FORD WSS-M21P33-A-1997 CORROSION PROTECTIVE COATING SOLID FILM LUBRICANT 96 H SALT SPRAY《96 H盐雾式固体膜润滑剂防腐涂层》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONMaterial Name Specification NumberDate Action Changes1997 07 31 Activated D. DrobnichWP 3948-a Page 1 of 3CORROSION PROTECTIVE COATING, SOLID FILM WSS-M21P33-ALUBRICANT, 96 H SALT SPRAY1. SCOPEThis specification defines the performance of a solid film lubricantcoat

2、ing containing molybdenum disulfide and other lubricating pigments.It is intended to be utilized on metallic parts to materially lower thecoefficient of friction, reduce wear, minimize metallic adhesion ofparts operating dry, and provide good corrosion resistance. It is a non-electrolytic type coati

3、ng which is suitable for use with heat treatedcomponents (will not induce hydrogen embrittlement).2. APPLICATIONThis specification was released originally for friction/wearapplications here the unit loading exceeds 35 MPa.3. REQUIREMENTS3.1 QUALITY SYSTEM REQUIREMENTSMaterial suppliers and part prod

4、ucers must conform to QualitySystem Requirements, QS-9000. Material specification requirementsare to be used for initial qualification of materials. A ControlPlan for ongoing production verification is required. This planmust be reviewed and approved by the relevant Ford Materialsactivity and/or For

5、d Supplier Technical Assistance (STA) prior toproduction parts submission. Appropriate statistical tools must beused to analyze process/product data and assure consistentprocessing of the materials.Part producers using this material in their products, must use Fordapproved materials and must conform

6、 to a process control plan whichhas been approved by STA and/or the relevant Materials Activity.3.2 INFRARED SPECTROPHOTOMETRY AND/OR THERMAL ANALYSISFord Motor Company, at its option, may conduct infrared and/orthermal analysis of material/parts supplied to this specification.The IR spectra and the

7、rmograms established for initial approvalshall constitute the reference standard and shall be kept on fileat the designated material laboratory. All samples shall produce IRspectra and thermograms that correspond to the reference standardwhen tested under the same conditions.ENGINEERING MATERIAL SPE

8、CIFICATIONWSS-M21P33-AWP 3948-b Page 2 of 33.3 CONDITIONING AND TEST CONDITIONSAll test values indicated herein are based on material conditionedin a controlled atmosphere of 23 +/- 2 C and 50 +/- 5 % relativehumidity for not less than 24 h prior to testing and tested underthe same conditions unless

9、 otherwise specified.3.4 APPLICATION CHARA CTERISTICSThis material is suitable for applications where either the entirepart or portions thereof are to be coated. This can be accomplishedby spraying or dipping the pretreated part. The proper pretreatmentof each part shall be specified on the Engineer

10、ing drawing.3.5 APPEARANCEThe parts as coated shall be dull charcoal gray to black in color,uniform in coverage and free from visual imperfections such ascracks, chips, tears or contaminants.3.6 FILM THICKNESSThe coating thickness s hall be 5 - 20 micrometers or as specifiedon the Engineering drawin

11、g and adequate to meet the specified saltspray resistance.3.7 FILM PROPERTIESTests are to be completed on components whenever possible. Thefollowing test results were run on test panels and are used toestablish a baseline for qualification. Test results on componentparts may vary and underscore the

12、need to run tests on the actualcomponents. In all cases, application of the coating must be doneby an approved source as the proper application of the material isas important as the material itself.3.7.1 Coefficient of Friction .02 - .05(ASTM D 2714)3.7.2 Endurance Life(ASTM D 2625, Procedure A)Aver

13、age 400 minutesMinimum 350 minutes3.7.3 Adhesion Grade 0(FLTM BI 106-01, zinc phosphated panels)The coating must not chip, flake or expose any base metalsurface. A uniform deposit of powdery material clinging tothe tape shall not be objectionable.3.7.4 Thermal Stability(ASTM D 2 511)This material re

14、mains stable within the temperature rangeof - 220 to + 260 C.ENGINEERING MATERIAL SPECIFICATIONWSS-M21P33-AWP 3948-b Page 3 of 33.8 CUREAs a check for the proper curing of the solid film lubricant, aswab dipped in methyl ethyl ketone shall be rubbed across thecoated surface under moderate pressure f

15、ive times without exposingbare metal. A slight discoloration from the lubricating pigment isnot objectionable.3.9 CORROSION RESISTANCE(ASTM B 117)Where corrosion resistance is required, the engineering drawingshall specify the minimum exposure time. For fasteners, corrosionresistance shall be conduc

16、ted in accordance to WX100.3.10 SUPPLIERS RESPONSIBILITYAll materials supplied to this specification must be equivalent inall characteristics to the material upon which approval wasoriginally granted.Prior to making any change in the properties, composition,construction, color, processing or labelin

17、g of the materialoriginally approved under this specification, whether or not suchchanges affect the materials ability to meet the specificationrequirements, the Supplier shall notify Purchasing, Toxicology andthe affected Materials Engineering activity of the proposed changesand obtain the written

18、approval of the Materials Engineeringactivity. Test data, test samples and a new code identification areto be submitted with the request.Substance restrictions imposed by law, regulations or Ford, applyto the materials addressed by this document. The regulations aredefined in Engineering Materials S

19、pecification WSS-M99P9999-A1.4. APPROVAL OF MATERIALSMaterials defined by this specification must have prior approval by theresponsible Materials Engineering activity. Suppliers desiring approvalof their materials shall first obtain an expression of interest from theaffected Purchasing, Design and M

20、aterials Engineering activity. Uponrequest, the Supplier shall submit to the affected Materials Engineeringactivity a completed copy of their laboratory test reports, signed by aqualified and authorized representative of the test facility,demonstrating full compliance with all the requirements of th

21、isspecification (test results, not nominal values), the materialdesignation and code number, and test specimens for Ford evaluation.Fords engineering approval of a material will be based on itsperformance to this specification and on an assessment of suitabilityfor intended processes and/or applications. Upon approval, the materialwill be added to the Engineering Material Approved Source List.