1、ASD STANDARD NORME ASD ASD NORM prEN 4655 Edition P1 December 2009 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. 32 2 775 8126 - Fax. 32 2 775 8131 - www.asd-stan.orgICS: Descriptors: ENGLISH VERSION Aerospac
2、e series Steel FE-PM1506 (X1CrNiMoAlTi12-10-2) Vacuum induction melted and consumable electrode remelted Solution treated and precipitation remelted Bars a or D 200 mm Rm 1 400 MPa Srie arospatiale Acier FE-PM1506 (X1CrNiMoAlTi12-10-2) labor sous vide par induction et refondu llectrode consommable M
3、is en solution et vieilli Barres a ou D 200 mm Rm 1 400 MPa Luft- und Raumfahrt Stahl FE-PM1506 (X1CrNiMoAlTi12-10-2) Vakuuminduktionserschmolzen und mit Selbstverzehrender Elektrode umgeschmolzen Lsungsgeglht und ausgelargert Stangen a oder D 200 mm Rm 1 400 MPa This “Aerospace Series“ Prestandard
4、has been drawn up under the responsibility of ASD-STAN (The AeroSpace and Defence Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace Industry. It has been technically approved by the experts of the concerned Domain following member comments.
5、Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be su
6、bmitted as a draft European Standard (prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to implement the EN at national level by giving the EN the status of a national standard and by withdrawin
7、g any national standards conflicting with the EN. Edition approved for publication 15 December 2009 Comments should be sent within six months after the date of publication to ASD-STAN Metallic Material Domain Copyright 2009 by ASD-STAN Copyright ASD-STAN Provided by IHS under license with AECMA Not
8、for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4655:2009 (E) 2 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-STANs Metallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in
9、 ASD-STANs General Process Manual, this standard has received approval for Publication. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4655:2009 (E) 3 Introduction This standard is part of the series
10、 of EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. This standard has been prepared in accordance with EN 4500-5. 1 Scope This standard specifies the requirements relating to: Steel FE-PM1506 (X1CrNiMoAlTi12-10-2) Vacuum ind
11、uction melted and consumable electrode remelted Solution treated and precipitation treated Bars a or D 200 mm Rm 1 400 MPa for aerospace applications. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edit
12、ion cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 2043, Aerospace series Metallic materials General requirements for semi-finished product qualification (excluding forgings and castings) 1)EN 2951, Aerospace series Metalli
13、c materials Test method Micrographic determination of content of non-metallic inclusionsEN 4258, Aerospace series Metallic materials General organization of standardization Links between types of EN standards and their use EN 4500-5, Aerospace series Metallic materials Rules for drafting and present
14、ation of material standards Part 5: Specific rules for steels 1) EN 4700-002, Aerospace series Steel and heat resisting alloy Technical specification Part 002: Bar and section 1) 1) Published as ASD-STAN Prestandard at the date of publication of this standard. Copyright ASD-STAN Provided by IHS unde
15、r license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4655:2009 (E) 4 1 Material designation FE-PM1506 (X1CrNiMoAlTi12-10-2) Element C Si Mn P S Cr Ni Mo Al Ti N2Fe min. 11,5 9,2 1,85 0,80 0,28 2 Chemical composition % max. 0,015 0,10 0,10 0,010
16、 0,005 12,5 10,2 2,15 1,10 0,40 0,01 base 3 Method of melting Vacuum induction melted and consumable electrode remelted 4.1 Form Bar 4.2 Method of production 4.3 Limit dimension(s) mm a or D 200 5 Technical specification EN 4700-002 Delivery condition Solution treated Solution treated and precipitat
17、ion treated 6.1 Heat treatment 820 C 860 C / OQ, AQ or WQ + cooling to 20 C 820 C 860 C / OQ, AQ or WQ + cooling to 20 C + 530 C 550C / t 4 h / AC + cooling to 20 C 6.2 Delivery condition code W U Use condition Solution treated and precipitation treated Delivery condition 7 Heat treatment Delivery c
18、ondition + 530 C 550C / t 4 h / AC Characteristics 8.1 Test sample(s) See EN 4700-002. 8.2 Test piece(s) See EN 4700-002. 8.3 Heat treatment Delivery condition Use condition 9 Dimensions concerned mm a or D 200 a or D 200 a 75 a or D 200 a 10 Thickness of cladding on each face % 11 Direction of test
19、 piece L T 12 Temperature C Ambient Ambient 13 Proof stress Rp0,2 MPa 1 300 1 300 14 Strength Rm MPa 1 400 1 400 15 Elongation A % 9 8 16 T Reduction of area Z % 50 45 17 Hardness 363 HB 400 HB 400 HB 18 Shear strength Rc MPa 19 Bending k 20 Impact strength Notch direction T KV 50 J, ambient + KV 20
20、 J, at 40 C Notch direction L KV 40 J, ambient + KV 15 J, at 40 C 21 Temperature C 22 Time h 23 Stress a MPa 24 Elongation a % 25 Rupture stress R MPa 26 C Elongation at rupture A % 27 Notes (see line 98) aCopyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or n
21、etworking permitted without license from IHS-,-,-prEN 4655:2009 (E) 5 30 Microstructure 1 EN 4700-002 2One per cast 3 Corresponding to ingot top 7 The ferrite content shall not exceed 2 %. 34 Grain size See EN 4700-002. 7 G 6 , some 5 accepted 44 External defects See EN 4700-002. 1 Visual 50 Cleanli
22、ness / inclusion content See EN 4700-002. (micro-cleanness) 7 EN 2951 - Category 5 51 Macrostructure See EN 4700-002. 7 Class Condition Severity 1 Freckles A 2 White spots A 3 Radial segregation A 4 Ring pattern B 61 Internal defects See EN 4700-002. 7 EN 4050-4 - Class 5 95 Marking inspection See E
23、N 4700-002. 96 Dimensional inspection See EN 4700-002. 98 Notes a75 mm a or D 2100 mm may be tested in L or T direction 99 Typical use Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4655:2009 (E) 6 100 Product qualification See EN 2043. Qualification programme to be agreed between manufacturer and purchaser. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-