each specimen. Note: Approval of new ceramic paste suppliers, mast

8、er samples of abraded test specimen of the acceptable standard, to be provided by Ford Motor Company, Glass Division. ENGINEERING MATERIAL SPECIFICATION WSB-M99P6-B Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 2 3.8 HEAT AGING No change in adhesion, color,

9、or gloss when heated at 88 +/- 2 C for 14 days. 3.9 THERMAL CYCLE ADHESION There shall be no loss of adhesion on three test samples, when subjected to 4 thermo cycles. Test Method: The test samples shall be placed in a cold box at -40 +/- 2 C for a period of 2 h. On removal from the cold box, the ba

10、cklite shall be placed immediately in an oven at 82 +/- 2 C for a period of 2 h. 3.10 ACCELERATED WEATHERING, min 488.8 kJ (SAE J1885) No checking, blistering or loss of adhesion, and no more dulling or color change than the approved sample on approved by Body Materials Engineering and kept on file

11、at the Glass Division. 3.11 FLORIDA EXPOSURE (For Qualification Only) (SAE J1976) No checking, blistering or loss of adhesion, and no more dulling or color change than the approved sample approved by Body Materials Engineering and kept on file at the Glass Division after 12 months minimum, exposure

12、at 5 facing south in the Miami, Florida area. In the event of differences in test results between accelerated and Florida weathering, results of the Florida exposure shall govern. 3.12 WATER RESISTANCE (Type II Only) min 240 h (FLTM BI 104-01) No blistering, dulling, color change, serious roughening

13、 or loss of adhesion. Adhesion shall be determined as follows: Remove the part from the water and scribe an “X“ through the film to the glass substrate. Dry the test area, using a paper towel, cloth or air pressure and immediately apply fiber reinforced tape to the scribed area with firm thumb press

14、ure. Remove the tape by pulling at a 90 angle with moderate speed. Any removal of decorative material more than 1.6 mm from the scribe line, or evidence of blistering, shall be basis for rejection. 3.13 WATER RESISTANCE AFTER WEATHERING 24 h (Type II Only) After either accelerated or Florida weathering exposure, the part shall be immersed in water per FLTM BI 104-01. There shall be no failure as defined in para 3.11. 3.14 MATERIAL COMPONENTS Approved decorative materials utilized in the fabrication of these windows are indicated in the Ford Motor Company Approved Source List.