1、raising standards worldwide NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW BSI Standards Publication BS ISO 6362-6:2012 Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 6: Round, square, rectangular and hexagonal tubes Tolerances on shape and
2、 dimensionsBS ISO 6362-6:2012 BRITISH STANDARD National foreword This British Standard is the UK implementation of ISO 6362-6:2012. The UK participation in its preparation was entrusted to Technical Committee NFE/35, Light metals and their alloys. A list of organizations represented on this committe
3、e can be obtained on request to its secretary. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. The British Standards Institution 2012. Published by BSI Standards Limited 2012 ISBN 978 0 580 72164 9 ICS 77.150
4、.10 Compliance with a British Standard cannot confer immunity from legal obligations. This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 October 2012. Amendments issued since publication Date Text affectedBS ISO 6362-6:2012 ISO 2012 Wrought a
5、luminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 6: Round, square, rectangular and hexagonal tubes Tolerances on shape and dimensions Aluminium et alliages daluminium corroys Barres, tubes et profils fils Partie 6: Tubes ronds, carrs, rectangulaires et hexagonaux Tolrances s
6、ur forme et dimensions INTERNATIONAL STANDARD ISO 6362-6 First edition 2012-07-01 Reference number ISO 6362-6:2012(E)BS ISO 6362-6:2012ISO 6362-6:2012(E) ii ISO 2012 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2012 All rights reserved. Unless otherwise specified, no part of this publication
7、 may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 T
8、el. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in SwitzerlandBS ISO 6362-6:2012ISO 6362-6:2012(E) ISO 2012 All rights reserved iii Contents Page Foreword iv 1 Scope 1 2 Normative references . 1 3 Terms and definitions . 1 4 Materials . 1 5 Tolerances on
9、 dimensions 2 5.1 General . 2 5.2 Tolerances on diameter for round tube . 3 5.3 Tolerances on width, depth or width across flats Squares, rectangles, hexagons . 4 5.4 Tolerances on wall thickness for round tube 6 5.5 Tolerances on wall thickness for tubes that are other than round 7 5.6 Tolerances o
10、n wall thickness variation (eccentricity) Round tube . 8 5.7 Tolerances on length of straight tube 9 5.8 Squareness of cut ends .10 6 Tolerances on form .10 6.1 General .10 6.2 Straightness 10 6.3 Convexity/concavity Square and rectangular tube . 11 6.4 Twist Square and rectangular tube 12 6.5 Angul
11、arity Square and rectangular tube 13 6.6 Corner and fillet radii Square and rectangular tube .14 6.7 Depth of dents for round tube14 Annex A (informative) Wall thickness variation (eccentricity) 15BS ISO 6362-6:2012ISO 6362-6:2012(E) Foreword ISO (the International Organization for Standardization)
12、is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be repres
13、ented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are
14、drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International
15、 Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 6362-6 was prep
16、ared by Technical Committee ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. ISO 6362 consists of the following parts, under the general title Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles : Part 1: Technical conditi
17、ons for inspection and delivery Part 2: Mechanical properties Part 3: Extruded rectangular bars Tolerances on shape and dimensions Part 4: Profiles Tolerances on shape and dimensions Part 5: Round, square and hexagonal bars Tolerances on shape and dimensions Part 6: Round, square, rectangular and he
18、xagonal tubes Tolerances on shape and dimensions Part 7: Chemical composition iv ISO 2012 All rights reservedBS ISO 6362-6:2012INTERNATIONAL STANDARD ISO 6362-6:2012(E) Wrought aluminium and aluminium alloys Extruded rods/ bars, tubes and profiles Part 6: Round, square, rectangular and hexagonal tub
19、es Tolerances on shape and dimensions 1 Scope This part of ISO 6362 specifies the tolerances on dimensions and shape of wrought aluminium and aluminium alloy extruded round bars having diameters in the range from 8 mm up to 350 mm; and square and hexagonal bars having widths across flats in the rang
20、e from 10 mm up to 220 mm. It applies to extruded round, square and hexagonal bars. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of th
21、e referenced document (including any amendments) applies. ISO 6362-1, Wrought aluminium and aluminium alloys Extruded rods/bars, tubes and profiles Part 1: Technical conditions for inspection and delivery 3 Terms and definitions For the purposes of this document, the terms and definitions given in I
22、SO 6362-1 apply. 4 Materials For the purposes of this part of ISO 6362, wrought aluminium and aluminium alloys are divided into two groups, which correspond to varying difficulty when manufacturing the products. The division into group I and group II of the most commonly used general engineering all
23、oys is specified in Table 1 (for seamless tube) and Table 2 (for porthole tube). Grouping of other alloys is subject to agreement between the purchaser and supplier. ISO 2012 All rights reserved 1BS ISO 6362-6:2012ISO 6362-6:2012(E) Table 1 Alloy group A (for seamless tube) Group I 1070, 1050, 1050A
24、, 1350, 1100, 1200 3102, 3003, 3103, 3203 5005, 5005A, 5051A 6101, 6101A, 6101B, 6005, 6005A, 6005C, 6008, 6014, 6060, 6360, 6063, 6063A, 6463 Group II 2007, 2011, 2011A, 2014, 2014A, 2017,2017A, 2024, 2030 5019, 5049, 5051, 5251, 5052, 5154, 5154A, 5454, 5754, 5056, 5083, 5086 6110A, 6012, 6018, 63
25、51, 6061, 6261, 6262, 6081, 6082 7003, 7204, 7005, 7108, 7108A, 7020, 7021, 7022, 7049A, 7050, 7075 NOTE The four-digit numbers listed are taken from the Registration of International Alloy Designations and Chemical Composition Limits for Wrought Aluminium Alloys, published by the Aluminum Associati
26、on, 1525 Wilson Boulevard, Suite 600, Arlington, VA 22209, USA (known as “Teal Sheets”). Table 2 Alloy group B (for porthole tube) Group I 1070, 1050, 1050A, 1350, 1100, 1200 3102, 3003, 3103, 3203 5005, 5005A 6101, 6101A, 6101B, 6005, 6005A, 6005C, 6008, 6014, 6060, 6360, 6063, 6063A, 6463 Group II
27、 5051, 5049, 5251, 5052 6110A, 6012, 6018, 6351, 6061, 6261, 6262, 6081, 6082 7003, 7005, 7108, 7108A, 7020 NOTE The four-digit numbers listed are taken from the Registration of International Alloy Designations and Chemical Composition Limits for Wrought Aluminium Alloys, published by the Aluminum A
28、ssociation, 1525 Wilson Boulevard, Suite 600, Arlington, VA 22209, USA (known as “Teal Sheets”). 5 Tolerances on dimensions 5.1 General When outside diameter OD, inside diameter ID, and wall thickness t, are all specified, standard tolerances shall apply to any two of these dimensions, but not to al
29、l three. As a result, the purchaser shall only state two nominal dimensions on any given order. For round tubes see Figure 1. For any tubes that are other than round, see Figure 2. 2 ISO 2012 All rights reservedBS ISO 6362-6:2012ISO 6362-6:2012(E) Key ID inside diameter OD outside diameter Figure 1
30、Round tube Key CD circumscribed diameter Figure 2 Circumscribing circle for tubes that are other than round 5.2 Tolerances on diameter for round tube Tolerances on diameter for round tube shall be in accordance with Table 3. ISO 2012 All rights reserved 3BS ISO 6362-6:2012ISO 6362-6:2012(E) Table 3
31、Tolerances on diameter for round tube Dimensions in millimetres Diameter OD or ID Tolerance on diameter for round tube Maximum allowable deviation of diameter at any point from specified diameter a Maximum allowable deviation of mean diameter from specified diameter b Alloy group I c Alloy group II
32、c Alloy group I c Alloy group II c 13 OD or ID 25 0,51 0,76 0,25 0,38 25 OD or ID 50 0,64 0,97 0,30 0,40 50 OD or ID 100 0,76 1,14 0,38 0,58 100 OD or ID 150 1,27 1,91 0,64 0,97 150 OD or ID 200 1,91 2,87 0,89 1,35 200 OD or ID 250 2,54 3,81 1,14 1,73 250 OD or ID 300 3,18 4,78 1,40 2,11 300 OD or I
33、D 350 3,81 5,72 1,65 2,49 350 OD or ID 400 4,45 6,68 1,91 2,87 400 OD or ID 450 5,08 7,62 2,16 3,25 When the tolerance is specified only for either the plus or the minus side, the values in this table shall be doubled. Tolerances on dimensions exceeding the specified range shall be agreed upon betwe
34、en the purchaser and the supplier. aThese values are not applied to the tubes of temper grade O, coiled tubes and tubes with wall thickness less than 2,5 % of the specified outside diameter. bThe mean diameter is defined as the average value of measurements made at two arbitrary points at right angl
35、es to each other. cRefer to Table 1. 5.3 Tolerances on width, depth or width across flats Squares, rectangles, hexagons 5.3.1 Seamless tube The tolerances on width, depth or width across flats for seamless tubes that are other than round are specified in Table 4. 4 ISO 2012 All rights reservedBS ISO
36、 6362-6:2012ISO 6362-6:2012(E) Table 4 Tolerances on width, depth or width across flats for seamless tubes that are other than round Dimensions in millimetres Width, depth or width across flats W Tolerances on width, depth or width across flats for seamless tubes that are other than round a,b CD 100
37、 100 CD 200 200 CD 300 300 CD 350 Alloy group c I II I II I II I II W 10 0,25 0,40 0,30 0,50 0,35 0,55 0,40 0,60 10 W 25 0,30 0,50 0,40 0,70 0,50 0,80 0,60 0,90 25 W 50 0,50 0,80 0,60 0,90 0,80 1,00 0,90 1,20 50 W 100 0,70 1,00 0,90 1,20 1,10 1,30 1,30 1,60 50 W 150 - - 1,10 1,50 1,30 1,70 1,50 1,80
38、 150 W 200 - - 1,30 1,90 1,50 2,20 1,80 2,40 200 W 300 - - - - 1,70 2,50 2,10 2,80 300 W 350 - - - - - - 2,80 3,50 aNot applicable to tubes having a wall thickness less than 2,5 % of the specified outside width, depth or width across flats. The tolerance for tubes with wall thickness less than 2,5 %
39、 of the specified width, depth or width across flats shall be determined by multiplying the applicable tolerance as follows: wall thickness over 2,0 % up to and including 2,5 % of outside parameter: 1,5 tolerance; wall thickness over 1,5 % up to and including 2,0 % of outside parameter: 2,0 toleranc
40、e; wall thickness over 1,0 % up to and including 1,5 % of outside parameter: 3,0 tolerance; wall thickness over 0,5 % up to and including 1,0 % of outside parameter: 4,0 tolerance. bThese tolerances do not apply to tempers O and Tx510. For these tempers, the tolerances shall be subject to agreement
41、between the supplier and purchaser. cRefer to Table 1. 5.3.2 Porthole tube The tolerances on width, depth or width across flats for porthole tubes that are other than round are specified in Table 5. ISO 2012 All rights reserved 5BS ISO 6362-6:2012ISO 6362-6:2012(E) Table 5 Tolerances on width, depth
42、 or width across flats for porthole tubes that are other than round Dimensions in millimetres Width, depth or width across flats W Tolerances on width, depth or width across flats for porthole tubes that are other than round a,b CD 100 100 CD 200 200 CD 300 300 CD 350 Alloy group c I II I II I II I
43、II W 10 0,25 0,40 0,30 0,50 0,35 0,55 0,40 0,60 10 W 25 0,30 0,50 0,40 0,70 0,50 0,80 0,60 0,90 25 W 50 0,50 0,80 0,60 0,90 0,80 1,00 0,90 1,20 50 W 100 0,70 1,00 0,90 1,20 1,10 1,30 1,30 1,60 50 W 150 - - 1,10 1,50 1,30 1,70 1,50 1,80 150 W 200 - - 1,30 1,90 1,50 2,20 1,80 2,40 200 W 300 - - - - 1,
44、70 2,50 2,10 2,80 300 W 350 - - - - - - 2,80 3,50 aNot applicable to tubes having a wall thickness less than 2,5 % of the specified outside width, depth or width across flats. The tolerance for tubes with wall thickness less than 2,5 % of the specified width, depth or width across flats shall be det
45、ermined by multiplying the applicable tolerance as follows: wall thickness over 2,0 % up to and including 2,5 % of outside parameter: 1,5 tolerance; wall thickness over 1,5 % up to and including 2,0 % of outside parameter: 2,0 tolerance; wall thickness over 1,0 % up to and including 1,5 % of outside
46、 parameter: 3,0 tolerance; wall thickness over 0,5 % up to and including 1,0 % of outside parameter: 4,0 tolerance. bThese tolerances do not apply to tempers O and Tx510. For these tempers, the tolerances shall be subject to agreement between the supplier and purchaser. cRefer to Table 2. 5.4 Tolera
47、nces on wall thickness for round tube The tolerances on wall thickness for round tubes are specified in Table 6. 6 ISO 2012 All rights reservedBS ISO 6362-6:2012ISO 6362-6:2012(E) Table 6 Tolerances on wall thickness for round tubes Dimensions in millimetres Wall thickness at Tolerance on wall thick
48、ness for round tubes Maximum allowable deviation of wall thickness at any point from specified wall thickness Maximum allowable deviation of mean wall thickness from specified wall thickness bOutside diameter OD OD 30 30 OD 75 75 OD 125 125 OD Alloy group c I II I II I II I II t 1 10 % of the mean wall thickness Max. 1,52 Min. 0,25 0,15 - - - - - - - 1 t 1,5 0,18