1、 AEROSPACE STANDARD INSULATION SLEEVING, ELECTRICAL, NONHEAT SHRINK SILICONE RUBBER, FLEXIBLE AS85080/2Copyright 2012 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical
2、, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org ISSUED 2004-04STABILIZED 20
3、12-03 THIRD ANGLE PROJECTION CUSTODIAN: AE-8/AE-8D REV.A FEDERAL SUPPLY CLASS 5970 AS85080/2REV. A PROCUREMENT SPECIFICATION: MIL-I-23053SAE Technical Standards Board Rules provide that: “This report ispublishedby SAE toadvance thestate of technicalandengineering sciences. Theuse ofthis report is en
4、tirely voluntary, andits applicability and suitability forany particular use,including any patent infringement arising therefrom, isthe soleresponsibilityofthe user.”SAE reviews eachtechnicalreport at least every five years at which time itmay berevised, reaffirmed, stabilized, orcancelled. SAE invi
5、tes yourwrittencomments andsuggestions. SAE values your input. To provide feedbackon this Technical Report, please visit http:/www.sae.org/technical/standards/AS85080/2A RATIONALE THIS DOCUMENT HAS BEEN DETERMINED TO CONTAIN BASIC AND STABLE TECHNOLOGY WHICH IS NOT DYNAMIC IN NATURE. DESIGN AUTHORIT
6、IES MAY DETERMINE THAT THIS DOCUMENT IS NO LONGER TO BE USED FOR NEW DESIGN. THE PRODUCT IS NOT RECOMMENDED FOR AIRCRAFT APPLICATIONS (SEE AS50881). STABILIZED NOTICE THIS DOCUMENT HAS BEEN DECLARED “STABILIZED” BY THE AE-8D COMMITTEE AND WILL NO LONGER BE SUBJECTED TO PERIODIC REVIEWS FOR CURRENCY.
7、 USERS ARE RESPONSIBLE FOR VERIFYING REFERENCES AND CONTINUED SUITABILITY OF TECHNICAL REQUIREMENTS. NEWER TECHNOLOGY MAY EXIST. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-NOTICE THIS DOCUMENT H
8、AS BEEN TAKEN DIRECTLY FROM U.S. MILITARY SPECIFICATION MIL-I-85080/2(AS), NOTICE 1 AND CONTAINS ONLY MINOR EDITORIAL AND FORMAT CHANGES REQUIRED TO BRING IT INTO CONFORMANCE WITH THE PUBLISHING REQUIREMENTS OF SAE TECHNICAL STANDARDS. THE INITIAL RELEASE OF THIS DOCUMENT IS INTENDED TO REPLACE MIL-
9、I-85080/2(AS), NOTICE 1. ANY PART NUMBERS ESTABLISHED BY THE ORIGINAL SPECIFICATION REMAIN UNCHANGED. THE ORIGINAL MILITARY SPECIFICATION WAS ADOPTED AS AN SAE STANDARD UNDER THE PROVISIONS OF THE SAE TECHNICAL STANDARDS BOARD (TSB) RULES AND REGULATIONS (TSB 001) PERTAINING TO ACCELERATED ADOPTION
10、OF GOVERNMENT SPECIFICATIONS AND STANDARDS. TSB RULES PROVIDE FOR (A) THE PUBLICATION OF PORTIONS OF UNREVISED GOVERNMENT SPECIFICATIONS AND STANDARDS WITHOUT CONSENSUS VOTING AT THE SAE COMMITTEE LEVEL, AND (B) THE USE OF THE EXISTING GOVERNMENT SPECIFICATION OR STANDARD FORMAT. UNDER DEPARTMENT OF
11、 DEFENSE POLICIES AND PROCEDURES, ANY QUALIFICATION REQUIREMENTS AND ASSOCIATED QUALIFIED PRODUCTS LISTS ARE MANDATORY FOR DOD CONTRACTS. ANY REQUIREMENT RELATING TO QUALIFIED PRODUCTS LISTS (QPLS) HAS NOT BEEN ADOPTED BY SAE AND IS NOT PART OF THIS TECHNICAL REPORT. AEROSPACE STANDARD AS85080/2SHEE
12、T 1 OF 3 REV. A INSULATION SLEEVING, ELECTRICAL, NONHEAT SHRINK SILICONE RUBBER, FLEXIBLE Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-AEROSPACE STANDARD AS85080/2SHEET 2 OF 3 REV. A INSULATION SL
13、EEVING, ELECTRICAL, NONHEAT SHRINK SILICONE RUBBER, FLEXIBLE REQUIREMENTS: CONTINUOUS OPERATING TEMPERATURE RANGE: -75C (-103F) TO +175C (347F) MODE OF SHRINKAGE: THE HEATLESS SHRINK TUBING SHALL RECOVER TO A PREDETERMINED DIAMETER UPON EXPOSURE TO THE ATMOSPHERE. NO EXTERNAL SOURCES OF HEAT ARE REQ
14、UIRED. COLOR: THE TUBING SHALL BE FURNISHED IN A BLACK COLOR THAT CONFORMS TO THE REQUIREMENTS OF CLASS II OF MIL-STD-104. LONGITUDINAL CHANGE: +3% -10% MILITARY PART NUMBER: THE MILITARY PART NUMBER SHALL CONSIST OF THE BASIC NUMBER OF THIS SPECIFICATION SHEET AND DASH NUMBERS AS SHOWN BELOW: M8508
15、0/2 - XXX - X | | | | _ COLOR CODE DESIGNATOR (SEE 1.2.2) | | | | | | _ SIZE IDENTIFIER (TABLE I) | | | | _ CLASS (WHERE NO CLASSES | ARE SPECIFIED, THE | NUMERIC “0“ SHALL BE USED) | | _ SPECIFICATION SHEET EXAMPLE: BLACK, 0.27 INCH AS SUPPLIED I.D. SLEEVING SHALL BE IDENTIFIED AS M85080/2-005-0. T
16、ABLE I. DIMENSIONS (INCHES) 1/ AFTER UNRESTRICTED SHRINKAGE MILITARY PART NUMBER 2/ AS SUPPLIED I.D. MIN 3/ I.D. MAX WALL THICKNESS 4/ M85080/2-001-0 M85080/2-002-0 M85080/2-003-0 M85080/2-004-0 M85080/2-005-0 M85080/2-006-0 M85080/2-007-0 M85080/2-008-0 M85080/2-009-0 M85080/2-010-0 M85080/2-011-0
17、M85080/2-012-0 M85080/2-013-0 M85080/2-014-0 M85080/2-015-0 .05 .09 .13 .18 .27 .36 .54 .72 .91 1.10 1.45 1.81 2.18 2.54 2.90 .031 .062 .093 .125 .187 .250 .375 .500 .625 .750 1.000 1.250 1.500 1.750 2.000 .020 .010 .020 .010 .025 .010 .035 .010 .045 .010 .045 .010 .055 .010 .065 .010 .070 .010 .090
18、 .015 .107 .020 .110 .020 .110 .020 .110 .020 .110 .025 1/ DIAMETER LIMITS FOR OBJECT TO BE ENCLOSED SHOULD BE IN ACCORDANCE WITH THE RECOMMENDATIONS OF THE MANUFACTURER. 2/ THE COLOR CODE IDENTIFIED IS THE STANDARD PROCUREMENT COLOR. 3/ THE INNER DIAMETER OF THE SLEEVE MAY BE MECHANICALLY EXPANDED
19、3.0X THE RECOVERED INSIDE DIAMETER WHEN IN THE AS-SUPPLIED CONDITION. THE MANUFACTURER SHOULD BE CONSULTED FOR SPECIAL APPLICATIONS AND RECOMMENDATIONS. 4/ WALL SHRINKAGE WILL BE LESS IF SHRINKAGE IS RESTRICTED. UNRESTRICTED SHRINKAGE: 4.6.3.13; 23 1C (73.4 2F) FOR 12 HOURS. Copyright SAE Internatio
20、nal Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-AEROSPACE STANDARD AS85080/2SHEET 3 OF 3REV. AINSULATION SLEEVING, ELECTRICAL, NONHEAT SHRINK SILICONE RUBBER, FLEXIBLE TABLE II. PROPERTIES AFTER UNRESTRICTED SHRINKAGE. PROP
21、ERTY REQUIREMENT TEST CONDITION RESTRICTED SHRINKAGE VOLTAGE WITHSTAND DIELECTRIC STRENGTH, VOLTS PER MIL MIN. VOLUME RESISTIVITY, OHMS-CM, MIN. WATER ABSORPTION, % MAX FUNGUS RESISTANCE LOW TEMPERATURE FLEX HEAT SHOCK PROPERTIES AFTER HEAT RESISTANCE TEST TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGAT
22、ION, %, MIN CORROSION PROPERTIES AFTER FLUID RESISTANCE TEST TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGATION, %, MIN ODOR TENSILE STRESS, 200% ELONGATION, PSI, MAX TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGATION, %, MIN FLAMMABILITY NO CRACKS PASS30010111.0NON NUTRIENT NO CRACKING NO CRACKS, FLOWING O
23、R DRIPPING 450200NO CORROSION OR PITTING 300100NO OBJECTIONABLE ODOR 1000800400SELF EXTINGUISHING; ONE MINUTE MAX. NO MORE THAN 25% OF INDICATOR FLAG BURNED. 4.6.3.24.6.64.6.1; ASTM D 876 4.6.2; ASTM D 876 4.6.2; ASTM D 570, PAR 6.1 4.6.2; ASTM G 21 4.6.6; -75 2F (-103 2F) 4.6.7; 300 4C (572 8F) 4.6
24、.8; 200 2C (392 6F) 4.6.94.6.103.6.114.6.2.2 ASTM D 412 4.6.13 ASTM D 638 SPEED D 4.6.13 ASTM D 638 SPEED D 4.6.14.1SHELF LIFE (AS SUPPLIED): TEST METHOD 4.6.16. MIL-I-85080/2(AS) IS INACTIVE FOR NEW DESIGN AND IS NO LONGER USED, EXCEPT FOR REPLACEMENT PURPOSES. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-