HOLDEN HN 2091-2001 Adhesive Structural - Two-Part《粘接剂 结构类 双组分》.pdf

1、A.C.N. 006 893 232 Holden Limited NUMBER : HN 2091 Engineering Department SHEET : 1 of5 RELEASE : February, 1993 HOLDEN MATERIAL SPECIFICATION REVISION : November, 2001 NAME: ADHESIVE, STRUCTURAL TWO-PART 1. SCOPE The material defined by this specification is a pumpable, two component structural adh

2、esive. It is obtained by mixing in a specific ratio HN 2089 and HN 2090. It is used to bond hem flanges of engine hoods, deck lids and doors. It is suitable for use on oily and unclean surfaces such as galvanised steel, zinc coat steel and cold rolled, low carbon steel (CRLC). A component of the adh

3、esive causes some initial strength to be obtained immediately on hem closure. This is followed by a partial room temperature cure and full cure in the Elpo oven. 2. MIXING RATIO HN 2089 3.44 Parts by Weight 4.0 Parts by Volume HN 2090 1.0 Part by Weight 1.0 Part byvolume Tolerance +/- 10%. When supp

4、lied in cartridges, the extruded product must be mixed according to the recommended ratios described above. It is the suppliers responsibility to ensure that the packaging of this two part adhesive reflect the correct mix ratio. It is the responsibility of the applicator to ensure that the correct a

5、pplication/ dispensing equipment is used. 3. REQUIREMENTS OF UNCURED AND PARTIAL ROOM TEMPERATURE CURED ADHESIVE 3.1 Dens i ty (ASTM D816) 1.26 +/- 5%. 3.2 Sag Resistance (HN 0237, use 6 mm diameter bead) - No sag. .- .,$ FORM : I:CentralLaboratoStandardFormsMaterialSpecicationMatspec.doc A.C.N. 006

6、 893 232 Holden Limited NUMBER : HN 2091 Engineering Department SHEET : 2 of5 RELEASE : February, 1993 HOLDEN MATERIAL SPECIFICATION REVISION : November, 2001 NAME: ADHESIVE, STRUCTURAL TWO-PART 3. REQUIREMENTS OF UNCURED AND PARTIAL ROOM TEMPERATURE CURED ADHESIVE (con ti n ued) 3.3 Work Life - Pur

7、ge Frequency Time frequency at which one static mixer volume of adhesive shall be purged to prevent curing of material in the dispensing tip during production application of the adhesive. 1. Ambient Temperature 12“ C - 16 minutes. 2. Ambient Temperature 18“ C - 13 minutes. 3. Ambient Temperature 25“

8、 C - 10 minutes. 5. Ambient Temperature 43“ C - 8 minutes. - 4. Ambient Temperature 35“ C 9 minutes. 3.4 Phosphate Coating System Resistance There shall be no displacement, washout or leaking of material which may have a deleterious effect on the phosphate cleaning system. 3.5 Electrocoat Compatibil

9、ity There shall be no displacement, washout or leaking of material which may have a deleterious effect on the electrocoat solution. 4. ROOM TEMPERATURE AND FULL CURE PERFORMANCE 4.1 Expansion (No porosity or expansion) Extrude a 13 mm dia bead 200 mm long on to a 100 x 300 mm CRLC steel panel. Place

10、 the test panel in an oven and bake at 190“ C for 30 minutes. Allow to cool for 1 hour then cut the adhesive and panel longitudinally through the centre of the bead. Examine for voids, porosity or expansion caused by internal gassing. .- .,$ FORM : I:CentralLaboratoStandardFormsMaterialSpecicationMa

11、tspec.doc A.C.N. 006 893 232 Holden Limited NUMBER : HN 2091 Engineering Department SHEET : 3 Of5 RELEASE : February, 1993 HOLDEN MATERIAL SPECIFICATION REVISION : November, 2001 NAME: ADHESIVE, STRUCTURAL TWO-PART 4. ROOM TEMPERATURE AND FULL CURE PERFORMANCE (con ti nued) 4.2 Corrosion Resistance

12、Prepare a corrosion test assembly by taking a 0.8 x 300 x 100 mm CRLC steel panel and place a 12 x 1 x 250 mm bead of adhesive centrally on it. Cure the adhesive by baking for 30 minutes at 190“ C. Have the panel assembly put through the production phosphate and Elpo paint system. Expose the panel t

13、o 20 cycles of the procedure given in HN 0214. After completion of the last cycle rinse the panel in warm water. With a sharp knife remove adhesive from the panel. Examine the panel condition below the adhesive. There must be no sign of rust. 4.3 Room Temperature/FuII Cure Performance 4.3.1 Shear St

14、rength Samples are prepared to SAE J 1523 using production CRLC test pieces. After cleaning with solvent, 2 drops of HN 0233 rust proofing oil solution is applied to each test piece and spread with a non-absorbent spreader. The adhesive is applied to a controlled thickness of 0.25 mm. 4.3.1 .I Initi

15、al Adhesion Tested after the following times and temperature. Test is performed at the temperature indicated: A. 4 hours 10C - 3 MPa min. B. 2 hours 25“ C - 3 MPa min. C. 30 minutes 40“ C - 3 MPa min. D. 24 hours 25“ C - 5 MPa min. .- .,$ FORM : I:CentralLaboratoStandardFormsMaterialSpecicationMatsp

16、ec.doc A.C.N. 006 893 232 Holden Limited NUMBER : HN 2091 Engineering Department SHEET : 4 of5 RELEASE : February, 1993 HOLDEN MATERIAL SPECIFICATION REVISION : November, 2001 NAME: ADHESIVE, STRUCTURAL TWO-PART 4. ROOM TEMPERATURE AND FULL CURE PERFORMANCE (Continued) 4.3 Room Temperature/FuII Cure

17、 Performance (con tin ued) 4.3.1 Shear Strength (con tin ued) 4.3.1.2 Aged Adhesion Adhesive is cured 1 hour at 25“ C plus 30 minutes at 190“ c. Assemblies are exposed to the times and environments indicated. Testing is done after 4 hours at 25“ C. A. 7 days -30“ C - 12 MPa min. B. 7 days 100“ C - 1

18、2 MPa min. C. 7 days 38“ C and D. 1 O cycles of the following: 95% Relative Humidity - 12 MPa min. 80“ C - 4 hours 38“ C + 95% R.H. - 4 hours -30“ C - 16 hours - 12 MPa. Min. 4.3.1.3 High Temperature Adhesion Adhesive is cured as in 4.3.1.2. Adhesive assembly is heated to 80“ C for 1 hour and tested

19、 at that temperature - 5 MPa. Min. 4.3.2 Peel Adhesion (ASTM DI 876) Adhesive cured 1 hour 25“ C plus 30 minute at 190“ C. Testing is done after 4 hours 25“ C - 3.0 N/mm min. .- .,$ FORM : I:CentralLaboratoStandardFormsMaterialSpecicationMatspec.doc A.C.N. 006 893 232 Holden Limited NUMBER : HN 2091

20、 Engineering Department SHEET : 5 Of5 RELEASE : February, 1993 HOLDEN MATERIAL SPECIFICATION REVISION : November, 2001 NAME: ADHESIVE, STRUCTURAL TWO-PART 5. 6. 7. 8. 9. APPROVAL, INSPECTION AND REJECTION Refer HN 1000, Clauses A, C and G. HAZARDOUS MATERIALS Refer HN 1000, Clause H. RESTRICTED CHEM

21、ICALS Refer HN 1000, Clause J. REFERENCES HN 2089 HN 0214 HN1000 REVIS I ON S Novem ber, 2001 Prepared by: Mark Franke HN 2090 ASTM D816 HN 0237 SAE J 1523 HN 0233 ASTM DI876 - Clause to ensure correct mix ratio of cartridges added - Revised section 5. - Added Sections 6,7 and 8 into Section 2. .- .,$ FORM : I:CentralLaboratoStandardFormsMaterialSpecicationMatspec.doc