GMKOREA EDS-T-3509-2008 HUMIDITY RESISTANCE OF SAFETY GLASS FOR AUTOMOBILES (VERSION 4 Replaced by GMW3136).pdf

1、GM DAEWOO Auto & Technology EDS Engineering, GM DAEWOO Auto & Technology Standards HUMIDITY RESISTANCE OF SAFETY GLASS FOR AUTOMOBILES Do Not Use on New Programs. Being Replaced by GMW3136 EDS-T-3509 ISSUED DATE: 1995. 01. 06 REVISED DATE: 2008. 10. 23 VERSION: 4 (Superceded) EDS-T-3509HUMIDITY RESI

2、STANCE OF SAFETY GLASS FOR AUTOMOBILES PAGE: 1/2 ISSUED DATE: 1995. 01. 06 REVISED DATE: 2008. 10. 23 VERSION: 4 GM DAEWOO Auto & Technology Note: This standard may be applied only for current project. It is Superceded for all future projects and replaced by GMW3136. 1. PURPOSE This standard specifi

3、es to examine whether a laminated glass produces any appreciable changes (in color, bubbles and turbidity) after exposed to high humidity in the atmosphere over an extended period of time. 2. SCOPE This standard applies to the safety glass (laminated glass with a high molecular film) for the front g

4、lass of automobiles 3. EQUIPMENT Climate chamber : 50relative humidity 4. TEST PIECE (SPECIMENS) Flat laminated glass about 300300mm manufactured by the same method as that for the product, or test pieces of about 300300mm cut from the product shall be subjected to the test. In the latter case, one

5、side of the test pieces shall coincide with part of the upper edge of the product. 5. PROCEDURE 5.1. Turn on the climate chamber 5.2. Maintain the temperature in the chamber at 502 and relative humidity at 954%. 5.3. Set the specimen vertically in the chamber 5.4. Keep the specimen for two week in t

6、he apparatus. 5.5. Take out the specimen and examine visually the change in color, bubbles and turbidity of the specimen. 6. CONDITION OF TEST 6.1. Three specimens shall be tested by the high temperature test, and all the specimens shall satisfy the requirements specified in Table 1. If one or no sp

7、ecimen satisfies the requirements, the results of the test shall be rejected. If two specimens satisfy the requirements, further three specimens shall newly be re-tested. And if all the new specimens satisfy the requirements given in Table 1, the safety glass shall be acceptable. EDS-T-3509HUMIDITY

8、RESISTANCE OF SAFETY GLASS FOR AUTOMOBILES PAGE: 2/2 ISSUED DATE: 1995. 01. 06 REVISED DATE: 2008. 10. 23 VERSION: 4 GM DAEWOO Auto & Technology 6.2. Result of test Type Condition after humidity resistance test Laminated glass There shall be no remarkable changes (color, bubble, turbidity) in ten portions beyond 10mm from the edge of the specimen, or beyond 15mm from the new edge formed in the specimen made by cutting out of a product. 7. REFERENCE KSL 2007 Safety glasses for road vehicles