FORD WSF-M1L108-A2-2010 THERMOCOUPLE WIRE POSITIVE (CHROMEL) TO BE USED WITH FORD WSS-M99P1111-A 《阳极（铬镍合金）热电偶丝 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2010 06 17 N-STATUS No replacement named M. Gramlich, NA 2003 04 29 Revised Para 3.0 inserted; Para 3.1, 3.2, 3.3, 3.7, 4 deleted 1993 04 30 NGA1E10269419003 Released K. Kasper Printed copies are uncontrolle

2、d Page 1 of 3 Copyright 2010, Ford Global Technologies, Inc. THERMOCOUPLE WIRE, POSITIVE (CHROMEL) WSF-M1L108-A2 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a corrosion and heat resistant nickel-chromium alloy, with temperature-electromotive force positive re

3、lation to nearly all other metals and alloys. 2. APPLICATION This specification was released originally for material used to connect thermocouples to wire assemblies in cooler areas of a vehicle without a loss of accuracy across the thermal gradient. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRO

4、DUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 CONSTRUCTION 3.4.1 Conductor The conductor shall be seven #28 gage solid wires combined to make #20 gage cable. Cable-to-cable butt welds are not

5、allowed. The maximum lay length shall be 25 mm. The conductor shall conform to para 3.4.1.1 - 3.4.1.7 of this specification. 3.4.1.1 Chemical Composition (ASTM E 32) Carbon 0.05% max Silicon 0.25 - 0.75% Chromium 8.0 - 10.0% Columbium & Tantalum 0.05 - 0.55% Nickel Balance 3.4.1.2 Tensile Strength 5

6、17 - 724 MPa (ASTM E 8) 3.4.1.3 Yield Strength 275 - 483 MPa (ASTM E 8) ENGINEERING MATERIAL SPECIFICATION WSF-M1L108-A2 Page 2 of 3 Copyright 2010, Ford Global Technologies, Inc. 3.4.1.4 Elongation, min 20% (ASTM E 8, 250 mm gage, for 25 mm length) 3.4.1.5 Magnetic Attraction The conductor shall be

7、 non-magnetic 3.4.1.6 Temperature-Electromotive Force (ASTM E 207/E 230, EMF in absolute millivolts) Temp C Positive Member vs Positive vs Negative Platinum Member (NBS P567) (Thermocouple Type K) 20 0.527 0.798 95 2.663 3.888 150 4.358 6.137 205 6.133 8.336 3.4.1.7 Limits of Error/ Positive Thermoe

8、lement (ASTM E 230) The positive thermoelement may deviate from the single leg values shown above by no more than the following amounts: Temp C Limit of Error, mV 95 +/- 0.044 150 +/- 0.044 205 +/- 0.044 Any pair of positive and negative thermoelements will be within ASTM E 230 standard limits as a

9、thermocouple. 3.4.2 Insulation 3.4.2.1 The insulating material shall be flame retardant, homogenous, cross-linked polyethylene, similar to SAE J1560 TXL. The material shall adhere closely to, but strip readily from the conductors, leaving them free of insulation and in suitable condition for applyin

10、g terminals. The minimum wall thickness, minimum wall average, and the maximum overall diameter of the finished cable shall be in accordance to Table 2 of SAE J1560. ENGINEERING MATERIAL SPECIFICATION WSF-M1L108-A2 Page 3 of 3 Copyright 2010, Ford Global Technologies, Inc. 3.4.3 Color The color of t

11、he cross-linked polyethylene (PE) cover shall be specified on the engineering drawing and/or release by a numerical suffix following the letter suffix of the material desired. The numerical color coding suffixes shall correspond to the following: 0 - Black 5 - Green 1 - Brown 6 - Blue 2 - Red 7 - Vi

12、olet 3 - Orange 8 - Gray 4 - Yellow 9 - White or natural The first color coding numerical suffix mentioned in describing cable color shall be the base or body color of the finished cable and the second number shall designate the tracer or other auxiliary marking. The base and stripe colors shall cor

13、respond to the Munsell color tolerances specified in SAE J1560, Appendix A, Table A1. 3.5 CABLE QUALITY TEST The following tests: Insulation Physical Properties, Dielectric Test, Cold Bend Test, Flame Test, Oil Absorption Test and Pinch Test correspond respectively to sections 5.2 through 5.7 of SAE

14、 J1560. Results of these tests shall comply with the requirements of SAE J1560 type TXL. The tests listed below shall be conducted in addition to the test listed above. 3.5.1 High Temperature Resistance 25 mm of the insulation shall be removed from each end of a 600 mm sample of the finished cable.

15、The sample shall be suspended around a cylindrical mandrel having a diameter of 115 mm. The weight specified for the Cold Bend Test above, SAE J1560, Section 5.4, Table 5, Type TXL shall be suspended from each end of the conductor. This condition shall be maintained for 168 h in a mechanical convect

16、ion oven at a temperature of 165 +/- 2 C. When cool, the specimen shall be removed from the mandrel and wrapped in the reverse direction around a mandrel of the diameter specified for the Cold Bend Test in the manner prescribed for the Cold Bend Test. The specimen shall then be subjected to the Diel

17、ectric Test, SAE J1560, Section 5.3. 3.5.2 Abrasion Resistance (SAE J 1128, weight support bracket “A“, 0.23 kg weight, min requirement 305 mm) 3.6 IDENTIFICATION Every shipment of Positive Thermocouple grade wire shall be accompanied by a green color coded identification tag certifying material with respect to its coil number, specification, and weight.