1、ASD STANDARD NORME ASD ASD NORM prEN 4800-008 Edition P 2 September 2009 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 775 8131 - www.asd-stan.orgICS: Supersedes edition P 1 of S
2、eptember 2002 Descriptors: ENGLISH VERSION Aerospace series Titanium and titanium alloys Technical specification Part 008: Pre-production and production castings Srie arospatiale Titane et alliages de titane Spcification technique Partie 008 : Pices types et pices de srie, moules Luft- und Raumfahrt
3、 Titan und Titanlegierungen Kneterzeugnisse Technische Lieferbedingungen Teil 008: Schmiedevormaterial This “Aerospace Series“ Prestandard has been drawn up under the responsibility of ASD-STAN (The AeroSpace and Defence Industries Association of Europe - Standardization). It is published for the ne
4、eds of the European Aerospace Industry. It has been technically approved by the experts of the concerned Domain following member comments. Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or fun
5、ctionally, without re-identification of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard (prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). Th
6、e CEN national members have then to implement the EN at national level by giving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Edition approved for publication 30 September 2009 Comments should be sent within six months after the date of
7、publication to ASD-STAN Metallic Material Domain Copyright 2009 by ASD-STAN Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4800-008:2009 (E) 2 Contents Page Foreword2 Introduction.3 1 Scope 3 2 Norma
8、tive references3 3 Terms and definitions .4 4 Wording of order5 5 Health and safety .5 6 Technical requirements 5 Annex A (normative) Flaw penetrant inspection standard21 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-STANs Metallic Material Domain. After inquiries an
9、d votes carried out in accordance with the rules of ASD-STAN defined in ASD-STANs General Process Manual, this standard has received approval for Publication. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-
10、,-prEN 4800-008:2009 (E) 3 Introduction This standard is part of the series of EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. 1 Scope This standard defines the requirements for the ordering, manufacture, testing, inspection
11、 and delivery of titanium and titanium alloy pre-production and production castings. It shall be applied when referred to and in conjunction with the EN material standard unless otherwise specified on the drawing, order or inspection schedule. 2 Normative references The following referenced document
12、s are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 2002-001, Aerospace series Metallic materials Test methods Part 001: Tensile te
13、sting at ambient temperature EN 2002-002, Aerospace series Metallic materials Test methods Part 002: Tensile testing at elevated temperature EN 2002-005, Aerospace series Test methods for metallic materials Part 005: Uninterrupted creep and stress-rupture testing EN 2002-16, Aerospace series Metalli
14、c materials Test methods Part 16: Non-destructive testing Penetrant testing1)EN 2002-21, Aerospace series Test methods for metallic materials Part 21: Radiographic testing of castings1)EN 2032-1, Aerospace series Metallic materials Part 1: Conventional designation. EN 2032-2, Aerospace series Metall
15、ic materials Part 2: Coding of metallurgical condition in delivery condition. EN 2078, Aerospace series Metallic materials Manufacturing schedule, inspection schedule, inspection and test report Definition, general principles, preparation and approval. EN 3976, Aerospace series Titanium and titanium
16、 alloys Test method Chemical analysis for the determination of hydrogen content EN 4258, Aerospace series Metallic materials General organization of standardization Links between types of EN standards and their use EN 4259, Aerospace series Metallic materials Definition of general terms 1)1) Publish
17、ed as ASD-STAN Prestandard at the date of publication of this standard. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4800-008:2009 (E) 4 EN 4800-007, Aerospace series Titanium and titanium alloys T
18、echnical specification Part 007: Remelting stock 1)EN 9100, Aerospace series Quality management systems Requirements (based on ISO 9001:2000) and Quality systems Model for quality assurance in design, development, production, installation and servicing (based on ISO 9001:1994) EN 9133, Aerospace ser
19、ies Quality management systems Qualification Procedure for aerospace standard parts TR 2410, Aerospace series Metallic materials Relationship between dimensional standards and material standards 2)ASTM E 1320, Standard reference radiographs for titanium castings3) AMS 2750, Pyrometry 3)3 Terms and d
20、efinitions For the purposes of this document, the terms and definitions given in EN 4259 and the following apply. 3.1 batch same melt, heat treat and HIP cycle 3.2 HIP Hot Isostatically Pressed 3.3 melt a mass of homogeneous liquid metal from a single charge 3.4 remelt solid metal resulting from a s
21、ingle melt 3.5 parent cast a cast of remelting stock to be used for the production of castings 3.6 remelting stock metal supplied in cast or wrought form, the composition of which has been established by chemical analysis 2) Published as ASD-STAN Technical Report at the date of publication of this s
22、tandard. 3) Published by: American Society for Testing and Materials (ASTM), 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA, 19428-2959 USA. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN
23、4800-008:2009 (E) 5 4 Wording of order The order shall clearly indicate: quantities to be supplied; dates of delivery; material standard number; delivery condition and metallurgical code of products; dimensions and tolerances or reference to an appropriate dimensional standard; product designation,
24、when required; forwarding address; nature and type of packing, if required; definition and frequency of any special tests and their retest procedures, if required. 5 Health and safety Products in the delivery condition shall fulfil the health and safety laws of the area of the country when and where
25、 it is to be delivered. A product safety data sheet shall be available. 6 Technical requirements 6.1 General The product shall be manufactured in accordance with the requirements of the relevant material standard and the applicable requirements of this specification. A manufacturing schedule shall b
26、e established and applied in accordance with EN 2078. Product shall satisfy the requirements of the material standard and/or order and shall be free from irregularities prejudicial to the subsequent manufacture or use of this product. Not with standing previous acceptance complying with this materia
27、l standard, any product that is found, at a later stage, to contain such defects shall be rejected. Unless otherwise specified, the requirements in Tables 1 and 2 shall apply in conjunction with those of the relevant material standard. Table 1 relates to lines 1 to 29 (inclusive) of the material sta
28、ndard and Table 2 relates to lines 30 onwards in which the sub-line format is also used. Lines 2 to 98 may also be opened in line 100 if the material standard details specific qualification requirements. If a specific line number is not shown in Tables 1 and 2, the requirement is stated in the mater
29、ial standard and/or order. The requirements of the order and/or material standard shall over-ride the requirements of the technical specification. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4800-
30、008:2009 (E) 6 6.2 Qualification requirements Qualification requirements when invoked by the material standard and/or order are detailed in Tables 1 and 2. Unless otherwise agreed between the manufacturer and purchaser the qualification phase shall be run on the first fair batches. 6.3 Release requi
31、rements 6.3.1 Release tests Release testing shall be the responsibility of the manufacturer. The purchaser reserves the right to perform any of the inspections and/or tests required by the material standard and/or order. The test samples shall be representative of the product. When required the manu
32、facturer shall inform the purchaser of the planned dates for extraction of samples and release testing in order that these operations may be witnessed. Tables 1 and 2 detail the requirements for each line of the material standard. Unless otherwise specifically requested by the purchaser, a particula
33、r inspection and/or test for release shall be carried out if corresponding acceptance criteria and/or values are stated in the applicable material standard, but see also in 6.3.5. 6.3.2 Retests If the test procedure or test piece preparation is faulty, testing shall be re-applied at the original fre
34、quency after rectification of the original cause of failure. When failure cannot be attributed to faulty testing, or test piece preparation, further test samples shall be selected at twice the original frequency from the product, one of which shall be that on which the original results were obtained
35、 unless already withdrawn by the manufacturer after suitable identification of the cause of failure. If all retest results are satisfactory, the batch shall be accepted. If one or more tests are unsatisfactory, the batch shall be: rejected, or 100 % retested and the conforming products accepted, or
36、partially or fully re-heat treated if heat treatment can rectify the cause of the failure and tested as a completely new batch except for chemical composition, for which redetermination of hydrogen content is required. No product or test sample shall be re-heat treated more than twice. 6.3.3 Rejecti
37、on Any failure to meet the requirements of the material standard shall be cause for rejection. 6.3.4 Special tests Special tests may be required by the purchaser. In such cases, the nature of the test, method, frequency and technical requirements shall be specified on the order or inspection schedul
38、e and shall be mutually agreed by the manufacturer and purchaser. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4800-008:2009 (E) 7 6.3.5 Capability clause Where capability clause is invoked and whe
39、re sufficient statistical evidence exists, the test need not be carried out (unless specifically requested by the purchaser). However, this in no way reduces the obligations of the manufacturer to fulfil the requirements. If subsequent testing indicates that the product does not comply with the requ
40、irements, the batch shall be rejected. If sufficient statistical evidence does not exist, the test shall be carried out at a frequency agreed between the manufacturer and the purchaser. 6.3.6 Statistical process control Reduction in the extent of release testing, other than that defined in 6.3.5 abo
41、ve, may be negotiated with the purchaser on the basis of appropriate statistical process control and/or statistical data. 6.3.7 Inspection and test report The manufacturer shall furnish, with each delivery, a report conforming to the requirements of EN 2078 stating the following: manufacturers name
42、and address and, if appropriate, identification of the plant; order number; drawing and/or part number; material standard number; delivery condition and metallurgical code of the product; quantity and dimensions; manufacturing and inspection schedule reference; cast and batch number; batch and/or te
43、st samples heat treatment conditions; results of the tests and retests if any. 6.4 Traceability Each product shall be traceable to the cast, production batch and/or heat treatment batch at all stages of manufacture, testing and delivery. Copyright ASD-STAN Provided by IHS under license with AECMA No
44、t for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4800-008:2009 (E) 8 Table 1 Technical requirements for lines 1 to 29, where appropriate Material standard line reference No Title Requirements Frequency of testing 1 Material designation See EN 2032-1. 2 Chemical c
45、omposition The test samples used for chemical analysis shall be representative of the product and shall be determined on samples cast integrally with/or gated to castings and cut from solidified material. The method of chemical analysis shall be at the discretion of the manufacturer unless otherwise
46、 stated in the material standard or order. In cases of dispute, the method of chemical analysis shall be agreed between the manufacturer and purchaser preferably using existing chemical analysis standards. The measured chemical composition shall be stated on the certificate of conformance 1 per cast
47、 Specific requirements for hydrogen content: The hydrogen content shall be determined on each batch in the delivery condition in accordance with EN 3976. 1 per batch 3 Method of melting Method of melting consists of multiple melt using combination of non-consumable electrode, consumable electrode an
48、d cold hearth (electron beam or plasma arc) melting practices. The technical requirements are defined in the technical specification for remelt stock (EN 4800-007). 4.1 Form Pre-production and production castings 4.2 Method of production Castings Pre-production castings: Prior to commencing series production of a particular design, pre-production castings shall be produced in order to qualify the method of manufacture and equipment configuration and to demonstrate that the requirements of the purchaser can be met. The following requirements shall be