1、 Collection of SANS standards in electronic format (PDF) 1. Copyright This standard is available to staff members of companies that have subscribed to the complete collection of SANS standards in accordance with a formal copyright agreement. This document may reside on a CENTRAL FILE SERVER or INTRA
2、NET SYSTEM only. Unless specific permission has been granted, this document MAY NOT be sent or given to staff members from other companies or organizations. Doing so would constitute a VIOLATION of SABS copyright rules. 2. Indemnity The South African Bureau of Standards accepts no liability for any
3、damage whatsoever than may result from the use of this material or the information contain therein, irrespective of the cause and quantum thereof. ISBN 978-0-626-21324-4 SANS 15614-4:2008Edition 1 and ISO tech. corr. 1 ISO 15614-4:2005Edition 1 tech. corr.1SOUTH AFRICAN NATIONAL STANDARD Specificati
4、on and qualification of welding procedures for metallic materials Welding procedure test Part 4: Finishing welding of aluminium castings This national standard is the identical implementation of ISO 15614-4:2005 and ISO technical corrigendum 1, and is adopted with the permission of the International
5、 Organization for Standardization. Published by Standards South Africa 1 dr lategan road groenkloof private bag x191 pretoria 0001 tel: 012 428 7911 fax: 012 344 1568 international code + 27 12 www.stansa.co.za Standards South Africa SANS 15614-4:2008 Edition 1 and ISO tech. corr. 1 ISO 15614-4:2005
6、 Edition 1 and tech. corr. 1 Table of changes Change No. Date Scope ISO tech. corr. 1 2007 Corrected to delete annex ZZ. National foreword This South African standard was approved by National Committee StanSA TC 5120.08, Welding and allied processes, in accordance with procedures of Standards South
7、Africa, in compliance with annex 3 of the WTO/TBT agreement. This SANS document was published in June 2008. ICS 25.160.10 Ref. No. ISO 15614-4:2005/Cor.1:2007(E) ISO 2007 All rights reserved Published in Switzerland INTERNATIONAL STANDARD ISO 15614-4:2005 TECHNICAL CORRIGENDUM 1 Published 2007-07-15
8、 INTERNATIONAL ORGANIZATION FOR STANDARDIZATION ORGANISATION INTERNATIONALE DE NORMALISATIONSpecification and qualification of welding procedures for metallic materials Welding procedure test Part 4: Finishing welding of aluminium castings TECHNICAL CORRIGENDUM 1 Descriptif et qualification dun mode
9、 opratoire de soudage pour les matriaux mtalliques preuve de qualification dun mode opratoire de soudage Partie 4: Rparation par soudage pour les travaux de finition des pices moules en aluminium RECTIFICATIF TECHNIQUE 1 Technical Corrigendum 1 to International Standard ISO 15614-4:2005 was prepared
10、 by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee SC 10, Unification of requirements in the field of metal welding. Page 15 Delete Annex ZZ SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .Reference
11、 numberISO 15614-4:2005(E)ISO 2005INTERNATIONAL STANDARD ISO15614-4First edition2005-07-01Specification and qualification of welding procedures for metallic materials Welding procedure test Part 4: Finishing welding of aluminium castings Descriptif et qualification dun mode opratoire de soudage pour
12、 les matriaux mtalliques preuve de qualification dun mode opratoire de soudage Partie 4: Rparation par soudage pour les travaux de finition des pices moules en aluminium SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 156
13、14-4:2005(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloadin
14、g this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the Gener
15、al Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given
16、below. ISO 2005 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member bo
17、dy in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2005 All rights reservedSANS 15614-4:2008This s tandard may only be used and printed by appr
18、oved subscription and freemailing clients of the SABS .ISO 15614-4:2005(E) ISO 2005 All rights reserved iiiContents Page Foreword iv 1 Scope . 1 2 Normative references . 1 3 Terms and definitions. 2 4 Preliminary welding procedure specification (pWPS) 2 5 Welding procedure test 2 6 Test pieces 3 7 E
19、xamination and testing 6 8 Range of qualification 10 9 Welding procedure qualification record (WPQR) 11 Annex A (informative) Welding procedure qualification record (WPQR) form 12 Annex ZZ (normative) Normative references to international publications with their relevant European publications . 15 S
20、ANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-4:2005(E) iv ISO 2005 All rights reservedForeword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO m
21、ember bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governm
22、ental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Dir
23、ectives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bo
24、dies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 15614-4 was prepared by Technical Committee ISO/TC 44, Welding and allied pr
25、ocesses, Subcommittee SC 10, Unification of requirements in the field of metal welding. ISO 15614 consists of the following parts, under the general title Specification and qualification of welding procedures for metallic materials Welding procedure test: Part 1: Arc and gas welding of steels and ar
26、c welding of nickel and nickel alloys Part 2: Arc welding of aluminium and its alloys Part 3: Arc welding of cast iron Part 4: Finishing welding of aluminium castings Part 5: Arc welding of titanium, zirconium and their alloys Part 6: Arc welding of copper and its alloys Part 7: Overlay welding Part
27、 8: Welding of tubes to tube-plate joints Part 9: Underwater hyperbaric wet welding Part 10: Hyperbaric dry welding Part 11: Electron and laser beam welding Part 12: Spot, seam and projection welding Part 13: Resistance butt and flash welding Annex ZZ provides a list of corresponding International a
28、nd European Standards for which equivalents are not given in the text. Requests for official interpretations of any aspects of this part of ISO 15614 should be directed to the Secretariat of ISO/TC 44/SC 10 via your national standards body. A complete listing of these bodies can be found at www.iso.
29、org. SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .INTERNATIONAL STANDARD ISO 15614-4:2005(E) ISO 2005 All rights reserved 1Specification and qualification of welding procedures for metallic materials Welding procedure test
30、 Part 4: Finishing welding of aluminium castings 1 Scope This part of ISO 15614 is one of a series of standards, details of which are given in ISO 15607:2003, Annex A. It specifies how a welding procedure specification for finishing welding of aluminium castings is qualified by welding procedure tes
31、ts. It does not apply to repair welding. For joint welding, ISO 15614-2 applies. Arc welding of aluminium castings is covered by the following processes as defined in ISO 4063: 131 metal inert gas welding, MIG welding; 141 tungsten inert gas arc welding; TIG welding; 15 plasma arc welding. Other fus
32、ion welding processes by agreement. Shielding gases used in these processes are: argon ISO 14175 I1; helium ISO 14175 I2; argon-helium mixture ISO 14175 I3. Other shielding gases by agreement. 2 Normative references The following referenced documents are indispensable for the application of this doc
33、ument. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 571-1, Non destructive testing Penetrant testing Part 1: General principles ISO 4063, Welding and allied processes Nomenclature of
34、 processes and reference numbers ISO 6947, Welds Working positions Definitions of angles of slope and rotation ISO 9017, Destructive tests on welds in metallic materials Fracture test SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the
35、 SABS .ISO 15614-4:2005(E) 2 ISO 2005 All rights reservedISO 10042, Arc-welded joints in aluminium and its weldable alloys Guidance on quality levels for imperfections ISO 14175, Welding consumables Shielding gases for arc welding and cutting ISO 15607:2003, Specification and qualification of weldin
36、g procedures for metallic materials General rules ISO/TR 15608, Welding Guidelines for a metallic materials grouping system ISO 15609-1, Specification and qualification of welding procedures for metallic materials Welding procedure specification Part 1: Arc welding ISO 15614-2:2005, Specification an
37、d qualification of welding procedures for metallic materials Welding procedure test Part 2: Arc welding of aluminium and its alloys ISO 17635, Non-destructive testing of welds General rules for fusion welds in metallic materials ISO 17636, Non-destructive testing of welds Radiographic testing of fus
38、ion-welded joints ISO 17637, Non-destructive testing of welds Visual testing of fusion-welded joints ISO 17639, Destructive tests on welds in metallic materials Macroscopic and microscopic examination of welds 3 Terms and definitions For the purposes of this document, the terms and definitions given
39、 in ISO 15607 and the following apply. 3.1 production welding any welding carried out before final delivery to the end user 3.1.1 joint welding production welding used to assemble components together to obtain an integral unit NOTE This includes the welding of cast or wrought components as well as c
40、ombinations of cast and wrought materials. 3.1.2 finishing welding welding carried out during production in order to remove casting defects and core openings to ensure the agreed quality of castings 4 Preliminary welding procedure specification (pWPS) The preliminary welding procedure specification
41、shall be prepared in accordance with ISO 15609-1. 5 Welding procedure test The preparation and testing of test pieces representing the type of welding used in production shall be in accordance with Clauses 6 and 7. The welder shall only be qualified by welding test pieces in accordance with Clause 6
42、. SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-4:2005(E) ISO 2005 All rights reserved 36 Test pieces 6.1 General Test pieces shall be cast as one test piece in accordance with Figure 1 or three separate test piec
43、es in accordance with Figure 2 or may be taken from a production casting which exhibits the same features as Figure 1 or 2 (slot, hole and groove). Machining of the test pieces is permitted. 6.2 Shape and dimensions of test pieces The shape and minimum dimensions shall be in accordance with Figures
44、1 and 2. Dimensions in millimetres Key t material thickness Figure 1 Combined test piece with slot, hole and groove SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-4:2005(E) 4 ISO 2005 All rights reservedDimensions
45、in millimetres Key t material thickness Figure 2 Single test pieces with slot, hole and groove 6.3 Welding of test pieces Preparation and welding of test pieces shall be carried out in accordance with the pWPS and under the general conditions of welding in production which they shall represent. The
46、demonstration shall be as shown in Figure 3. In each case one stop and restart is required. SANS 15614-4:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-4:2005(E) ISO 2005 All rights reserved 5Dimensions in millimetres slot hole
47、 groove Key A1 shall show the filling up of a slot. Normally the test piece shall be welded in “vertical up” position PF or “flat” position PA as defined in ISO 6947. Undercuts on the corner and lack of fusion are critical. A2 shall show the filling up of a slot. Normally the test piece shall be wel
48、ded in position PA. Cracks, crater pipes, crater cracks, undercuts and lack of fusion are critical. B1 shall show the filling up of a hole. Normally the test piece shall be welded in position PA, in which it demonstrates the welding of a hole in a casting. Normally a backing will be used. Inclusions
49、 and lack of fusion are critical. C1 shows the production welding of a rib. Normally the test piece shall be welded in position PF or PA. Undercuts on the corner and lack of fusion are critical. C2 shall be welded in the direction shown in the figure. One stop and restart is required. Normally the test piece shall be welded in position PA. Undercuts, crater cracks and lack of fusion ar