FORD WSS-M3H105-A14-2010 CARPET POLYESTER FLAT NEEDLED HEAT ACTIVATED BINDER FUSED BACK TO BE USED WITH FORD WSS-M99P1111-A 《背面熔凝热激活粘合剂的聚酯扁平针刺地毯 与标准FORD WSS-M99P1111-A一起使用 》.pdf

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2010 02 12 Activated L. Sinclair, NA Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, Inc. Page 1 of 2 CARPET, POLYESTER, FLAT NEEDLED, WSS-M3H105-A14 HEAT ACTIVATED BINDER, FUSED BACK 1. SCOPE The materials defined by

2、 this specification are flat needled, polyester, non-woven carpets of good quality and uniform composition. The face fiber is 100% recycled post consumer polyester. Low melt polyethylene binder forms the backing. 2. APPLICATION This specification was originally released for material used as trunk co

3、vering and seat back material for D385. 3. REQUIREMENTS In addition to the requirements listed herein, the end-item carpet assembly (molded or otherwise fabricated), shall meet all requirements of the WSS-M15P32-C and WSS-M8P16-A performance specifications. 3.1 STANDARD REQUIREMENTS FOR PRODUCTION M

4、ATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 SAMPLE SELECTION All evaluations shall be conducted on test specimens taken from finished roll goods prior to any subsequent operations, such as reheating

5、or molding. Unless otherwise specified in the Performance Specification. 3.3 APPEARANCE (FLTM BI 109-01) The color, pattern, and finish shall match the approved Design Center master sample, or shall be as specified on the engineering drawing. 3.4 COMPOSITION (ASTM D 629) Fiber 80% Polyester 20% Low

6、Melt Polyethylene Binder ENGINEERING MATERIAL SPECIFICATIONWSS-M3H105-A14 Printed copies are uncontrolled Copyright 2010, Ford Global Technologies, Inc. Page 2 of 2 3.5 METHOD OF DYEING Solution dyed or equivalent 3.6 CONSTRUCTION 3.6.1 Fiber Size and Description 5 dtex/4 dtex (ASTM D 1244) (Polyest

7、er/Low Melt Polyethylene Binder) 3.6.2 Thickness, range 2.2-2.8 mm (ASTM D 1777) 3.7 WEIGHT (FLTM BN 106-01) Pile Fiber 275-336 g/m23.8 PHYSICAL PROPERTIES 3.8.1 Breaking Strength, target (ASTM D 5034, Grab Method, 305 mm/minute jaw speed) MD 445 N AMD 575 N 3.8.2 Stretch and Set (for seat back applications only) (SAE J855) WMD & AMD Stretch, max 18% WMD & AMD Set, max 5%