1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there
2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2012 SAE International All rights reserved. No part of this publication m
3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U
4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5870E AEROSPACE MATERIAL SPECIFICATION AMS5870 REV. E Issued 1972-05 Reaffirmed 2000-08 Re
5、vised 2012-06 Superseding AMS5870D Nickel Alloy, Corrosion and Heat-Resistant, Sheet, Strip, and Plate 60.5Ni - 23Cr - 14Fe - 0.35Ti - 1.4Al Solution Heat Treated (Composition similar to UNS N06601) RATIONALE AMS5870E revises bending (3.3.2) and is a Five Year Review and update of this specification
6、. 1. SCOPE 1.1 Form This specification covers a corrosion and heat-resistant nickel alloy in the form of sheet, strip, and plate. 1.2 Application These products have been used typically for parts requiring corrosion and oxidation resistance up to 2200 F (1204 C), particularly where such parts may re
7、quire welding during fabrication, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision
8、of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendal
9、e, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2262 Tolerances, Nickel, Nickel Alloy, and Cobalt Alloy Sheet, Strip, and Plate AMS2269 Chemical Check Analysis Limits, Nickel, Nickel Alloys, and Cobalt Alloys AMS2371 Quality Assurance Sampli
10、ng and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock SAE AMS5870E Page 2 of 5 AMS2807 Identification, Carbon and Low-Alloy Steels, Corrosion and Heat-Resistant Steels and Alloys, Sheet, Strip, Plate, and Aircraft Tubing AS4194 Sheet and Strip Surface Fin
11、ish Nomenclature 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM A 480/A 480M Flat-Rolled Stainless and Heat Resisting Steel Plate, Sheet, and Strip ASTM E 8/E 8M Tension Testing of
12、 Metallic Materials ASTM E 290 Semi-Guided Bend Test for Ductility of Metallic Materials ASTM E 354 Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight show
13、n in Table 1, determined by wet chemical methods in accordance with ASTM E 354, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon - 0.10 Manganese - 1.00 Silicon - 0.50 Sulfur - 0.015 Chromium 21.00 25.00 Nickel 58.00 63.
14、00 Titanium 0.10 0.60 Aluminum 1.00 1.70 Boron - 0.006 Copper - 1.00 Iron remainder 3.1.1 Check Analysis Composition variations shall meet the applicable requirements of AMS2269. 3.2 Condition The product shall be supplied in the following condition: 3.2.1 Sheet and Strip Cold rolled, solution heat
15、treated, and, unless solution heat treatment is performed in an atmosphere yielding a bright finish, descaled having a surface appearance comparable to the following commercial corrosion resistant steel finishes as described in ASTM A 480/A 480M and AS4194 and 3.2.1.1 or 3.2.1.2 as applicable. SAE A
16、MS5870E Page 3 of 5 3.2.1.1 Sheet No. 2D finish. 3.2.1.2 Strip No. 1 strip finish. 3.2.2 Plate Hot rolled and solution heat treated. 3.2.2.1 Surface finish shall be as hot rolled unless plate is ordered descaled. 3.3 Properties The product shall conform to the following requirements: 3.3.1 Tensile P
17、roperties Shall be as shown in Table 2 for product 0.010 to 2.000 inches (0.25 to 50.80 mm), inclusive, in nominal thickness, determined in accordance with ASTM E 8/E 8M . TABLE 2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 80 ksi (552 MPa) Yield Strength at 0.2% Offset 30.0 ksi (20
18、7 MPa) Elongation in 2 inches (50.8 mm) or 4D 35% 3.3.2 Bending Product, 0.250-inch (6.35-mm) and under in nominal thickness, shall be tested in accordance with ASTM E 290 using a sample prepared nominally 0.75 inch (19.0 mm) in width with its axis of bending parallel to the direction of rolling, an
19、d shall withstand, without cracking, when bending at room temperature through the angle and bend diameter shown in Table 3. In case of dispute, the results of tests using the guided bend test of ASTM E 290 shall govern. TABLE 3 - BENDING PARAMETERS Nominal Thickness Inch Nominal Thickness Millimeter
20、s Bend Angle Degrees Bend Diameter t=nominal thickness Up to 0.050, incl Up to 1.27, incl 180 1t Over 0.050 to 0.250, incl Over 1.27 to 6.35, incl 180 2t 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from impe
21、rfections detrimental to usage of the product. 3.5 Tolerances Shall conform to all applicable requirements of AMS2262. SAE AMS5870E Page 4 of 5 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsi
22、ble for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests All technical requirements are acceptance tests and shall be perfo
23、rmed on each heat or lot as applicable. 4.3 Sampling and Testing Shall be in accordance with AMS2371. 4.4 Reports The vendor of the product shall furnish with each shipment a report showing the results of tests for composition of each heat and for tensile and bending properties of each lot, and stat
24、ing that this product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5870E, size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS2371. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in ac
25、cordance with AMS2807. 5.2 Packaging The product shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. A
26、CKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A chang
27、e bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including
28、technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. SAE AMS5870E Page 5 of 5 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary
29、; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS5870E Type and size of product desired Quantity of product desired. PREPARED BY AMS COMMITTEE “F“