1、 AEROSPACE STANDARD INSULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYCHLOROPRENE AS85080/5Copyright 2012 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical
2、, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org ISSUED 2004-04STABILIZED 20
3、12-03 THIRD ANGLE PROJECTION CUSTODIAN: AE-8/AE-8D REV.A FEDERAL SUPPLY CLASS 5970 AS85080/5REV. A PROCUREMENT SPECIFICATION: MIL-I-85080SAE Technical Standards Board Rules provide that: “This report ispublishedby SAE toadvance thestate of technicalandengineering sciences. Theuse ofthis report is en
4、tirely voluntary, andits applicability and suitability forany particular use,including any patent infringement arising therefrom, isthe soleresponsibilityofthe user.”SAE reviews eachtechnicalreport at least every five years at which time itmay berevised, reaffirmed, stabilized, orcancelled. SAE invi
5、tes yourwrittencomments andsuggestions. SAE values your input. To provide feedbackon this Technical Report, please visit http:/www.sae.org/technical/standards/AS85080/5A RATIONALE THIS DOCUMENT HAS BEEN DETERMINED TO CONTAIN BASIC AND STABLE TECHNOLOGY WHICH IS NOT DYNAMIC IN NATURE. DESIGN AUTHORIT
6、IES MAY DETERMINE THAT THIS DOCUMENT IS NO LONGER TO BE USED FOR NEW DESIGN. THE PRODUCT IS NOT RECOMMENDED FOR AIRCRAFT APPLICATIONS (SEE AS50881). STABILIZED NOTICE THIS DOCUMENT HAS BEEN DECLARED “STABILIZED” BY THE AE-8D COMMITTEE AND WILL NO LONGER BE SUBJECTED TO PERIODIC REVIEWS FOR CURRENCY.
7、 USERS ARE RESPONSIBLE FOR VERIFYING REFERENCES AND CONTINUED SUITABILITY OF TECHNICAL REQUIREMENTS. NEWER TECHNOLOGY MAY EXIST. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-AEROSPACE STANDARD AS8
8、5080/5SHEET 1 OF 3 REV. A INSULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYCHLOROPRENE NOTICE THIS DOCUMENT HAS BEEN TAKEN DIRECTLY FROM U.S. MILITARY SPECIFICATION MIL-I-85080/5(AS), NOTICE 1 AND CONTAINS ONLY MINOR EDITORIAL AND FORMAT CHANGES REQUIRED TO BRING IT INTO CONFORMANCE WIT
9、H THE PUBLISHING REQUIREMENTS OF SAE TECHNICAL STANDARDS. THE INITIAL RELEASE OF THIS DOCUMENT IS INTENDED TO REPLACE MIL-I-85080/5(AS), NOTICE 1. ANY PART NUMBERS ESTABLISHED BY THE ORIGINAL SPECIFICATION REMAIN UNCHANGED. THE ORIGINAL MILITARY SPECIFICATION WAS ADOPTED AS AN SAE STANDARD UNDER THE
10、 PROVISIONS OF THE SAE TECHNICAL STANDARDS BOARD (TSB) RULES AND REGULATIONS (TSB 001) PERTAINING TO ACCELERATED ADOPTION OF GOVERNMENT SPECIFICATIONS AND STANDARDS. TSB RULES PROVIDE FOR (A) THE PUBLICATION OF PORTIONS OF UNREVISED GOVERNMENT SPECIFICATIONS AND STANDARDS WITHOUT CONSENSUS VOTING AT
11、 THE SAE COMMITTEE LEVEL, AND (B) THE USE OF THE EXISTING GOVERNMENT SPECIFICATION OR STANDARD FORMAT. UNDER DEPARTMENT OF DEFENSE POLICIES AND PROCEDURES, ANY QUALIFICATION REQUIREMENTS AND ASSOCIATED QUALIFIED PRODUCTS LISTS ARE MANDATORY FOR DOD CONTRACTS. ANY REQUIREMENT RELATING TO QUALIFIED PR
12、ODUCTS LISTS (QPLS) HAS NOT BEEN ADOPTED BY SAE AND IS NOT PART OF THIS TECHNICAL REPORT. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-AEROSPACE STANDARD AS85080/5SHEET 2 OF 3 REV. A INSULATION SL
13、EEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYCHLOROPRENE REQUIREMENTS: CONTINUOUS OPERATING TEMPERATURE RANGE: -55C (-67F) TO +120C (+248F). MODE OF SHRINKAGE: THE HEATLESS SHRINK SLEEVING SHALL RECOVER TO A PREDETERMINED DIAMETER UPON EXPOSURE TO THE ATMOSPHERE. NO EXTERNAL SOURCES OF HEAT ARE
14、REQUIRED. COLOR: THE SLEEVING SHALL BE FURNISHED IN A BLACK COLOR THAT CONFORMS TO THE REQUIREMENTS OF CLASS II OF MIL-STD-104. OTHER COLORS ARE AVAILABLE. LONGITUDINAL CHANGE: 10 PERCENT. MILITARY PART NUMBER: THE MILITARY PART NUMBER SHALL CONSIST OF THE BASIC NUMBER OF THIS SPECIFICATION SHEET AN
15、D DASH NUMBERS AS SHOWN BELOW: M85080/5 - X XX - X | | | | _ COLOR CODE DESIGNATOR (SEE 1.2.2) | | | | | | _ SIZE IDENTIFIER (TABLE I) | | | | _ CLASS (WHERE NO CLASSES ARE | SPECIFIED, THE NUMERIC “0“ | SHALL BE USED) | | _ SPECIFICATION SHEET EXAMPLE: BLACK, 0.843 INCH AS SUPPLIED I.D. SLEEVING SH
16、ALL BE IDENTIFIED AS M85080/5-006-0. TABLE I. DIMENSIONS (INCHES) 1/ AFTER UNRESTRICTED SHRINKAGE MILITARY PART NUMBER 2/ AS SUPPLIED I.D. MIN 3/ I.D. MAX WALL THICKNESS 4/ M85080/5-001-0 M85080/5-002-0 M85080/5-003-0 M85080/5-004-0 M85080/5-005-0 M85080/5-006-0 M85080/5-007-0 M85080/5-008-0 M85080/
17、5-009-0 M85080/5-010-0 M85080/5-011-0 M85080/5-012-0 M85080/5-013-0 M85080/5-014-0 M85080/5-015-0 .170 .252 .338 .506 .672 .843 1.012 1.181 1.350 1.688 2.025 2.363 2.700 3.375 4.050 .125 .187 .250 .375 .500 .625 .750 .875 1.000 1.250 1.500 1.750 2.000 2.500 3.000 .062 .062 .062 .062 .062 .062 .062 .
18、062 .062 .062 .070 .070 .070 .070 .070 1/ DIAMETER LIMITS FOR OBJECT TO BE ENCLOSED SHOULD BE IN ACCORDANCE WITH THE RECOMMENDATIONS OF THE MANUFACTURER. 2/ THE COLOR IDENTIFIED IS THE STANDARD ACQUISITION COLOR. 3/ THE INNER DIAMETER OF THE SLEEVE MAY BE MECHANICALLY EXPANDED 2X THE RECOVERED INSID
19、E DIAMETER WHEN IN THE AS-SUPPLIED CONDITION. THE MANUFACTURER SHOULD BE CONSULTED FOR SPECIAL APPLICATIONS AND RECOMMENDATIONS. 4/ WALL SHRINKAGE WILL BE LESS IF SHRINKAGE IS RESTRICTED. UNRESTRICTED SHRINKAGE: 4.6.3.13; 23 1C (73.4 2F) FOR 24 HOURS. Copyright SAE International Provided by IHS unde
20、r license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-AEROSPACE STANDARD AS85080/5SHEET 3 OF 3REV. AINSULATION SLEEVING, ELECTRICAL, SHRINKABLE WITHOUT HEAT, POLYCHLOROPRENE TABLE II. PROPERTIES AFTER UNRESTRICTED SHRINKAGE. PROPERTY REQUIREMENT TEST CO
21、NDITION RESTRICTED SHRINKAGE VOLTAGE WITHSTAND DIELECTRIC STRENGTH, VOLTS PER MIL MIN VOLUME RESISTIVITY, OHM-CM, MIN WATER ABSORPTION, % MAX FUNGUS RESISTANCE LOW TEMPERATURE FLEX HEAT SHOCK PROPERTIES AFTER HEAT RESISTANCE TEST: TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGATION, %, MIN CORROSION PROP
22、ERTIES AFTER FLUID RESISTANCE TEST: TENSILE STRENGTH, PSI, MIN ULTIMATE ELONGATION, %, MIN ODOR TENSILE STRESS, PSI, MIN ULTIMATE ELONGATION, %, MIN FLAMMABILITY NO CRACKS PASS20010101.0NON NUTRIENT NO CRACKING NO CRACKS, FLOWING OR DRIPPING 1200150NO CORROSION OR PITTING 900150NO OBJECTION- ABLE OD
23、OR 1500300SELF EXTINGUISHING; ONE MINUTE MAX. NO MORE THAN 25% OF IN- DICATOR FLAG BURNED. 4.6.3.24.6.64.6.2; ASTM D 876 4.6.2; ASTM D 876 4.6.2; ASTM D 570, PAR 6.1 4.6.2; ASTM G 21 4.6.6; -55 2C (-67 2F) 4.6.7; 150 1C (302 2F) 4.6.8; 100 1C (212 2F) FOR 96 HOURS. 4.6.94.6.103.6.114.6.13 ASTM D 638
24、 SPEED D 4.6.13 ASTM D 638 SPEED D 4.6.14.1SHELF LIFE (AS SUPPLIED): TEST METHOD 4.6.16. MIL-I-85080/5(AS) IS INACTIVE FOR NEW DESIGN AND IS NO LONGER USED, EXCEPT FOR REPLACEMENT PURPOSES. Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-