1、Designation: A483/A483M 10 (Reapproved 2015)Standard Specification forSilicomanganese1This standard is issued under the fixed designation A483/A483M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revision. A numb
2、er in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers grades of silicomanganese.1.2 UnitsThe values stated in either SI units or inch-pound units are to be regarded s
3、eparately as standard. Thevalues stated in each system may not be exact equivalents;therefore, each system shall be used independently of the other.Combining values from the two systems may result in non-conformance with the standard.1.2.1 This specification is expressed in both inch-poundunits and
4、in SI units (within the text, the SI units are shown inbrackets); however, unless the purchase order or contractspecifies the applicable M specification designation (SI units),the inch-pound units shall apply.2. Referenced Documents2.1 ASTM Standards:2A1025 Specification for Ferroalloys and Other Al
5、loyingMaterials, General RequirementsE11 Specification for Woven Wire Test Sieve Cloth and TestSieves3. General Conditions for Delivery3.1 Materials furnished to this specification shall conform tothe requirements of Specification A1025, including any supple-mentary requirements that are indicated i
6、n the purchase order.Failure to comply with the general requirements of Specifica-tion A1025 constitutes nonconformance with this specification.In case of conflict between the requirements of this specifica-tion and Specification A1025, this specification shall prevail.4. Chemical Composition4.1 The
7、 various grades shall conform to the requirements asto chemical composition specified in Tables 1 and 2.4.2 The manufacturer shall furnish an analysis of eachshipment showing the percentage of each element specified inTable 1.4.3 Upon request of the purchaser, the manufacturer shallfurnish an analys
8、is for the elements specified in Table 2 on acumulative basis over a period mutually agreed upon by themanufacturer and the purchaser.5. Size5.1 The various grades are available in sizes as listed inTable 3.5.2 The sizes listed in Table 3 are typical as shipped fromthe manufacturers plant. These all
9、oys exhibit varying degreesof friability; therefore, some attrition may be expected intransit, storage, and handling.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.18 on Castings.Curr
10、ent edition approved Nov. 1, 2015. Published November 2010. Originallyapproved in 1963. Last previous edition approved in 2010 as A483 10. DOI:10.1520/A0483_A0483M-15.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual
11、Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1SUMMARY OF CHAN
12、GESCommittee A01 has identified the location of selected changes to this standard since the last issue (A483 04(2009) that may impact the use of this standard. (Approved Oct. 1, 2010.)(1) Converted designation to dual.(2) Corrected 1.2.(3) Added and editorially corrected SI units in Table 3.ASTM Int
13、ernational takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirel
14、y their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand sh
15、ould be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on St
16、andards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 61
17、0-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Chemical Requiremen
18、tsElement Composition, %Grade A Grade B Grade CManganese 65.068.0 65.068.0 65.068.0Silicon 18.521.0 16.018.5 12.516.0Carbon, max 1.5 2.0 3.0Phosphorus, max 0.20 0.20 0.20Sulfur, max 0.04 0.04 0.04TABLE 2 Supplemental Chemical RequirementsComposition, max, % All GradesArsenic 0.10Tin 0.010Lead 0.030C
19、hromium 0.50Nickel 0.20Molybdenum 0.10TABLE 3 Standard Sizes and TolerancesStandard Sizes (All Grades) TolerancesA8 in. by 4 in. 200 mm by 100mm90 lb 40 kg lump, max 10 % max passing 4 in. 100 mm sieve8 in. by 2 in. 200 mm by 50mm90 lb 40 kg lump, max 10 % max passing 2 in. 50 mm sieve4 in. by 1 in.
20、 100 mm by 25mm10 % max retained on 4 in. 100 mm sieve 10 % max passing 1 in. 25.0 mm sieve2 in. by14 in. 50 mm by 5mm10 % max retained on 2 in. 50 mm sieve 10 % max passing14 in. 5 mm sieve2 in. 50 mm by down. 10 % max retained on 2 in. 50 mm sieve 15 % max passing No. 8 5 mm sieveASpecifications of sieve sizes used to define tolerances in this specification are as listed in Specification E11.A483/A483M 10 (2015)2