1、UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL UL 19 Lined Fire Hose and Hose Assemblies STANDARD FOR SAFETYUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM ULUL COPYRIGHTED MATERIAL NO
2、T AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL UL Standard for Safety for Lined Fire Hose and Hose Assemblies, UL 19 Fourteenth Edition, Dated August 13, 2018 SUMMARY OF TOPICS This new edition of ANSI/UL 19 includes the following: Addition of Radiant Heat Test Meth
3、od Addition of Conductive Heat Test Method Addition of Appendix C Radiant Heat and Conductive Heat Test Results (Informative) The new/revised requirements are substantially in accordance with Proposal(s) on this subject dated June 8, 2018. All rights reserved. No part of this publication may be repr
4、oduced, stored in a retrieval system, or transmitted in any form by any means, electronic, mechanical photocopying, recording, or otherwise without prior permission of UL. UL provides this Standard as is without warranty of any kind, either expressed or implied, including but not limited to, the imp
5、lied warranties of merchantability or tness for any purpose. In no event will UL be liable for any special, incidental, consequential, indirect or similar damages, including loss of prots, lost savings, loss of data, or any other damages arising out of the use of or the inability to use this Standar
6、d, even if UL or an authorized UL representative has been advised of the possibility of such damage. In no event shall ULs liability for any damage ever exceed the price paid for this Standard, regardless of the form of the claim. Users of the electronic versions of ULs Standards for Safety agree to
7、 defend, indemnify, and hold UL harmless from and against any loss, expense, liability, damage, claim, or judgment (including reasonable attorneys fees) resulting from any error or deviation introduced while purchaser is storing an electronic Standard on the purchasers computer system. AUGUST 13, 20
8、18 UL 19 tr1UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL AUGUST 13, 2018 UL 19 tr2 No Text on This PageUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL AUGUST 13, 2018 1 UL 19 Stan
9、dard for Lined Fire Hose and Hose Assemblies The First through Sixth editions were titled Cotton Rubber-Lined Hose. First Edition July, 1914 Second Edition March, 1931 Third Edition December, 1937 Fourth Edition August, 1941 Fifth Edition April, 1948 Sixth Edition August, 1953 Seventh Edition August
10、, 1967 Eighth Edition October, 1971 Ninth Edition March, 1978 Tenth Edition December, 1992 Eleventh Edition December, 1995 Twelfth Edition November, 2001 Thirteenth Edition October, 2013 Fourteenth Edition August 13, 2018 This ANSI/UL Standard for Safety consists of the Fourteenth Edition. The most
11、recent designation of ANSI/UL 19 as an American National Standard (ANSI) occurred on August 13, 2018. ANSI approval for a standard does not include the Cover Page, Transmittal Pages, and Title Page. The Department of Defense (DoD) has adopted UL 19 on April 5, 1999. The publication of revised pages
12、or a new edition of this Standard will not invalidate the DoD adoption. Comments or proposals for revisions on any part of the Standard may be submitted to UL at any time. Proposals should be submitted via a Proposal Request in ULs On-Line Collaborative Standards Development System (CSDS) at https:/
13、. ULs Standards for Safety are copyrighted by UL. Neither a printed nor electronic copy of a Standard should be altered in any way. All of ULs Standards and all copyrights, ownerships, and rights regarding those Standards shall remain the sole and exclusive property of UL. COPYRIGHT 2018 UNDERWRITER
14、S LABORATORIES INC. ANSI/UL 19-2018UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLIES - UL 19 2 No Text on This PageUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUT
15、ION WITHOUT PERMISSION FROM UL CONTENTS INTRODUCTION 1 Scope .7 2 Units of Measurement .7 3 Undated References 7 4 Glossary .7 CONSTRUCTION 5 Internal Diameter .8 6 Jacket and Inner Reinforcements .8 7 Lining9 8 Cover9 9 Coatings and Treatments 9 10 Couplings .9 PERFORMANCE 11 Hydrostatic Proof-Pres
16、sure Tests .10 11.1 General .10 11.2 Sample .11 11.3 Equipment.11 11.4 Test method .11 12 Kink Test 13 12.1 General .13 12.2 Sample .13 12.3 Equipment.13 12.4 Test method .13 13 Hydrostatic Strength Test 13 13.1 General .13 13.2 Sample .14 13.3 Equipment.14 13.4 Test method .14 14 Repeated Bending T
17、est .14 14.1 General .14 14.2 Sample .14 14.3 Equipment.15 14.4 Test method .16 15 Alternating Pressure Test 16 15.1 General .16 15.2 Sample .16 15.3 Equipment.16 15.4 Test method .17 16 Abrasion Test 17 16.1 General .17 16.2 Sample .17 16.3 Equipment.17 16.4 Test method .18 17 Heat-Resistance Test
18、.18 17.1 General .18 AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLIES - UL 19 3UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL 17.2 Sample .18 17.3 Equipment.18 17.4 Test method .18 18 Fold-Resistance Test19 18.1 General .19 18.2 Sample .
19、19 18.3 Equipment.19 18.4 Test method .19 19 Wet Hose Test .19 19.1 General .19 19.2 Sample .20 19.3 Test method .20 20 Low-Temperature Test 20 20.1 General .20 20.2 Sample .20 20.3 Equipment.20 20.4 Test method .20 21 Coupling Retention Test .21 21.1 General .21 21.2 Sample .21 21.3 Equipment.21 21
20、.4 Test method .21 22 Friction Loss Test.21 22.1 General .21 22.2 Sample .22 22.3 Equipment.22 22.4 Test method .22 23 Accelerated Aging Test of Threads .23 23.1 General .23 23.2 Sample .23 23.3 Equipment.23 23.4 Test method .23 24 Adhesion Tests .23 24.1 General .23 24.2 Sample .24 24.3 Equipment.2
21、4 24.4 Test method .24 25 Accelerated Aging Test of Linings and Covers .25 25.1 General .25 25.2 Sample .25 25.3 Equipment.25 25.4 Test method .26 26 Ozone-Exposure Test of Linings and Covers .27 26.1 General .27 26.2 Sample .27 26.3 Equipment.27 26.4 Test method .27 27 Water Immersion Test of Linin
22、gs .27 27.1 General .27 27.2 Sample .28 27.3 Equipment.28 27.4 Method Effect on tensile strength and ultimate elongation .28 27.5 Method Effect on volume 29 AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLIES - UL 19 4UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WI
23、THOUT PERMISSION FROM UL 28 Pull Test .29 28.1 General .29 28.2 Sample .29 28.3 Test method .29 29 Accelerated Aging Test of Hose Assembly .29 29.1 General .29 29.2 Sample .30 29.3 Equipment.30 29.4 Test method .30 30 Rough Usage Test 30 30.1 General .30 30.2 Sample .30 30.3 Equipment.30 30.4 Test m
24、ethod .30 31 Moist Ammonia-Air Stress Cracking Test 31 31.1 General .31 31.2 Sample .31 31.3 Equipment.31 31.4 Method .31 32 Salt-Spray Corrosion Test .32 32.1 General .32 32.2 Sample .32 32.3 Equipment.32 32.4 Test method .32 33 Accelerated Aging Test of Gaskets .33 33.1 General .33 33.2 Sample .33
25、 33.3 Equipment.33 33.4 Test method .33 34 Compression Set Test.33 34.1 General .33 34.2 Samples 33 34.3 Equipment.34 34.4 Test method .34 35 Ozone Resistance Test of Gaskets .34 35.1 General .34 35.2 Sample .34 35.3 Equipment.34 35.4 Test method .34 36 Water Immersion Test of Gaskets 35 36.1 Genera
26、l .35 36.2 Sample .35 37 Radiant Heat Test 35 37.1 General .35 37.2 Samples 35 37.3 Equipment.36 37.4 Test method 36 37.5 Radiant heat test results 38 38 Conductive Heat Test .39 38.1 General .39 38.2 Samples 39 38.3 Equipment.39 38.4 Test method .39 AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLI
27、ES - UL 19 5UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL 38.5 Conductive heat test results .40 MANUFACTURING AND PRODUCTION TESTS 39 General41 MARKING 40 Details.41 40.1 General .41 40.2 Hose .41 40.3 Hose assemblies .42 Appendix A (Infor
28、mative) Example Radiant Heat Test Apparatus A.1 General A1 A.2 Support Frame A1 A.3 Stainless Steel Heating Element .A2 A.4 Premixed Flow Control .A4 A.5 Heater Traverse .A4 A.6 Heat Flux Gauge A5 A.7 Sensing Surface .A5 A.8 Gauge Position A5 Appendix B (Informative) Conductive Heat Test Apparatus B
29、.1 General.B1 Appendix C (Informative) Radiant Heat and Conductive Heat Test Results C.1 General C1 C.2 Radiant Heat and Conductive Heat Test Results C1 C.3 History on Method Development and Choice of Parameters C2 AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLIES - UL 19 6UL COPYRIGHTED MATERIAL
30、NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL INTRODUCTION 1 Scope 1.1 These requirements cover single- and multiple-jacketed lined re hose with or without couplings attached, in the trade sizes of 1-1/2, 1-3/4, 2, 2-1/2, 3, 3-1/2, 4, 5, and 6 inch (38, 45, 51, 6
31、5, 76, 89, 102, 127, and 152 mm nominal ID). Single-jacketed hose is intended for service test pressures of 150, 200, or 250 psig (1035, 1380, or 1725 kPa). Multiple-jacketed hose or covered hose judged equivalent to multiple-jacketed hose is intended for service test pressures of 200, 300, or 400 p
32、sig (1380, 2070, or 2760 kPa). 1.2 These products are intended for municipal and industrial re protection purposes. Single-jacketed hose is for use at re hydrants, standpipes, and similar places. They are not intended for hard usage nor where the hose will be subjected to chang on rough or sharp sur
33、faces. Multiple-jacketed hose or covered hose judged equivalent to multiple-jacketed hose are for use on pumpers and in places where service conditions require the additional protection against wear afforded by the extra woven jacket or cover. 1.3 The products covered by these requirements are inten
34、ded to be periodically inspected and maintained while in service, as outlined in the Standard for the Care, Use, Inspection, Service Testing and Replacement of Fire Hose, Couplings, Nozzles, and Fire Hose Appliances, NFPA 1962. 2 Units of Measurement 2.1 Values stated without parentheses are the req
35、uirement. Values in parentheses are explanatory or approximate information. 3 Undated References 3.1 Any undated reference to a code or standard appearing in the requirements of this standard shall be interpreted as referring to the latest edition of that code or standard. 4 Glossary 4.1 For the pur
36、pose of this standard, the following denitions apply. 4.2 EXPANSION RING A ring that expands against the hose lining, forcing the hose tightly against the coupling. 4.3 FILLER THREADS The threads or yarns of the jacket or reinforcement that are helically wound throughout the length of the hose at ap
37、proximately right angles to the warp threads. 4.4 HOSE ASSEMBLY Hose furnished with couplings attached to each end. 4.5 MULTIPLE-JACKETED HOSE Hose having two or more woven jackets or a covered hose that complies with all of the performance tests in this standard for multiple-jacketed hose. See 6.3.
38、 AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLIES - UL 19 7UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL 4.6 PROOF PRESSURE A specied pressure applied to new hose to indicate its acceptability at intended maximum normal highest operatin
39、g pressures. 4.7 SERVICE TEST PRESSURE The pressure to which the hose is periodically tested to determine that it can remain in service. The service test pressure is at least 10 percent greater than the maximum normal highest operating pressure. 4.8 WARP THREADS The threads or yarns of the jacket or
40、 reinforcement that run lengthwise to the hose. CONSTRUCTION 5 Internal Diameter 5.1 Hose shall have an internal diameter of not less than the trade size of the hose. 5.2 A tapered plug gauge having a taper of 3/8 inch per foot (31.2 mm/m) marked to indicate variations of 1/64 inch (0.4 mm) in diame
41、ter, is to be used to measure the internal diameter. If the lining of the hose has a lap joint, the tapered plug gauge is to be provided with a slot to accommodate the lap joint. 5.3 To determine the internal diameter, the end of the hose is to be cut square and the tapered plug gauge inserted in th
42、e hose sample until a close t is obtained without forcing. The diameter of the gauge at the end of the sample, to the nearest 1/64 inch (0.4 mm), is to be recorded as the internal diameter of the hose. 6 Jacket and Inner Reinforcements 6.1 A jacket shall be evenly and rmly woven, and free from visib
43、le defects, thread knots, lumps, and irregularities of twist provided that they would not impair its intended use. The threads shall be continuous, and any knots in the ller threads shall be tucked under the warp threads. 6.2 A jacket shall be seamless and shall have the llers woven around the hose
44、throughout its length and the warps interwoven with the llers. A jacket may be made with a cover over the woven jacket. 6.3 Hose having a woven jacket or hose having an inner reinforcement and a protective cover may be considered equivalent to multiple-jacketed hose if it complies with the applicabl
45、e performance requirements specied in this standard. AUGUST 13, 2018 LINED FIRE HOSE AND HOSE ASSEMBLIES - UL 19 8UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL 7 Lining 7.1 A lining shall be of uniform thickness and free from pitting or ot
46、her irregularities or imperfections and shall comply with the applicable test requirements specied in Sections 24 27. 8 Cover 8.1 A cover shall be of uniform thickness and free from pitting, blisters, or other imperfections that would impair its intended use, and shall comply with the applicable tes
47、t requirements in Sections 24 26. 8.2 A cover may have intentional pricking, ribs, corrugations, or a wrapped nish. 9 Coatings and Treatments 9.1 Hose may have jackets with treatments or coatings if the hose complies with the applicable performance requirements in this standard. 10 Couplings 10.1 Th
48、e couplings of hose assemblies shall be made from metals having the strength and other characteristics necessary to comply with the applicable performance requirements in this standard. 10.2 A metal used in the construction of any part shall have corrosion-resistant properties equivalent to those of
49、 high-strength yellow brass, UNS No. C86500 in the Standard Specication for Copper Alloys in Ingot form, ASTM B30 and in the Standard Specication for Copper Alloy Sand Castings for General Applications, ASTM B584. 10.3 To determine if a metal has the properties mentioned in 10.2, it shall comply with the requirements of the Salt-Spray Corrosion Test, Section 32. 10.4 A copper-alloy part containing more than 15 percent zinc shall comply with the requirements of