JEDEC JESD22-A103E-2015 High Temperature Storage Life.pdf

1、JEDEC STANDARD High Temperature Storage Life JESD22-A103E (Revision of JESD22-A103D, December 2010) OCTOBER 2015 JEDEC SOLID STATE TECHNOLOGY ASSOCIATION NOTICE JEDEC standards and publications contain material that has been prepared, reviewed, and approved through the JEDEC Board of Directors level

2、 and subsequently reviewed and approved by the JEDEC legal counsel. JEDEC standards and publications are designed to serve the public interest through eliminating misunderstandings between manufacturers and purchasers, facilitating interchangeability and improvement of products, and assisting the pu

3、rchaser in selecting and obtaining with minimum delay the proper product for use by those other than JEDEC members, whether the standard is to be used either domestically or internationally. JEDEC standards and publications are adopted without regard to whether or not their adoption may involve pate

4、nts or articles, materials, or processes. By such action JEDEC does not assume any liability to any patent owner, nor does it assume any obligation whatever to parties adopting the JEDEC standards or publications. The information included in JEDEC standards and publications represents a sound approa

5、ch to product specification and application, principally from the solid state device manufacturer viewpoint. Within the JEDEC organization there are procedures whereby a JEDEC standard or publication may be further processed and ultimately become an ANSI standard. No claims to be in conformance with

6、 this standard may be made unless all requirements stated in the standard are met. Inquiries, comments, and suggestions relative to the content of this JEDEC standard or publication should be addressed to JEDEC at the address below, or refer to www.jedec.org under Standards and Documents for alterna

7、tive contact information. Published by JEDEC Solid State Technology Association 2015 3103 North 10th Street Suite 240 South Arlington, VA 22201-2107 This document may be downloaded free of charge; however JEDEC retains the copyright on this material. By downloading this file the individual agrees no

8、t to charge for or resell the resulting material. PRICE: Contact JEDEC Printed in the U.S.A. All rights reserved PLEASE! DONT VIOLATE THE LAW! This document is copyrighted by JEDEC and may not be reproduced without permission. For information, contact: JEDEC Solid State Technology Association 3103 N

9、orth 10th Street Suite 240 South Arlington, VA 22201-2107 or refer to www.jedec.org under Standards-Documents/Copyright Information. JEDEC Standard No. 22-A103E Page 1 Test Method A103E (Revision of A103D) TEST METHOD A103E HIGH TEMPERATURE STORAGE LIFE (From JEDEC Board Ballot JCB-15-48, formulated

10、 under the cognizance of JC-14.1 Subcommittee on Reliability Test Methods for Packaged Devices.) 1 Scope The test is applicable for evaluation, screening, monitoring, and/or qualification of all solid state devices. The high temperature storage test is typically used to determine the effects of time

11、 and temperature, under storage conditions, for thermally activated failure mechanisms and time-to-failure distributions of solid state electronic devices, including nonvolatile memory devices (data retention failure mechanisms). Thermally activated failure mechanisms are modeled using the Arrhenius

12、 Equation for acceleration. During the test, accelerated stress temperatures are used without electrical conditions applied. This test may be destructive, depending on time, temperature and packaging (if any). 2 Reference documents (informative) JEP122, Failure Mechanisms and Models for Semiconducto

13、r Devices. JESD22-A113, Preconditioning of Nonhermetic Surface Mount Devices Prior to Reliability Testing. JESD22-B101, External Visual. JESD47, Stress-Test-Driven Qualification of Integrated Circuits. JESD94, Application Specific Qualification Using Knowledge Based Test Methodology. J-STD-020, Join

14、t IPC/JEDEC Standard, Moisture/Reflow Sensitivity Classification for Nonhermetic Solid State Surface-Mount Devices. JEDEC Standard No. 22-A103E Page 2 Test Method A103E (Revision of A103D) 3 Apparatus 3.1 High temperature storage chambers The apparatus required for this test shall consist of a contr

15、olled temperature chamber capable of maintaining the specified temperature over the entire sample population under test. 3.2 Electrical test equipment Electrical equipment capable of performing the appropriate measurements for the devices being tested, including write and verify the required data re

16、tention pattern(s) for nonvolatile memories. 4 Procedure 4.1 High temperature storage conditions The devices under test shall be subjected to continuous storage at one of the temperature conditions of Table 1. Table 1 High temperature storage conditions Condition A: +125 (-0/+10) C Condition B: +150

17、 (-0/+10) C Condition C: +175 (-0/+10) C Condition D: +200 (-0/+10) C Condition E: +250 (-0/+10) C Condition F: +300 (-0/+10) C NOTE CAUTION should be exercised when selecting an accelerated test condition since the accelerated temperature used may exceed the capabilities of the device and materials

18、, thereby inducing (overstress) failures that would not occur under normal use conditions. As a minimum the following items should be taken into consideration: 1) Melting point of metals present, especially solder. Degradation of metals including metallurgical interfaces. 2) Package degradation. For

19、 example: glass transition temperature and thermal stability (in air) of any polymeric materials. 3) Moisture rating of package (per J-STD-020). 4) Temperature limitations of silicon devices. For example: charge loss in nonvolatile memories. 5) Test conditions (temperature, time) should be selected

20、to cover the acceleration of the corresponding failure mechanism and the anticipated lifetime (operational time) of the device. JEDEC Standard No. 22-A103E Page 3 Test Method A103E (Revision of A103D) 4.1 High temperature storage conditions (contd) Qualification documents such as JESD47 and reliabil

21、ity monitoring agreements should provide stress durations for the stress conditions stated in Table 1. 1000 hours is a typical duration for condition B. Other conditions and durations may be used as appropriate. JESD471also recommends that some package styles be subjected to SMT reflow simulation pr

22、ior to stress. Alternatively, application of a knowledge-based test method that reconciles use condition data (JESD94) and an understanding of reliability models and failure mechanisms (JEP122) can provide the test durations for any selected stress condition in Table 1. The devices may be returned t

23、o room ambient conditions or any other defined temperature for interim electrical measurements. 4.2 Measurements Unless otherwise specified, interim and final electrical test measurements shall be completed within 168 hours after removal of the devices from the specified test conditions. Interim mea

24、surements are optional unless otherwise specified. The time window need not be met if verification data for a given technology is provided. If the final readpoint time window is exceeded then the units may be restressed for the same amount of time that the window is exceeded. The electrical test mea

25、surements shall consist of parametric and functional tests specified in the applicable procurement document. For nonvolatile memories, the data specified data retention pattern must be written initially, and then subsequently verified without re-writing. 4.3 Failure criteria A device will be conside

26、red a high temperature storage failure if parametric limits are exceeded, or if functionality cannot be demonstrated under nominal and worst-case conditions, as specified in the applicable procurement document. For nonvolatile memories, the specified data retention pattern shall be verified before a

27、nd after storage. A margin test may be used to detect data retention degradation. Mechanical damage, such as cracking, chipping, or breaking of the package, (as defined in JESD22-B101) will be considered a failure, provided that such damage was not induced by fixtures or handling and it is critical

28、to the package performance in the specific application. Cosmetic package defects and degradation of lead finish, or solderability are not considered valid failure criteria for this stress. 1From Table 2 of JESD47 - Preconditioning to JESD22A113 is recommended, specifically for wirebonded products qu

29、alified to Pb-free reflow profiles. Moisture soak as part of the preconditioning is optional. JEDEC Standard No. 22-A103E Page 4 Test Method A103E (Revision of A103D) 5 Summary The following details shall be specified in the applicable procurement document. a) Electrical test measurements, failure c

30、riteria and specifications b) Sample size and number of failures (specify zero if none observed) c) Condition per Table 1, and duration of stress d) Interim electrical test measurements, if required e) Nonvolatile memory data retention pattern (for appropriate devices) JEDEC Standard No. 22-A103E Pa

31、ge 5 Test Method A103E (Revision of A103D) Annex A (informative) Differences between JESD22-A103E and JESD22-A103D This annex briefly describes most of the changes made to entries that appear in this standard, JESD22-A103E, compared to its predecessor, JESD22-A103D (December 2010). If the change to

32、a concept involves any words added or deleted (excluding deletion of accidentally repeated words), it is included. Some punctuation changes are not included. Clause Description of change 2 Added JEP122 and JESD94, as well as JESD22-A113 which is mentioned in a note. 4.1 Modified text to emphasize th

33、at stress duration requirements are stated in qualification documents, such as JESD47 or in customer agreements, and not in this test method. Also added a reference that JEP122 and JESD94 can be used to determine appropriate stress duration. 5 Modified item C to remove reference of stress duration r

34、equirement. JEDEC Standard No. 22-A103E Page 6 Test Method A103E (Revision of A103D) Standard Improvement Form JEDEC JESD22-A103E The purpose of this form is to provide the Technical Committees of JEDEC with input from the industry regarding usage of the subject standard. Individuals or companies ar

35、e invited to submit comments to JEDEC. All comments will be collected and dispersed to the appropriate committee(s). If you can provide input, please complete this form and return to: JEDEC Attn: Publications Department 3103 North 10thStreet Suite 240 South Arlington, VA 22201-2107 Fax: 703.907.7583

36、 1. I recommend changes to the following: Requirement, clause number Test method number Clause number The referenced clause number has proven to be: Unclear Too Rigid In Error Other 2. Recommendations for correction: 3. Other suggestions for document improvement: Submitted by Name: Phone: Company: E-mail: Address: City/State/Zip: Date: