FORD WSS-M2F213-A1-2017 FLEXIBLE COVERSTOCK PREMIUM VINYL (PVC) COATED WITH HIGH STRETCH PERFORMANCE TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 01 2017 06 27 Editorial Corrected footer A. Collins, NA 2016 05 19 Released S. Gatzek, NA Controlled document at www.MATS Copyright 2017, Ford Global Technologies, LLC Page 1 of 3 FLEXIBLE COVERSTOCK, PREMIUM VINYL (PVC) COATED, WSS-M2F2

2、13-A1 WITH HIGH STRETCH PERFORMANCE 1. SCOPE The material defined by this specification is an expanded polyvinyl chloride film laminated to a knitted high stretch polyester fabric. These materials can be used laminated with foam and/or a backing fabric/scrim, based on the application. 2. APPLICATION

3、 This specification was released originally for the MKX door and is intended for use in interior trim as a covering for door trim or IP wrapping applications in passenger vehicles. Any other applications must be evaluated by the appropriate product engineer with functional testing and approved by Ma

4、terials Engineering. 2.1 LIMITATIONS This material is not intended for seating applications. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS 3.1.1 Materials used in interior applications must meet the requirements outlined in WSS-M99P2222-D1/latest, Performance, Vehicle Interior E

5、nvironmental Quality Material/Component Requirements. Data must be included in material submission package. 3.1.2 In addition to the requirements listed herein, this material shall meet the requirements of WSS-M15P45-B/Latest Instrument Panel and Soft Interior Components, Flexible Cover Skin Materia

6、l Performance specification. Depending on the application, the material may be required to meet WSS-M8P3-E1/E2/E3/latest, Performance, Flexible Polymeric Film, Interior Quality. 3.2 APPROVED SOURCES This specification requires the use of approved sources. Only the sources identified on the Ford Appr

7、oved Source List (ASL) can be used when this specification is listed on the drawing, CADfile or other documents. The list of approved sources is located within Ford at or available externally through a Ford Materials Engineer. 3.3 CONDITIONING AND TEST CONDITIONS All values are based on material co

8、nditioned for not less than 24 h prior to testing in a controlled environment of 23 +/- 2 C and 50 +/- 5% relative humidity. Testing of the material should occur in the conditioning environment or soon after removal. 3.4 APPEARANCE The color, pattern, grain, gloss level and finish shall match the ap

9、proved Corporate Design Master Sample. ENGINEERING MATERIAL SPECIFICATION WSS-M2F213-A1 Copyright 2017, Ford Global Technologies, LLC Page 2 of 3 3.5 COMPOSITION 3.5.1 Vinyl Coated Fabric Composite 3.5.1.1 Total Weight Vinyl and Supporting Fabric 640 780 g/m2 (ASTM D751, Sample Method) 3.5.1.2 Thick

10、ness 1.0 1.3 mm 3.5.2 Supported Fabric 3.5.2.1 Fabric Composition 100% Polyester (ASTM D276) Circular Knit 3.5.2.2 Weight 67 82 g/m2 (ASTM D751, Sample Method) 3.6 PHYSICAL PROPERTIES 3.6.1 Breaking Strength (ASTM D751, Grab Method) WMD 300 N min AMD 300 N min 3.4.2 Tear Strength (ASTM D751, Trapezo

11、id Tear) WMD 70 N min AMD 70 N min 3.4.3 Stretch and Set (SAE J855, 5 MIN/120 N) Stretch WMD 40% min AMD 100% min Set WMD Report Only AMD Report Only 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Con

12、tact for questions concerning Engineering Material Specifications. 4.1 APPROVAL OF MATERIALS Suppliers desiring approval of their materials shall first obtain an expression of interest from Purchasing, Design or Product Development, and Materials Engineering. The supplier shall submit a completed c

13、opy of their laboratory test reports, signed by a qualified and authorized representative of the test facility, demonstrating full compliance with all the requirements of the Material Specification. Tested material samples must be available for review upon request and kept for a minimum of one year.

14、 Upon request, the supplier will review the associated quality ENGINEERING MATERIAL SPECIFICATION WSS-M2F213-A1 Copyright 2017, Ford Global Technologies, LLC Page 3 of 3 control documents (Process Failure Mode and Effects Analysis, Control Plans, Certification testing) with Ford. 4.2 SUPPLIERS ONGOI

15、NG RESPONSIBILITY All materials must be equivalent in all characteristics to the material upon which approval was originally granted. Prior to making any changes to the material originally approved, whether or not such changes affect the materials ability to meet the specification requirements, the

16、supplier shall notify the affected Supplier Technical Assistance (STA), Purchasing, and Materials Engineering activities of the proposed changes (with reasons) by submission of a completed Suppliers Request for Engineering Approval, SREA. For parts and components using Ford Engineering Material Spec

17、ifications, all samples tested to the specifications for Design Verification (DV), Production Verification (PV) and Production Part Approval Process (PPAP) sign off must be kept until Job 1. 4.3 RESTRICTED SUBSTANCE MANAGEMENT STANDARD Substance restrictions imposed by regulations or Company directi

18、on applies to the materials addressed by this document. The restrictions are identified in the Restricted Substance Management Standard WSS-M99P9999-A1 which is updated yearly. It is the suppliers responsibility to comply with this standard on a continuing basis through IMDS and or GMAP reporting. 5. SUMMARY OF REVISIONS