FORD WSH-M2A158-A1-2009 ALUMINUM TUBING BRAZED CONDENSER TO BE USED WITH FORD WSS-M99P1111-A 《钎焊冷凝器用铝管件 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2009 11 19 N-STATUS No known use. No replacement named B. Curtiss, NA 2003 10 17 Revised Para 3.0 inserted, para 3.1, 3.6 and 4 deleted 1994 12 31 NGA1E10370437012 Released C.C. Gray, C. Sales Printed copies are uncontrolled Copyright 2009, Fo

2、rd Global Technologies, Inc. Page 1 of 2 ALUMINUM TUBING, BRAZED CONDENSER WSH-M2A158-A1 NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is an aluminum multi-void tube which is coated with zinc. 2. APPLICATION This material was released originally for tubes used in

3、brazed aluminum condensers. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 CHEMICAL COMPOSITION (Weight %) (ASTM E 227) Silicon plus Iron 0.95 m

4、ax Copper 0.05 - 0.20 Manganese 0.05 max Zinc 0.10 max Each Other Element 0.05 max Total Other Elements 0.15 max Aluminum 99.00 min 3.3 ZINC COATING REQUIREMENTS 3.3.1 Percentage of Zinc (TBD) The amount of zinc as measured on the tube flat surfaces shall be 8 to 12 grams per square meter of surface

5、 area. 3.3.2 Surface Roughness (TBD) The roughness average for the zinc coating surface shall not exceed 30 micrometers. 3.3.3 Zinc Uniformity (TBD) The zinc coating will be uniform around the periphery of tube, and shall not peel or show signs of delamination when the tube is subject to a 180 bend

6、test. ENGINEERING MATERIAL SPECIFICATIONWSH-M2A158-A1 Printed copies are uncontrolled Copyright 2009, Ford Global Technologies, Inc. Page 2 of 2 3.4 MECHANICAL PROPERTIES (Material as supplied) (ASTM B 557M) H112 Temper Ultimate Tensile Strength, min 70 MPa Yield Strength, min 20 MPa Elongation, 50

7、mm, min 30% The temper as supplied should be such that tube material dissolution by the braze filler is kept to a minimum during the braze process. 3.5 LOT CONTROL The supplier shall prepare, for each lot of every shipment, a certificate of inspection for items 3.2 through 3.4 of this specification. This information will be forwarded to the appropriate Ford Manufacturing Engineering Activity.