ASTM A565 A565M-2010 Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service《高温用马氏体不锈钢棒的标准规格》.pdf

上传人:Iclinic170 文档编号:458787 上传时间:2018-11-25 格式:PDF 页数:4 大小:77.68KB
下载 相关 举报
ASTM A565 A565M-2010 Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service《高温用马氏体不锈钢棒的标准规格》.pdf_第1页
第1页 / 共4页
ASTM A565 A565M-2010 Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service《高温用马氏体不锈钢棒的标准规格》.pdf_第2页
第2页 / 共4页
ASTM A565 A565M-2010 Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service《高温用马氏体不锈钢棒的标准规格》.pdf_第3页
第3页 / 共4页
ASTM A565 A565M-2010 Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service《高温用马氏体不锈钢棒的标准规格》.pdf_第4页
第4页 / 共4页
亲,该文档总共4页,全部预览完了,如果喜欢就下载吧!
资源描述

1、Designation: A565/A565M 10Standard Specification forMartensitic Stainless Steel Bars for High-TemperatureService1This standard is issued under the fixed designation A565/A565M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the ye

2、ar of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers hot-

3、finished and cold-finishedmartensitic chromium steel bars for high-temperature service.The mechanical properties are developed by suitable heattreatment, as indicated for each alloy.1.2 Where strength at temperature is a factor, these steelsare generally limited to a maximum service temperature of12

4、00F 650C. For oxidation (scaling) resistance and at lowstresses, these steels are useful to 1450F 790C.1.3 This specification is expressed in both inch-pound unitsand SI units; however, unless the purchase order or contractspecifies the applicable M specification designation (SI units),the inch-poun

5、d units shall apply. The values stated in eitherinch-pound units or SI units are to be regarded separately asstandard. Within the text, the SI units are shown in brackets.The values stated in each system may not be exact equivalents;therefore, each system shall be used independently of the other.Com

6、bining values from the two systems may result in noncon-formance with the specification.2. Referenced Documents2.1 ASTM Standards:2A370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA484/A484M Specification for General Requirements forStainless Steel Bars, Billets, and Forgings

7、A751 Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel ProductsA994 Guide for Editorial Procedures and Form of ProductSpecifications for Steel, Stainless Steel, and RelatedAlloysE112 Test Methods for Determining Average Grain SizeE292 Test Methods for Conducting Time-for-Ruptu

8、reNotch Tension Tests of MaterialsE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)E562 Test Method for Determining Volume Fraction bySystematic Manual Point Count2.2 SAE Document:3SAE J1086 Recommended Practice for Numbering Metalsand Alloys (UNS)3. Ordering Informa

9、tion3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Such requirements may include, but are notlimited to, the following:3.1.1 Quantity (weight or number of pieces);3.1.2 Name of material (martensitic stainless

10、steel);3.1.3 Form (bar, etc.);3.1.4 Condition;3.1.5 Finish;3.1.6 Size, or applicable dimension including diameter,thickness, width, length, etc.;3.1.7 Grade designation (Table 1); and3.1.8 ASTM designation number and date of issue.4. General Requirements4.1 Product furnished to this specification sh

11、all conform tothe requirements of Specification A484/A484M, including anysupplementary requirements indicated in the purchase order.Failure to comply with the general requirements of Specifica-tion A484/A484M constitutes nonconformance with this speci-fication. In case of conflict between the requir

12、ements of thisspecification and SpecificationA484/A484M, this specificationshall prevail.5. Manufacture5.1 Heat Treatment:5.1.1 The product forms covered in this specification maybe furnished in one of the following conditions:5.1.1.1 Condition AAnnealed,1This specification is under the jurisdiction

13、 of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled and Wrought Stainless Steel.Current edition approved Oct. 1, 2010. Published October 2010. Originallyapproved in 1966. Last previous edition approved in 2009 as A5

14、65 05A(2009).DOI: 10.1520/A0565_A0565M-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from Soc

15、iety of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.1.2 Condition

16、 THeat treated (for machining),5.1.1.3 Condition HTHeat treated (for high-temperatureservice), or5.1.1.4 Condition HHeat treated.5.2 Condition and Finish:5.2.1 Bars may be furnished in one of the followinghot-finished conditions:5.2.1.1 Hot rolled, or5.2.1.2 Rough turned (rounds only).5.2.2 Bars may

17、 be furnished in one of the followingcold-finished conditions:5.2.2.1 Cold drawn,5.2.2.2 Centerless ground (rounds only), or5.2.2.3 Polished (rounds only).6. Chemical Requirements6.1 Each alloy covered by this specification shall conform tothe chemical composition specified in Table 1.6.2 Methods an

18、d practices relating to chemical analysisrequired by this specification shall be in accordance with TestMethods, Practices, and Terminology A751.7. Metallurgical Requirements7.1 The microstructure shall not contain more than 5 %delta-ferrite after full heat treatment as described in Table 2.Visual e

19、xamination for the volume fraction of delta ferrite ofvarious representative areas of examination is acceptable.When the visual estimation method indicates the delta ferritecontent is greater than the allowed limit, the manufacturer mayemploy Test Method E562 for determining the acceptability ofthe

20、lot.8. Mechanical Properties Requirements8.1 The material shall conform to the mechanical propertieslisted in Table 3 for the ordered condition.8.2 Material furnished in Condition A or T shall be capableof developing the room-temperature properties specified forCondition HT when subjected to heat tr

21、eatment as specified inTable 2.8.3 The yield strength shall be determined by the offsetmethod as described in the current edition of Test Methods andDefinitions A370.8.4 The impact strength shall be determined at 70 to 80F21 to 27C, by Charpy V-notch specimen TypeAas describedin Test Methods and Def

22、initions A370.8.5 Stress rupture testing of UNS S42226 shall be con-ducted as specified in Table 4 using a combination test bar inaccordance with Test Methods E292. Rupture must occur in thesmooth section of each test specimen. The test may bediscontinued after the time specified, provided the certi

23、ficationso notes. Stress rupture testing is not required on bars less than12 in. in diameter or thickness.TABLE 1 Chemical RequirementsGrade UNSDesig-nationACarbon Man-ganesePhos-phorusSulfur Silicon Chromium Nickel Molyb-denumVana-diumTungsten Nitrogen Alumi-numColum-biumCopperXM-32 S64152 0.080.15

24、 0.500.90 0.025max0.025max0.35 max 11.0012.50 2.003.00 1.502.00 0.250.40 . . . 0.010.05 . . . . . . . . . . . S41041 0.130.18 0.400.60 0.030max0.030max0.50 max 11.5013.00 0.50 max 0.20 max . . . . . . . . . 0.05max0.150.45. . . S41425 0.05 max 0.501.00 0.02 max 0.005max0.50 max 12.0015.00 4.007.00 1

25、.502.00 . . . . . . 0.060.12 . . . . . . 0.30max615 S41800 0.150.20 0.50 max 0.040max0.030max0.50 max 12.0014.00 1.802.20 0.50 max . . . 2.503.50 . . . . . . . . . . . .616 S42200 0.200.25 0.501.00 0.025max0.025max0.50 max 11.0012.50 0.501.00 0.901.25 0.200.30 0.901.25 . . . . . . . . . . . .619 S42

26、300 0.270.32 0.951.35 0.025max0.025max0.50 max 11.0012.00 0.50 max 2.503.00 0.200.30 . . . . . . . . . . . . . . . . . S42226 0.150.20 0.500.80 0.020 0.010 0.200.60 10.011.5 0.300.60 0.801.10 0.150.25 0.25 0.040.08 0.05 0.350.55.ANew designation established in accordance with Practice E527 and SAE J

27、1086.TABLE 2 Heat TreatmentNOTE 1 If straightened, a stress-relieving treatment is necessary. Stress-relieving temperature should be 50F 28C below the final temperingtemperature.NOTE 2Air or oil quenching depends on section size; heavier sections, approximately 3 in. 76.2 mm or greater, should be oi

28、l quenched. Suitablesynthetic quenchants may be substituted for oil.Grade UNS DesignationACondition Heat Treatment615 S41800 HT 1800 to 1850F 980 to 1010C, quench in air or oil and double temper at 1150F 620C min for 2 h min for eachtempering treatment. . . S41425 HT 1700 to 1800F 925 to 980C, quenc

29、h in air and temper at 1100F 595C min for 1 h, min, per inch thickness.616 S42200 HT 1875 to 1925F 1020 to 1050C, quench in air or oil and temper at 1150F 620C min for 2 h min.H 1875 to 1925F 1020 to 1050C, quench in air or oil and temper at 1250F 675C min for 2 h min.619 S42300 HT 1875 to 1925F 102

30、0 to 1050C, quench in air or oil and temper at 1150F 620C min for 2 h min.XM-32 K64152 HT 1825 to 1875F 995 to 1020C, quench in air or oil and temper at 1050F 565C min for 2 h min. . . S41041 HT 2075 to 2125F 1135 to 1165C for 2 h min, quench in air or oil and temper at 1250F 675C min for 2 h min. .

31、 . S42226 HT 2000 to 2500F 1095 to 1150C, quench in rapid air, oil, or polymer and temper at 1185F 640C min.ANew designation established in accordance with Practice E527 and SAE J1086.A565/A565M 1029. Keywords9.1 martensitic stainless steel; stainless steel bars; stainlesssteel billets; stainless st

32、eel forgings; temperature serviceapplicationshighSUPPLEMENTARY REQUIREMENTSThe following supplementary requirements shall apply only when specified by the purchaser in theinquiry, contract, and order. Details of these supplementary requirements shall be agreed upon by themanufacturer and purchaser.S

33、1. Non-Destructive ExaminationUNS S42200S1.1 MethodEach bar shall be subjected to NDE. Themethod used shall be: Eddy Current (ET), Magnetic Particle(MPI wet or dry), Liquid Penetrant (LPI), or Ultrasonic (UT),at the option of the vendor unless otherwise indicated in thepurchase order.S1.2 Acceptance

34、 CriteriaFor LPI or MPI, linear indica-tions (those indications longer than116 in. 1.5 mm with alength greater than three times their width) are unacceptable.For UT or ET, reject levels for linear indications shall be basedon the alarm response from a 0.012-in. 0.3-mm maximumdeep surface notch in a

35、calibration bar.S2. MicrostructureUNS S42200 and UNS S42226Condition H or HTS2.1 Metallographic inspection shall be performed at1003 magnification to determine the metallurgical structure,grain size, and delta ferrite content.S2.2 The microstructure shall be tempered martensite withno more than 1 %

36、delta ferrite.S2.3 The average grain size shall be 4 or finer. Themaximum size of individual grains, distributed at random, shallbe a 2. When the average grain size is 5 or finer, only theaverage size needs be reported. Grain size determination shallbe performed in accordance with Test Methods E112.

37、S3. Stress Rupture TestingUNS S42200 Condition HTS3.1 Stress rupture testing shall be conducted at 1200F650C and 26 000 psi 180 MPa using a combination test barin accordance with Test Methods E292. Rupture shall occur inthe smooth section of each test specimen. The test may bediscontinued after 25 h

38、 provided the certification so notes.Stress rupture testing is not required on bars less than12 in. indiameter or thickness.TABLE 3 Mechanical Property RequirementsAGradeUNSDesignationBConditionTensile Strength min,ksi MPaYield Strength, min,0.2 % Offset, ksiMPaElongation in 2in. 50 mm or4D, min, %R

39、eduction ofArea, min, %Impact at RoomTemperature,Charpy V-notch,min, ftlbf JBrinell HardnessC615 S41800 A . . . . . . . . . . . . . . . 311 maxHT 140 965 110 760 15 45 . . . 302 to 352. . . S41425 HT 120 825 95 655 15 45 50 70 321 max616 S42200 A . . . . . . . . . . . . . . . 248 maxT . . . . . 285m

40、axHT 140 965 110 760 13 30 8 11 302 to 352H 120 825 85 585 17 35 . . . 241 to 285619 S42300 A . . . . . . . . . . . . . . . 248 maxT . . . . . 285maxHT 140 965 110 760 8 20 8 11 302 to 352XM-32 K64152 A . . . . . . . . . . . . . . . 311 maxHT 145 1000 115 795 15 30 30 40 302 to 352. . . S41041 HT 11

41、5 795 75 515 15 50 20 27 277 max. . . S42226 A . . . . . . . . . . . . . . . 302 maxS42226 HT 140 965 100 690 15 45 8 11 321 maxAThe properties and associated heat treatments are those most commonly specified. For sections greater than 30 in.2193 cm2 in cross-sectional area, it is suggestedthat an a

42、greement be reached between purchaser and materials vendor.BNew designation established in accordance with Practice E527 and SAE J1086.CHardness taken at the surface for control purposes only. For acceptance purposes, tensile properties govern.TABLE 4 Rupture TestingUNS S42226Temperature F C 1200 65

43、0Stress ksi MPa, min. 33 230Time to rupture, h, min 25A565/A565M 103SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this specification since the last issue(A565/A565M-05a), which may impact the use of this specification. (Approved Oct. 1, 2010.)(1) Revised S1 and S

44、2 to cover UNS S42200. Added S3.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof

45、infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this st

46、andard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your

47、 views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).A565/A565M 104

展开阅读全文
相关资源
猜你喜欢
相关搜索

当前位置:首页 > 标准规范 > 国际标准 > ASTM

copyright@ 2008-2019 麦多课文库(www.mydoc123.com)网站版权所有
备案/许可证编号:苏ICP备17064731号-1