1、AMSC N/A FSC 5950 MIL-PRF-39010/20 20 September 2013 PERFORMANCE SPECIFICATION SHEET COILS, RADIO FREQUENCY, MOLDED, IRON CORE, FIXED, SURFACE MOUNT ESTABLISHED RELIABILITY test condition B. Both end terminations are to be immersed simultaneously. Rates of immersion, dwell time and withdrawal are hu
2、man controlled. Resistance to solvents: Test is not applicable Resistance to soldering heat: Method 210 of MIL-STD-202, test condition C. Mounting board to be SMD test substrate per this document. Test to be performed after final electrical in qualification subgroup II; or after final electrical in
3、group B subgroup 3 inspection. Overload: Test coil shall be mounted on SMD test substrate. Low temperature storage: Test coil shall be mounted on SMD test substrate. Vibration: Test coil shall be mounted on SMD test substrate. Mechanical shock: Test coil shall be mounted on SMD test substrate. Life:
4、 Test coil shall be mounted on SMD test substrate. Moisture resistance: Method 106 of MIL-STD-202; polarization voltage not required. Step 7a shall be performed during any five of the first eight cycles only. Step 7b is not applicable. Test coil shall be mounted on SMD test substrate. Provided by IH
5、SNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-39010/20 3 SMD test substrate: Material shall be a minimum of 95 percent alumina with metallized areas for part mounting. The substrate shall not cause, or contribute to, any failure in any test which it is u
6、sed. Coil mounting: Test coils are to be soldered to the SMD test substrate metallized areas using Sn63 solder, or equivalent, by any suitable method that does not exceed a temperature of 265C and a solder time period greater than five seconds. Table II electrical characteristics (final): For any su
7、bgroup test requiring coils to be mounted to an SMD test substrate, the electrical characteristics (final) measurements are to be referenced to the electrical characteristic (initial) measurements determined after the test coil is mounted to the test substrate. Part or identifying number (PIN): M390
8、10/20-* (dash number from table 1) Part marking: The parts shall be laser marked. The PIN number marked on the coil shall not include the M39010/ identifier due to body surface area size constraints. Remaining part marking requirements of MIL-PRF-39010 apply. Provided by IHSNot for ResaleNo reproduc
9、tion or networking permitted without license from IHS-,-,-MIL-PRF-39010/20 4 Table I Electrical characteristics (initial) and dash numbers Dash Number 1/ Inductance H 2/ Inductance Tolerance percent Q minimum 2/ Test frequency (MHz) Self Resonant Frequency min (MHz) 3/ DC resistance (25C) max (ohms)
10、 Rated DC current (mA) 4/ A1R1* A1R2* A1R3* A1R5* 1.10 1.20 1.30 1.50 5 5,10 5 5, 10 25 25 25 28 7.9 7.9 7.9 7.9 150 150 140 140 0.180 0.180 0.220 0.220 620 620 560 560 A1R6* A1R8* A2R0* A2R2* 1.60 1.80 2.00 2.20 5 5,10 5 5, 10 28 30 30 30 7.9 7.9 7.9 7.9 125 125 115 115 0.300 0.300 0.400 0.400 480
11、480 415 415 A2R4* A2R7* A3R0* A3R3* 2.40 2.70 3.00 3.30 5 5,10 5 5, 10 30 37 37 45 7.9 7.9 7.9 7.9 100 100 90 90 0.550 0.550 0.850 0.850 355 355 285 285 A3R6* A3R9* A4R3* A4R7* 3.60 3.90 4.30 4.70 5 5,10 5 5, 10 45 45 45 45 7.9 7.9 7.9 7.9 80 80 75 75 1.00 1.00 1.20 1.20 263 263 239 239 A5R1* A5R6*
12、A6R2* A6R8* 5.10 5.60 6.20 6.80 5 5,10 5 5, 10 45 50 50 50 7.9 7.9 7.9 7.9 65 65 60 60 1.80 1.80 2.00 2.00 195 195 185 185 A7R5* A8R2* A9R1* A100* 7.50 8.20 9.10 10.0 5 5,10 5 5, 10 50 55 55 55 7.9 7.9 7.9 7.9 55 55 50 50 2.70 2.70 3.70 3.70 160 160 144 144 See footnotes at end of table. Provided by
13、 IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-39010/20 5 Table I Electrical characteristics (initial) and dash numbers Dash Number 1/ Inductance H 2/ Inductance Tolerance percent Q minimum 2/ Test frequency (MHz) Self Resonant Frequency min (MHz) 3/ D
14、C resistance (25C) max (ohms) Rated DC current (mA) 4/ A110* A120* A130* A150* 11.0 12.0 13.0 15.0 5 5,10 5 5, 10 45 45 45 45 2.5 2.5 2.5 2.5 40 40 35 35 2.70 2.70 2.80 2.80 160 160 157 157 A160* A180* A200* A220* 16.0 18.0 20.0 22.0 5 5,10 5 5, 10 45 50 50 50 2.5 2.5 2.5 2.5 30 30 25 25 3.10 3.10 3
15、.30 3.30 149 149 144 144 A240* A270* 24.0 27.0 5 5, 10 50 50 2.5 2.5 20 20 3.50 3.50 140 140 1/ The complete dash number will include two additional letters (indicated by *). The first additional letter will indicate the inductance tolerance (e.g. J = 5%, K = 10%) and the second additional letter wi
16、ll indicate the product level (e.g. C, M, P, R, S) and will be added to the end of the dash number. 2/ Inductance and Q are tested using HP4194A with test fixture 16034E, or equivalent. 3/ Self resonant frequency tested using HP8753C, HP4292A, HP4194A or equivalent 4/ The rated dc current is based o
17、n 90C ambient temperature with a 15C rise. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-39010/20 6 Table II Electrical characteristics (final) Inspection Group Allowable variation from initial measurement Allowable percent from specified m
18、inimum value in electrical characteristics (initial) table Inductance (percent) DC resistance Self resonant frequency Q Qualification inspection Group II Group IV Group VI 2 5 5 (3% + 0.001 ohm) (2% +0.001 ohm) 1/ 1/ -10 -10 -15 Group B inspection Subgroup 1 Subgroup 3 Subgroup 4 5 2 5 (2% +0.001 oh
19、m) (3% + 0.001 ohm) 1/ 1/ -15 -10 -10 1/ The self-resonant frequency shall not be less than the value specified in table I Referenced documents: In addition to MIL-PRF-39010, this document references: MIL-STD-202 MIL-STD-883 Custodians: Preparing activity: Army CR Army - CR Navy EC Air Force 85 Agen
20、t: DLA CC DLA - CC Review activities: (Project 5950-2013-042) Army AR, CR4, MI Navy AS, CG, MC, OS, SH Air Force 19, 99 NOTE: The activities listed above were interested in this document as of the date of this document. Since organizations and responsibilities can change, you should verify the currency of the information above using the ASSIST Online database at https:/assist.dla.mil. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-