1、Designation: A1067 10 A1067/A1067M 12Standard Specification forTest Coupons for Steel Castings1This standard is issued under the fixed designation A1067;A1067/A1067M; the number immediately following the designation indicatesthe year of original adoption or, in the case of revision, the year of last
2、 revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This standardspecification defines the geometries of several separately-cast and integrally-cast test coupons for use ass
3、pecified in the applicable casting product or common requirements standard. This standard does not address procedures formolding, casting, heat treating, machining, or testing; these items are addressed as needed and appropriate by the applicableproduct or common requirements standard.NOTE 1The test
4、 coupons described herein were formerly defined in multiple casting specifications. Those standards now reference this documentwhen test coupons are required and should be consulted for applicable manufacturing and processing requirements.1.2 UnitsThe values stated in either SI units or inch-pound u
5、nits are to be regarded separately as standard. The values statedin each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining valuesfrom the two systems may result in non-conformance with the standard.1.3 This standard does not purport to ad
6、dress all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Ordering Information2.1 The applicable casting product
7、 standard or common requirements standard or both provide information regarding thenumber of coupons, molding materials to be used, heat treatment concerns, and other processing issues.3. Materials and Manufacture3.1 Unless specified otherwise by the purchaser, test coupons shall be poured from the
8、same heat, or from the same master heat,or from a sub-heat from the same master heat as the castings they are to represent.3.2 Except where specified herein or in the applicable product or common requirements standard, the details of the gating andrisering of the coupons are left to the discretion o
9、f the producer.3.3 The test coupons shall be processed and heat-treated as specified in the applicable product or common requirementsspecification. Except when specified otherwise, the portion of the test coupon from which the test specimen or specimens are tobe machined may be cut from the riser or
10、 feeder prior to heat treatment.4. Performance Requirements4.1 The primary function of the test coupon is to provide sound specimens useable for the determination of mechanical,physical, corrosion, or other properties of the metal used to produce the castings. If the test results conform to the stat
11、edrequirements, then the test coupon may be considered to have functioned acceptably.5. Other Requirements5.1 The casting producer shall establish procedures for the identification and traceability of the coupons from pouring throughtesting.6. Dimensions and Permissible Variations6.1 The drawings sh
12、own in this standard are not necessarily drawn to scale. The values shown in the tables constitute thedimensional requirements.1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.18on C
13、astings.Current edition approved May 1, 2010May 1, 2012. Published June 2010August 2012. Originally approved in 2010. Last previous edition approved in 2010 asA1067/A1067M10. DOI: 10.1520/A1067_A1067M-12.This document is not an ASTM standard and is intended only to provide the user of an ASTM standa
14、rd an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM
15、is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16.2 The drawings shown in this standard depict the more commonly used test coup
16、ons (Figs. 1-89). Other designs may besuitable when shown to produce acceptable properties or where agreed.7. Workmanship, Finish, and Appearance7.1 Care should be taken in the preparation and pouring of the molds to avoid the creation of inclusions or other anomalies inthe resulting test specimens.
17、8. Sampling8.1 Care shall be taken in the production and processing of the test coupon to assure that it is representative of the casting orcastings it represents.9. Number of Tests and Retests9.1 Sufficient test coupons shall be produced to provide the needed number of test specimens.Feature 4leg d
18、esign 2leg designin. mm in. mmA 214 60 214 60B 114 35 114 35C 2 50 2 50D 114 35 114 35E Optional Optional Optional OptionalW 838 215 378 100T * * * *L 5 min. 125 min. 5 min. 125 min.R1 12 12.5 12 12.5Rx 0 116 0 2 0 116 0 2*Use of and size of taper is at the discretion of the foundryFIG. 1 Test Coupo
19、ns for CastingsA1067/A1067M 12210. Certification10.1 Certification of the test coupon is not applicable, except when specified by the casting purchaser.11. Product Marking11.1 Marking of test coupons other than as necessary to provide the identification and traceability described in 6.1 is not neede
20、d,except where specified by the casting purchaser and agreed by the producer.Feature in. mmA 1 116 30B 5 to 11 125 to 280C 4 100D 12 to 312 13 to 90E 5 125F 4 116 105G 3 75H 1 12 40I 18 3FIG. 2 Test Coupon for Tension TestFeature in. mmA 1 14 35B 3 min.* 80 min.*C 1.00 25d 14 * 5*R 14 * 5* E 12 * 13
21、*Suggested Dimension *Plus finishing stockFIG. 3 Design and Dimensions of the ICI Test CouponA1067/A1067M 12312. Keywords12.1 Castings; steel; stainless steel; test coupon; test bar; heat; master heat; sub-heatFeature in. mmA 12 * 13*B 2 50C 2 14 60E 8* 200*F 3* 75*G 2 12 * 65*H 12 * 13*I 58 * 17*J
22、1 58 * 40 min.*K 14 min.* 7 min.*L 12 * 13*M 1 12 * 40*N 12* 300*R 38 10* Suggested dimension. * Plus finishing stock.FIG. 4 Cast-to-Shape Test Coupon for Tension Test SpecimenA1067/A1067M 124FIG. 5 Specimen from CastingA1067/A1067M 125NOTE 1Longitudinal axis and gage length of test specimen must be
23、 within cross-hatched zone.FIG. 6 Separately Cast BlockFeature in. mmA 1 12 min. 40 min.B 1 12 min. 40 min.C 1 12 min. 40 min.D 34 min. 20 min.FIG. 7 Prolongation Test CouponA1067/A1067M 126NOTE 1Longitudinal axis and gage length of test specimen must be within cross-hatched zone.FIG. 8 Thermal Buff
24、er PadsFeature In. MmL 4 100D 5 130FIG. 9 Cylindrical Coupon for Centrifugal CastingsA1067/A1067M 127SUPPLEMENTARY REQUIREMENTSThere are currently no supplementary requirements for this standard.APPENDIX(Nonmandatory Information)X1. MOLD MATERIALX1.1 A test coupon is used to demonstrate that the met
25、al can obtain the specified minimum properties, not that the casting hascertain properties. Thus it serves as a check of the composition and heat treatment. It is not (and cannot be) a check of the gatingand feeding system used for the casting or of any of the other processing variables.X1.2 Since t
26、he coupons are used to demonstrate the capability of the metal, any design that produces compliant properties shouldbe acceptable. There are a few exceptions:X1.2.1 The mold material used for the test coupons must not be a more powerful chill than the material used for the casting.(Chilling may prov
27、ide improved properties in some instances.) Conversely, test coupons may be produced using a mold materialthat is a less powerful chill (more insulating) than that used for the casting.X1.2.2 In the case of a heavy section casting, a heavy section coupon may be appropriate for thickness-sensitive al
28、loys. (This isrelated to the chilling issue; a thin section test coupon cools more quickly than a thick section casting.)X1.3 Pursuant to the above, a test specimen taken from a sacrificial casting and which produces test results that comply with therequirements of the applicable product standard sh
29、ould be considered as acceptable.SUMMARY OF CHANGESThese test coupons were previously defined in multiple other standards. Committee A01 has identified thelocationslocation of selected changes to these test coupon definitions this standard since the last issue(A1067/A1067M 10) that may impact the us
30、e of this standard. (Approved May 1, 2012.)(1) Fig. 1, (Keel block re-drawn; previously defined in A703, Fig. 2; A781, Fig. 1; A957, Fig. 2; and A985, Fig. 2.): Key lettersreplaced numeric dimensions in the sketch; SI values revised to be more rational, to reflect more realistic precision levels, an
31、d tobe compatible with A1058; and explanatory table deleted. Added Fig. 9 and revised 6.2 accordingly.(2) Fig. 2, (Round bar previously defined in A447, Fig. 1; A703, Fig. 3; A781, Fig. 2; A957, Fig. 3; and A985, Fig 3.): Key lettersreplaced numeric dimensions in the sketch and SI values revised to
32、be more rational, to reflect more realistic precision levels, andto be compatible with A1058.(3) Fig. 3, (ICI bar re-drawn; previously defined in A703, Fig. 1; A957, Fig. 1; and A985, Fig. 1.): Key letters replaced numericdimensions in the sketch and SI values revised to be more rational, to reflect
33、 more realistic precision levels, and to be morecompatible with A1058. Certain dimensions designated as “suggested.”(4) Fig. 4, (Investment cast bar previously defined in A703, Fig. 4; A781, Fig. 3; A957, Fig. 4; and A985, Fig. 4.): Key lettersreplaced numeric dimensions in the sketch and SI values
34、revised to be more rational, to reflect more realistic precision levels, andto be more compatible with A1058. Certain dimensions designated as “suggested.”(5) Fig. 5, (Attached test coupon previously defined in A703, Fig. S26.1; A781, Fig. S15.1; and A985, Fig. S26.1.)(6) Fig. 6, (Separately cast bl
35、ock previously defined in A703, Fig. S26.2; A757, Fig. 4, A781, Fig. 4; and A985, Fig. S26.2.)(7) Fig. 7, (Prolongation previously defined in A703, Fig. S26.3; A757, Fig. 6; A781; Fig. S15.3; and A985, Fig. S26.3.): Keyletters replaced numeric dimensions in the sketch and SI values revised to reflec
36、t more realistic precision levels.(8) Fig. 8, (Thermal buffer pad previously defined in A703, Fig. 26.4; A757, Fig. 5; A781, Fig. S15.4, and A985, Fig. S26.4.)A1067/A1067M 128ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentio
37、nedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee an
38、d must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting o
39、f theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box
40、 C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A1067/A1067M 129