1、Designation: A314 13aA314 15Standard Specification forStainless Steel Billets and Bars for Forging1This standard is issued under the fixed designation A314; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision.
2、 A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers stainless steel bil
3、lets and bars intended only for forging.2. Referenced Documents2.1 ASTM Standards:2A484/A484M Specification for General Requirements for Stainless Steel Bars, Billets, and ForgingsA751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsE527 Practice for Numbering Metals
4、and Alloys in the Unified Numbering System (UNS)2.2 Other Document:SAE J1086 Recommended Practice for Numbering Metals and Alloys33. Ordering Information3.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under thisspecification. Such req
5、uirements may include but are not limited to the following:3.1.1 Quantity (weight or number of pieces),3.1.2 Name of material: type or UNS designation (Table 1),3.1.3 Condition,3.1.4 Cross section (round, round-cornered square, etc.), and so forth),3.1.5 Form: bar or forging billet,3.1.6 Applicable
6、dimensions, including size, thickness, width, and length,3.1.7 ASTM designation and date of issue,3.1.8 Preparation for delivery (see Specification A484/A484M),3.1.9 Marking (see Specification A484/A484M), and3.1.10 Exceptions to the specification or special requirements.3.2 If possible, the intende
7、d use of the item should be given on the purchase order especially when the item is ordered for aspecific end use or uses.NOTE 1A typical ordering description is as follows: 10 000 lb, Type 420, annealed, round-cornered square billets, ASTM A314 dated forvalve parts.4. Manufacture4.1 AnnealingBlooms
8、 and billets of the 400 series of stainless steel types which are highly hardenable, such as Types 414,420, 431, 440A, 440B, and 440C, are commonly annealed prior to shipment and so specified in order to avoid the possibility ofthermal cracking. Those grades are not normally furnished in the as-roll
9、ed or as-forged condition. Other hardenable grades, suchas Types 403, 410, 416, and 416 Se, which may also require annealing, depending on their composition and size, are furnishedsuitable for cold cutting when so specified on the purchase order.1 This specification is under the jurisdiction ofASTM
10、Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.17on Flat-Rolled and Wrought Stainless Steel.Current edition approved Oct. 1, 2013July 15, 2015. Published October 2013July 2015. Originally approved in 1947. Last previous edition approved
11、 in 2013 asA314 13.A314 13a. DOI: 10.1520/A0314-13a.10.1520/A0314-15.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM
12、website.3 Available from Society of Automotive Engineers (SAE), 400 Commonwealth Dr., Warrendale, PA 15096-0001, http:/www.sae.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version.
13、Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section a
14、ppears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1TABLE 1 Chemical RequirementsUNSDesig-nationATypeNumberChemical Composition, %BCarbon Man-ganese Phos-phorus Sulfur Silicon Chromium Nickel Molyb-denum
15、Nitrogen OtherElementsAustenitic GradesS20161 . . . 0.15 4.006.00 0.040 0.040 3.004.00 15.0018.00 4.006.00 . . . 0.080.20 . . .S20200 202 0.15 7.5010.00 0.060 0.030 1.00 17.0019.00 4.006.00 . . . 0.25 . . .S20910 XM-19 0.06 4.006.00 0.040 0.030 1.00 20.5023.50 11.5013.50 1.503.00 0.200.40 Cb 0.100.3
16、0V 0.100.30S21800 . . . 0.10 7.009.00 0.060 0.030 3.504.50 16.0018.00 8.009.00 . . . 0.080.18 . . .S21900 XM-10 0.08 8.0010.00 0.060 0.030 1.00 19.0021.50 5.507.50 . . . 0.150.40 . . .S21904 XM-11 0.04 8.0010.00 0.060 0.030 1.00 19.0021.50 5.507.50 . . . 0.150.40 . . .S24000 XM-29 0.08 11.5014.50 0.
17、060 0.030 1.00 17.0019.00 2.253.75 . . . 0.200.40 . . .S24100 XM-28 0.15 11.0014.00 0.060 0.030 1.00 16.5019.00 0.502.25 . . . 0.200.45 . . .S28200 . . . 0.15 17.0019.00 0.045 0.030 1.00 17.0019.00 . . . 0.751.25 0.400.60 . . .S30200 302 0.15 2.00 0.045 0.030 1.00 17.0019.00 8.0010.00 . . . 0.10 . .
18、 .S30215 302B 0.15 2.00 0.045 0.030 2.003.00 17.0019.00 8.0010.00 . . . . . . . . .S30300 303 0.15 2.00 0.20 0.15 min 1.00 17.0019.00 8.0010.00 . . . . . . . . .S30323 303Se 0.15 2.00 0.20 0.06 1.00 17.0019.00 8.0010.00 . . . . . . Se 0.15 minS30400 304 0.08 2.00 0.045 0.030 1.00 18.0020.00 8.0010.5
19、0 . . . 0.10 . . .S30403 304L 0.030 2.00 0.045 0.030 1.00 18.0020.00 8.0012.00 . . . 0.10 . . .S30500 305 0.12 2.00 0.045 0.030 1.00 17.0019.00 10.5013.00 . . . . . . . . .S30800 308 0.08 2.00 0.045 0.030 1.00 19.0021.00 10.0012.00 . . . . . . . . .S30900 309 0.20 2.00 0.045 0.030 1.00 22.0024.00 12
20、.0015.00 . . . . . . . . .S30908 309S 0.08 2.00 0.045 0.030 1.00 22.0024.00 12.0015. . . . . . . . .S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.0024.00 12.0016.00 . . . . . . Cb + Ta 10 CS31000 310 0.25 2.00 0.045 0.030 1.50 24.0026.00 19.0022.00 . . . . . . . . .S31008 310S 0.08 2.00 0.045 0.030 1.5
21、0 24.0026.00 19.0022.00 . . . . . . . . .S31266 . . . 0.030 2.004.00 0.035 0.020 1.00 23.025.0 21.024.0 5.26.2 0.350.60 Cu 1.002.50W 1.502.50S31400 314 0.25 2.00 0.045 0.030 1.503.00 23.0026.00 19.0022.00 . . . . . . . . .S31600 316 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 0.10 . .
22、.S31603 316L 0.030 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 0.10 . . .S31635 316Ti 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 . . . Ti 5 (C+N)min; 0.70S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.0018.00 10.0014.00 2.003.00 . . . Cb + Ta 10 C min; 1.10S31700 317 0.08 2.00 0.
23、045 0.030 1.00 18.0020.00 11.0015.00 3.004.00 0.10S32100 321 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0012.00 . . . . . . Ti 5 C minS33228 . . . 0.040.08 1.00 0.020 0.015 0.030 26.0028.00 31.0033.00 . . . . . . Cb 0.61.0Ce 0.050.10Al 0.025S34700 347 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0013.00 . .
24、 . . . . Cb + Ta 10 CminS34800 348 0.08 2.00 0.045 0.030 1.00 17.0019.00 9.0013.00 . . . . . . Cb + Ta 10 Cmin; Ta 0.10S38031 . . . 0.015 2.0 0.020 0.010 0.3 26.028.0 30.032.0 6.07.0 0.150.25 Cu 1.01.5S38926 . . . 0.020 2.00 0.03 0.01 0.5 19.0021.00 24.0026.00 6.07.0 0.150.25 Cu 0.51.5Austenitic-Fer
25、ritic GradesS31803 . . . 0.030 2.00 0.030 0.020 1.00 21.023.0 4.56.5 2.53.5 00.080.20 . . .S32003 . . . 0.030 2.00 0.030 0.020 1.00 19.522.5 3.04.0 1.502.00 0.140.20 . . .S32101 . . . 0.040 4.006.00 0.040 0.030 1.00 21.022.0 1.351.70 0.100.80 0.200.25 Cu 0.100.80S32202 . . 0.030 2.00 0.040 0.010 1.0
26、0 21.5024.00 1.002.80 0.45 0.180.26 . . .S32205 . . . 0.030 2.00 0.030 0.020 1.00 22.023.0 4.56.5 3.03.5 0.140.20 . . .S32304 . . . 0.030 2.50 0.040 0.030 1.00 21.524.5 3.05.5 0.050.60 0.050.20 Cu 0.050.60S32750 . . . 0.030 1.20 0.035 0.020 0.80 24.026.0 6.08.0 3.05.0 0.240.32 Cu 0.50 maxS32760C . .
27、 . 0.030 1.00 0.030 0.010 1.00 24.0026.00 6.008.00 3.004.00 0.200.30 Cu 0.501.00W 0.501.00S32950 . . . 0.030 2.00 0.035 0.010 0.60 26.029.0 3.55.2 1.002.50 0.150.35 . . .S82441 . . . 0.030 2.504.00 0.035 0.005 0.70 23.025.0 3.04.5 1.002.00 0.200.30 Cu 0.100.80Ferritic GradesS42900 429 0.12 1.00 0.04
28、0 0.030 1.00 14.0016.00 . . . . . . . . . . . .S43000 430 0.12 1.00 0.040 0.030 1.00 16.0018.00 . . . . . . . . . . . .S43020 430F 0.12 1.25 0.06 0.15 min 1.00 16.0018.00 . . . 0.60D . . . . . .S43023 430F Se 0.12 1.25 0.06 0.06 1.00 16.0018.00 . . . . . . . . . Se 0.15 minS44600 446 0.20 1.50 0.040
29、 0.030 1.00 23.0027.00 . . . . . . 0.25 . . .S44625 XM-27E 0.010 0.40 0.020 0.020 0.40 25.0027.50 0.50 0.751.50 0.015 . . .Martensitic GradesS40300 403 0.15 1.00 0.040 0.030 0.50 11.5013.00 . . . . . . . . . . . .S41000 410 0.15 1.00 0.040 0.030 1.00 11.5013.50 . . . . . . . . . . . .S41400 414 0.15
30、 1.00 0.040 0.030 1.00 11.5013.50 1.252.50 . . . . . . . . .S41425 . . . 0.05 0.501.00 0.020 0.005 0.50 12.015.0 4.07.0 1.502.00 0.060.12 Cu 0.30S41600 416 0.15 1.25 0.06 0.15 min 1.00 12.0014.00 . . . 0.60D . . . . . .S41623 416Se 0.15 1.25 0.06 0.06 1.00 12.0014.00 . . . . . . . . . Se 0.15 minS42
31、000 420 0.15 min 1.00 0.040 0.030 1.00 12.0014.00 . . . . . . . . . . . .S42010 . . . 0.150.30 1.00 0.04 0.03 1.00 13.5015.00 0.350.85 0.400.85 . . . . . .S43100 431 0.20 1.00 0.040 0.030 1.00 15.0017.00 1.252.50 . . . . . . . . .A314 1524.2 ConditioningMaterial may be conditioned by chipping or gri
32、nding to remove injurious surface defects provided the depthof conditioning does not exceed that which will affect the surface condition or dimensions of the article to be forged from the baror billet.5. Chemical Composition5.1 The steel shall conform to the chemical composition prescribed in Table
33、1 for the respective grades.5.2 Methods and practices relating to chemical analysis required by this specification shall be in accordance with Test Methods,Practices, and Terminology A751.6. Dimensions6.1 Billets and bars shall conform to the shape and dimensions specified by the purchaser within a
34、permissible variation of65 %.7. General Requirements7.1 In addition to the requirements of this specification, all requirements of the current edition of Specification A484/A484Mshall apply. Failure to comply with the general requirements of Specification A484/A484M constitutes nonconformance with t
35、hisspecification.8. Keywords8.1 austenitic stainless steel; austenitic-ferritic duplex stainless steel; ferritic stainless steel; martensitic stainless steel; stainlesssteel bars; stainless steel billetsSUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard
36、since the last issue(A314 13a) that may impact the use of this standard. (Approved July 15, 2015.)(1) UNS S31266 to Table 1.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue (A31413)that may impact the use of this standard. (Approve
37、d Oct. 1, 2013.)(1) Added UNS S31803, UNS S32003, UNS S32101, UNS S32205, UNS S32304, and UNS S32750 to Table 1.(2) Corrected grades in UNS S32950 and UNS 32202.Committee A01 has identified the location of selected changes to this standard since the last issue (A31408)that may impact the use of this
38、 standard. (Approved May 1, 2013.)(1) Added UNS S82441 to Table 1.TABLE 1 ContinuedUNSDesig-nationATypeNumberChemical Composition, %BCarbon Man-ganese Phos-phorus Sulfur Silicon Chromium Nickel Molyb-denum Nitrogen OtherElementsS44002 440A 0.600.75 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . .
39、 . .S44003 440B 0.750.95 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S44004 440C 0.951.20 1.00 0.040 0.030 1.00 16.0018.00 . . . 0.75 . . . . . .S50100 501 0.10 min 1.00 0.040 0.030 1.00 4.006.00 . . . 0.400.65 . . . . . .S50200 502 0.10 1.00 0.040 0.030 1.00 4.006.00 . . . 0.400.65 . . .
40、 . . .A New designation established in accordance with Practice E527 and SAE J1086.B Maximum unless otherwise indicated.C % Cr + 3.3 % Mo + 16 % N $ 40.D At the option of the manufacturer.E Nickel plus copper combined; 0.50 max. Product analysis tolerance over the maximum limit for carbon and nitrog
41、en to be 0.002 %.A314 153ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infring
42、ement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard o
43、r for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views k
44、nown to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting A
45、STM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 154