FORD WSS-M3B83-A4-2014 PRETREATMENT SOLUTION ALUMINUM SUBSTRATE PASSIVATION TO BE USED WITH FORD WSS-M99P1111-A .pdf

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Rev. 0 2014 06 27 Released C. Mracna FNA Controlled document at www.MATS Copyright 2014, Ford Global Technologies, LLC Page 1 of 1 PRETREATMENT SOLUTION, ALUMINUM SUBSTRATE, PASSIVATION WSS-M3B83-A4 1. SCOPE The material defined by this speci

2、fication is designed to passivate properly prepared aluminum substrates prior to subsequent adhesive bonding applications. 2. APPLICATION This specification was released originally for a Chromium-free pretreatment passivate that can be used for both sheet and wrought aluminum alloys. It is received

3、as a concentrated solution, and is required to be diluted prior to use per the manufacturers instructions. 2.1 LIMITATIONS The material approved to this specification is intended to be used as part of a system with materials approved to specifications WSS-M3B83-A1/A2/A3 resulting in a pretreated sub

4、strate that is compliant to the performance requirements defined per WSS-M10P12-B2. 3. REQUIREMENTS 3.1 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.3 TOTAL ACID, m

5、L titrant 15.5 22.4 (Chemetall Gardotest Procedure 129, or technical equivalent) 3.4 pH 2.0 (Chemetall Test Method QC-04, or technical equivalent) 3.5 ODOR Slightly Acid 3.6 COLOR Clear 3.7 PHYSICAL FORM Liquid 3.8 SHELF LIFE 1 Year 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. Contact for questions concerning Engineering Material Specifications. 4.1 SPECIFIC GRAVITY 1.034 (Chemetall Test Method QC-02, or technical equivalent) 5. SUMMARY OF REVISIONS