1、raising standards worldwide NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW BSI Standards Publication BS ISO 5892:2013 Rubber building gaskets Materials for preformed solid vulcanized structural gaskets SpecificationBS ISO 5892:2013 BRITISH STANDARD National foreword This Brit
2、ish Standard is the UK implementation of ISO 5892:2013. The UK participation in its preparation was entrusted to Technical Committee PRI/70, Elastomeric seals for joints in pipework and pipelines. A list of organizations represented on this committee can be obtained on request to its secretary. This
3、 publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2013. Published by BSI Standards Limited 2013 ISBN 978 0 580 72968 3 ICS 83.140.50; 91.100.50 Compliance with a British Standard c
4、annot confer immunity from legal obligations. This British Standard was published under the authority of the Standards Policy and Strategy Committee on 30 June 2013. Amendments issued since publication Date Text affectedBS ISO 5892:2013 ISO 2013 Rubber building gaskets Materials for preformed solid
5、vulcanized structural gaskets Specification Profils en caoutchouc pour le btiment Matriaux pour profils de structure compacts prforms vulcaniss Spcifications INTERNATIONAL STANDARD ISO 5892 Second edition 2013-06-15 Reference number ISO 5892:2013(E)BS ISO 5892:2013ISO 5892:2013(E)ii ISO 2013 All rig
6、hts reserved COPYRIGHT PROTECTED DOCUMENT ISO 2013 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without pr
7、ior written permission. Permission can be requested from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switz
8、erlandBS ISO 5892:2013ISO 5892:2013(E) ISO 2013 All rights reserved iii Contents Page Foreword iv 1 Scope . 1 2 Normative references 1 3 Terms and definitions . 1 4 Types of material . 2 5 Working temperature range. 2 6 Material and workmanship . 2 7 Dimensions and tolerances . 2 8 General requireme
9、nts . 2 8.1 Test pieces . 2 8.2 Hardness . 3 8.3 Tensile strength and elongation at break . 3 8.4 Compression set . 3 8.5 Accelerated ageing . 3 8.6 Ozone resistance 3 9 Specific requirements . 4 9.1 General . 4 9.2 High-density ozone resistance 4 9.3 Holding force 4 9.4 Watertightness 4 9.5 Flammab
10、ility . 4 9.6 Contact and migration staining 4 9.7 Low-temperature brittleness . 4 9.8 Low-temperature compression set . 4 Annex A (informative) Holding force test 6 Bibliography 9BS ISO 5892:2013ISO 5892:2013(E) Foreword ISO (the International Organization for Standardization) is a worldwide federa
11、tion of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committ
12、ee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. The procedures used to develop this document and
13、those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part
14、2. www.iso.org/directives Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the docum
15、ent will be in the Introduction and/or on the ISO list of patent declarations received. www.iso.org/patents Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement. The committee responsible for this document is ISO/TC 45, Rubber
16、and rubber products, Subcommittee SC 4, Products (other than hoses). This second edition cancels and replaces the first edition ( ISO 5892:1981), which has been technically revised.iv ISO 2013 All rights reservedBS ISO 5892:2013INTERNATIONAL ST ANDARD ISO 5892:2013(E) Rubber building gaskets Materia
17、ls for preformed solid vulcanized structural gaskets Specification 1 Scope This International Standard specifies material requirements for preformed, solid vulcanized rubber structural gaskets in sealing and supporting applications for buildings. NOTE Specifications for non-supporting gaskets are gi
18、ven in ISO 3934. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (in
19、cluding any amendments) applies. ISO 37, Rubber, vulcanized or thermoplastic Determination of tensile stress-strain properties ISO 188, Rubber, vulcanized or thermoplastic Accelerated ageing and heat resistance tests ISO 812:2011, Rubber, vulcanized or thermoplastic Determination of low-temperature
20、brittleness ISO 815-1, Rubber, vulcanized or thermoplastic Determination of compression set Part 1: At ambient or elevated temperatures ISO 815-2, Rubber, vulcanized or thermoplastic Determination of compression set Part 2: At low temperatures ISO 1382, Rubber Vocabulary ISO 1431-1, Rubber, vulcaniz
21、ed or thermoplastic Resistance to ozone cracking Part 1: Static and dynamic strain testing ISO 3302-1, Rubber Tolerances for products Part 1: Dimensional tolerances ISO 3865, Rubber, vulcanized or thermoplastic Methods of test for staining in contact with organic material ISO 7619-1, Rubber, vulcani
22、zed or thermoplastic Determination of indentation hardness Part 1: Durometer method (Shore hardness) ISO 15821, Doorsets and windows Water-tightness test under dynamic pressure Cyclonic aspects 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO 1382 and
23、 the following apply. 3.1 structural gasket building gasket that directly supports glasses, etc. and makes components watertight and airtight Note 1 to entry: It consists of gaskets and lock strips. ISO 2013 All rights reserved 1BS ISO 5892:2013ISO 5892:2013(E) 3.2 gasket component with channels whi
24、ch support both glasses and support frames Note 1 to entry: Gaskets having two channels are called double-channel gaskets and those having one channel are called single-channel gaskets. 3.3 lock strip component that is inserted into the lock-strip cavities for ensuring the required watertightness an
25、d airtightness 4 Types of material Two types of materials are specified. Type E, with a nominal hardness of 75 Shore A, is intended for the gaskets and for the lock strip. Type F, with a nominal hardness of 85 Shore A, is intended only for the lock strip. 5 Working temperature range The working temp
26、erature ranges of gaskets are divided into the following categories: a) P 1 : temperature of gasket: 20 C to +55 C; b) P 2 : temperature of gasket: 20 C to +85 C; c) P 3 : temperature of gasket: 40 C to +70 C; d) P 4 : temperature of gasket: 40 C to +100 C. 6 Material and workmanship 6.1 All materia
27、ls and workmanship shall be in accordance with good commercial practice. 6.2 Gaskets shall be made from ozone-resistant rubber and shall not depend for ozone resistance solely on surface protection which can be removed by abrasion, detergents, or other means. 6.3 Gaskets shall be free from porosity,
28、 significant surface defects, and dimensional irregularities, particularly on the sealing faces. 7 Dimensions and tolerances Dimensions shall be the subject of agreement between the interested parties. Tolerances shall be in accordance with the specifications of ISO 3302-1. 8 General requirements 8.
29、1 Test pieces Test pieces shall be cut from the finished product. If they cannot be so prepared, they shall be taken from moulded test slabs of suitable dimensions made from the same batch of material used for the gaskets and vulcanized under conditions which are comparable with the conditions used
30、in production.2 ISO 2013 All rights reservedBS ISO 5892:2013ISO 5892:2013(E) 8.2 Hardness When tested in accordance with the method specified in ISO 7619-1, the hardness shall comply with the requirements of Table 1. 8.3 Tensile strength and elongation at break When tested in accordance with the met
31、hod specified in ISO 37 using a dumbbell test piece, the tensile strength and elongation at break shall comply with the requirements of Table 1. 8.4 Compression set When tested in accordance with the method specified in ISO 815-1, the compression set shall comply with the requirements of Table 1 aft
32、er 24 h at 100 C. 8.5 Accelerated ageing After the test pieces have been aged in accordance with the method specified in ISO 188 and the conditions specified in Table 2, the change in hardness, tensile strength, and elongation at break shall comply with the requirements of Table 1. 8.6 Ozone resista
33、nce When tested in accordance with the method specified in ISO 1431-1, test pieces shall show no cracks after 96 h at 40 C, under 20 % elongation, at an ozone concentration of 500 ppb. Table 1 Property requirements Property Unit Limit Document specifying test method Type E Type F Hardness Shore A 75
34、 5 85 5 ISO 7619-1 Tensile strength, min. MPa 12 12 ISO 37 Elongation at break, min. % 175 125 ISO 37 Compression set, after 24 h at 100 C, max. % 35 35 ISO 815-1 Ozone resistance 500 ppb; elongation 20 %; duration 96 h at 40 C No cracking No cracking ISO 1431-1 Maximum change from unaged values aft
35、er ageing under conditions specified in Table 2: a) hardness b) tensile strength c) elongation at breakShore A % %+10 to 0 15 40+10 to 0 15 40ISO 188 and ISO 7619-1 ISO 188 and ISO 37 ISO 188 and ISO 37 Table 2 Accelerated ageing test conditions Working temperature range Test temperature C Test time
36、 d P 1 70 14 P 2 100 P 3 85 P 4 125 ISO 2013 All rights reserved 3BS ISO 5892:2013ISO 5892:2013(E) 9 Specific requirements 9.1 General These requirements are optional. Requirements and corresponding test methods shall be the subject of agreement between the interested parties. Requirements specified
37、 in 9.2 to 9.8 are summarized in Table 3. 9.2 High-density ozone resistance When tested in accordance with the method specified in ISO 1431-1, test pieces shall show no cracks after 96 h at 40 C, under 20 % elongation, at an ozone concentration of 2 000 g/m 3 . 9.3 Holding force Holding force should
38、 be measured according to the method described in Annex A. This method is given as an example. Details of the procedure and requirements depend on the profile of the gasket and shall be the subject of agreement between the interested parties. 9.4 Watertightness A suitable test method is described in
39、 ISO 15821. 9.5 Flammability The flammability of the material shall comply with the requirements of the national regulations regarding the structure of which it is a part. 9.6 Contact and migration staining A suitable test method is described in ISO 3865. 9.7 Low-temperature brittleness When tested
40、in accordance with the method specified in ISO 812, procedure C, no failure shall be observed in any one of the test pieces at the lowest temperature in thermal conditions of use. 9.8 Low-temperature compression set When tested in accordance with the method specified in ISO 815-2, the median value o
41、f type E compression set after recovery periods of 30 min shall be 80 % or less after 24 h at 25 C. The median value of type F compression set after recovery periods of 30 min shall be 90 % or less after 24 h at 25 C. Table 3 Summary of the specific property requirements Property Unit Limit Document
42、 specifying test method Type E Type F High-density ozone resistance 2 000 g/m 3 ; elongation 20 %; duration 96 h at 40 C No cracking ISO 1431-1 Holding force N/m Agreement between interested parties Annex A Watertightness Agreement between interested parties ISO 15821 Flammability Requirements of na
43、tional regulations National regulations Contact and migration staining Agreement between interested parties ISO 38654 ISO 2013 All rights reservedBS ISO 5892:2013ISO 5892:2013(E) Property Unit Limit Document specifying test method Type E Type F Low-temperature brittleness C Lowest temperature in the
44、rmal conditions of use or below ISO 812, procedure C Low-temperature compression set, after 24 h at 25 C Median value after recovery period of 30 min % 80 % or less 90 % or less ISO 815-2Table 3 (continued) ISO 2013 All rights reserved 5BS ISO 5892:2013ISO 5892:2013(E) Annex A (informative) Holding
45、force test A.1 Principle This test method determines the force exerted by the gaskets to hold glass, etc. It simulates actual use conditions by applying a load to the pressure plate, which is a simulated glass. In the case of double- channel gaskets, place the test pieces between the pressure plate
46、and support frames with thickness equal to that of the articles. In the case of single-channel gaskets, attach the pressure plate and test pieces to the reglets and support frames. Thus, these measurements reflect the wind pressure that would be encountered during application. A.2 Apparatus A.2.1 Th
47、e testing machine shall be a power-driven tensile testing machine of the movable crosshead type, equipped with adjustable crosshead speed control, a suitable dynamometer, and an indicating or recording device for measuring the applied force with an accuracy of 2 % of the full-scale reading. A.2.2 Th
48、e pressure plate and support frames to be used with the testing machine shall be of a type similar to those shown in Figures A.1 and A.2. The thickness of the support frames and the groove dimensions of the reglets shall be subject to actual use conditions. A.2.3 The pressure plate and support frame
49、s shall be made of steel. The reglets shall be made of steel or a material equivalent to that of the actual reglets. Their length shall be at least 100 mm. A.3 Test piece A.3.1 The extruded test pieces shall be at least 50 mm long but no longer than the pressure plate, support frames, and reglets. A.3.2 A minimum of eight test pieces from each lot shall be tested. A.4 Procedure A.4.1 Place the test pieces in the support frames as shown in Figu