1、Designation: B249/B249M 12B249/B249M 14Standard Specification forGeneral Requirements for Wrought Copper and Copper-Alloy Rod, Bar, Shapes and Forgings1This standard is issued under the fixed designation B249/B249M; the number immediately following the designation indicates the yearof original adopt
2、ion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense
3、.1. Scope*1.1 This specification2 establishes the general requirements common to wrought copper and copper alloy rod, bar, shapes, andforgings which shall apply to Specifications B16/B16M, B21/B21M, B98/B98M, B124/B124M, B138/B138M, B139/B139M,B140/B140M, B150/B150M, B151/B151M, B187/B187M, B196/B19
4、6M, B283/B283M, B301/B301M, B371/B371M, B411/B411M, B441, B453/B453M, B455, B570, B870, B927/B927M, B929, B967/B967M, and B974/B974M to the extent referencedtherein.1.2 The chemical composition, physical and mechanical properties, and all other requirements not included in this specificationare pres
5、cribed in the product specification.1.3 UnitsThe values stated in either SI units or inch-pound units are to be regarded separately as standard. The values statedin each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining valuesfrom the two
6、 systems may result in non-conformance with the standard.1.3.1 Within the text the SI values are given in brackets.1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibilityof the user of this standard to establish appropriate
7、safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B16/B16M Specification for Free-Cutting Brass Rod, Bar and Shapes for Use in Screw MachinesB21/B21M Specification for Naval Brass Rod, Bar, and ShapesB98/B98M
8、Specification for Copper-Silicon Alloy Rod, Bar and ShapesB124/B124M Specification for Copper and Copper Alloy Forging Rod, Bar, and ShapesB138/B138M Specification for Manganese Bronze Rod, Bar, and ShapesB139/B139M Specification for Phosphor Bronze Rod, Bar, and ShapesB140/B140M Specification for C
9、opper-Zinc-Lead (Red Brass or Hardware Bronze) Rod, Bar, and ShapesB150/B150M Specification for Aluminum Bronze Rod, Bar, and ShapesB151/B151M Specification for Copper-Nickel-Zinc Alloy (Nickel Silver) and Copper-Nickel Rod and BarB154 Test Method for Mercurous Nitrate Test for Copper AlloysB187/B18
10、7M Specification for Copper, Bus Bar, Rod, and Shapes and General Purpose Rod, Bar, and ShapesB193 Test Method for Resistivity of Electrical Conductor MaterialsB194 Specification for Copper-Beryllium Alloy Plate, Sheet, Strip, and Rolled BarB196/B196M Specification for Copper-Beryllium Alloy Rod and
11、 BarB283/B283M Specification for Copper and Copper-Alloy Die Forgings (Hot-Pressed)B301/B301M Specification for Free-Cutting Copper Rod, Bar, Wire, and Shapes1 This specification is under the jurisdiction of ASTM Committee B05 on Copper and Copper Alloys and is the direct responsibility of Subcommit
12、tee B05.02 on Rod,Bar, Wire, Shapes and Forgings.Current edition approved April 1, 2012Sept. 1, 2014. Published May 2012September 2014. Originally approved in 1951. Last previous edition approved in 20112012 asB249/B249M 11.B249/B249M 12. DOI: 10.1520/B0249_B0249M-12. 10.1520/B0249_B0249M-14.2 For A
13、SME Boiler and Pressure Vessel Code applications see related Specifications SB-249 in Section II of that Code.3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the sta
14、ndards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurat
15、ely, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Dr
16、ive, PO Box C700, West Conshohocken, PA 19428-2959. United States1B371/B371M Specification for Copper-Zinc-Silicon Alloy RodB411/B411M Specification for Copper-Nickel-Silicon Alloy Rod and BarB441 Specification for Copper-Cobalt-Beryllium, Copper-Nickel-Beryllium, and Copper-Nickel-Lead-Beryllium Ro
17、d and Bar(UNS Nos. C17500, C17510, and C17465)B453/B453M Specification for Copper-Zinc-Lead Alloy (Leaded-Brass) Rod, Bar, and ShapesB455 Specification for Copper-Zinc-Lead Alloy (Leaded-Brass) Extruded ShapesB570 Specification for Copper-Beryllium Alloy (UNS Nos. C17000 and C17200) Forgings and Ext
18、rusionsB577 Test Methods for Detection of Cuprous Oxide (Hydrogen Embrittlement Susceptibility) in CopperB846 Terminology for Copper and Copper AlloysB858 Test Method for Ammonia Vapor Test for Determining Susceptibility to Stress Corrosion Cracking in Copper AlloysB870 Specification for Copper-Bery
19、llium Alloy Forgings and Extrusions Alloys (UNS Nos. C17500 and C17510)B900 Practice for Packaging of Copper and Copper Alloy Mill Products for U.S. Government AgenciesB927/B927M Specification for Brass Rod, Bar, and ShapesB929 Specification for Copper-Nickel-Tin Spinodal Alloy Rod and BarB967/B967M
20、 Specification for Copper-Zinc-Tin-Bismuth Alloy Rod, Bar and WireB974/B974M Specification for Free-Cutting Bismuth Brass Rod, Bar and WireD4855 Practice for Comparing Test Methods (Withdrawn 2008)4E3 Guide for Preparation of Metallographic SpecimensE8/E8M Test Methods for Tension Testing of Metalli
21、c MaterialsE18 Test Methods for Rockwell Hardness of Metallic MaterialsE29 Practice for Using Significant Digits in Test Data to Determine Conformance with SpecificationsE53 Test Method for Determination of Copper in Unalloyed Copper by GravimetryE54 Test Methods for Chemical Analysis of Special Bra
22、sses and Bronzes (Withdrawn 2002)4E62 Test Methods for Chemical Analysis of Copper and Copper Alloys (Photometric Methods) (Withdrawn 2010)4E75 Test Methods for Chemical Analysis of Copper-Nickel and Copper-Nickel-Zinc Alloys (Withdrawn 2010)4E76 Test Methods for Chemical Analysis of Nickel-Copper A
23、lloys (Withdrawn 2003)4E112 Test Methods for Determining Average Grain SizeE118 Test Methods for Chemical Analysis of Copper-Chromium Alloys (Withdrawn 2010)4E121 Test Methods for Chemical Analysis of Copper-Tellurium Alloys (Withdrawn 2010)4E255 Practice for Sampling Copper and Copper Alloys for th
24、e Determination of Chemical CompositionE290 Test Methods for Bend Testing of Material for DuctilityE478 Test Methods for Chemical Analysis of Copper AlloysE581 Test Methods for Chemical Analysis of Manganese-Copper Alloys3. Terminology3.1 For definitions of terms related to copper and copper alloys,
25、 refer to Terminology B846.3.2 Definitions of Terms Specific to This Standard:3.2.1 lengths, mill, nstraight lengths, including ends, that can be conveniently manufactured in the mill. Full length pieces areusually 10 or 12 ft 3000 or 3600 mm.3.2.2 lengths, stock, nstraight lengths that are mill cut
26、 and stored in advance of orders. They are usually 10 or 12 ft 3000 or3600 mm and subject to established length tolerances.4. Materials and Manufacture4.1 Materials:4.1.1 The material of manufacture shall be a form of the Copper or CopperAlloy UNS No. designation specified in the orderinginformation
27、 of such purity and soundness as to be suitable for processing into the products described in the product specification.4.1.2 When specified in the contract or purchase order, that heat identification or traceability is required, the purchaser shallspecify the details desired.NOTE 1Due to the discon
28、tinuous nature of the processing of castings into wrought products, it is not always practical to identify specific castinganalysis with a specific quantity of finished product.4.2 ManufactureThe product shall be manufactured by such hot working, cold working, and annealing processes as to producea
29、uniform wrought structure in the finished product.4.2.1 The product shall be hot or cold worked to the finished size and subsequently annealed or heat treated when required, andstraightened to meet the properties specified.4.2.2 EdgesThe edge shall be drawn, extruded, or rolled; refer to Edge Contou
30、rs in Section 6.4 The last approved version of this historical standard is referenced on www.astm.org.B249/B249M 1425. Chemical Composition5.1 The material shall conform to the chemical composition requirements prescribed in the product specification.5.1.1 Results of analysis on a product (check) sa
31、mple shall conform to the composition requirements within the permittedanalytical variance given in the product specification.5.2 The composition limits established for the Copper or Copper Alloy UNS No. designation specified in the productspecification do not preclude the presence of other elements
32、. By agreement between the manufacturer or supplier and the purchaser.Limits may be established and analysis required for unnamed elements.5.3 When material composition has been determined during the course of manufacture, analysis of the finished product by themanufacturer is not required.6. Dimens
33、ions, Mass and Permissible Variations6.1 GeneralFor the purpose of determining conformance with the dimensional requirements, any measured value outside thespecified limiting values for any dimension may be cause for rejection.6.1.1 The dimensions and tolerances for products referenced to this speci
34、fication, shall be as noted in the following paragraphsand tables, where the product specification is noted in the table heading.NOTE 2Blank spaces in the tolerance tables indicate either that the material generally is not available or that no tolerances are established.6.2 Diameter or Distance Betw
35、een Parallel SurfacesThe diameter of round sections or the distance between parallel surfacesin the case of other sections, except shapes, shall not vary from that specified by more than the amounts specified in Tables 1-12,incl, for the product, specification indicated:Table 1 and Table 2List the t
36、olerances for diameter or distance between parallel surfaces of cold-drawn rod in round,hexagonal and octagonal cross sections. Applicable product specifications and alloys are shown in the table titles.Table 3Lists the diameter tolerances for piston finish rod applicable to product specifications s
37、hown in the table title.Table 4 and Table 5List the tolerances for diameter or distance between parallel surfaces of as-extruded rod and bar applicableto the specifications and alloys shown in the table titles. These tolerances are applicable to round, hexagonal, and octagonal rodas well as square a
38、nd rectangular bar.TABLE 1 Tolerances for Diameter or Distance Between ParallelSurfaces of Cold-Drawn Rod(Applicable to Specifications B16/B16M, B21/B21M, B98/B98M (Cop-per Alloy UNS No. C65100), B124/B124M (Copper Alloy UNS Nos.C11000, C14500, C14700, C46400, C48200, C48500, C49250,C49255, C49260,
39、C49300, C49340, C49350, and C49360), B140/B140M, B301/B301M, B453/B453M, B927/B927M, B967/B967M, andB974/B974M.)Diameter or Distance BetweenParallel Surfaces, in. mmTolerances, Plus and Minus,A in. mmRound Hexagonal,OctagonalUp to 0.150 3.8, incl 0.0013 0.035 0.0025 0.06Over 0.150 to 0.500 3.8 to 12
40、, incl 0.0015 0.04 0.003 0.08Over 0.500 to 1.00 12 to 25, incl 0.002 0.05 0.004 0.10Over 1.00 to 2.00 25 to 50, incl 0.0025 0.06 0.005 0.13Over 2.00 50 0.15B 0.15B 0.30B0.30BTABLE 1 Tolerances for Diameter or Distance Between ParallelSurfaces of Cold-Drawn Rod(Applicable to Specifications B16/B16M,
41、B21/B21M, B98/B98M (Cop-per Alloy UNS No. C65100), B124/B124M (Copper Alloy UNS Nos.C11000, C14500, C14700, C46400, C46750, C48200, C48500,C49250, C49255, C49260, C49300, C49340, C49350, and C49360),B140/B140M, B301/B301M, B453/B453M, B927/B927M, B967/B967M, and B974/B974M.)Diameter or Distance Betw
42、eenParallel Surfaces, in. mmTolerances, Plus and Minus,A in. mmRound Hexagonal,OctagonalUp to 0.150 3.8, incl 0.0013 0.035 0.0025 0.06Over 0.150 to 0.500 3.8 to 12, incl 0.0015 0.04 0.003 0.08Over 0.500 to 1.00 12 to 25, incl 0.002 0.05 0.004 0.10Over 1.00 to 2.00 25 to 50, incl 0.0025 0.06 0.005 0.
43、13Over 2.00 50 0.15B 0.15B 0.30B 0.30BA When tolerances are specified as all plus or all minus, double the values given.B Percent of specified diameter or distance between parallel surfaces expressed tothe nearest 0.001 in. 0.01 mm.B249/B249M 143Table 6Lists the diameter tolerances for hot-rolled ro
44、und rod applicable to the porduct specification shown in the table title.Table 7, Table 8 and Table 9List the thickness tolerances for rectangular and square bar applicable to the product specificationsand alloys shown in the table titles.Table 10 and Table 11List the width tolerances for rectangula
45、r bar applicable to the product specifications and alloys shownin the table titles.Table 12Lists the diameter or distance between parallel surfaces tolerances for hot-forged rod and bar applicable to the productspecification shown in the title.6.3 LengthRod, bar, and shapes shall be furnished in sto
46、ck lengths with ends, unless the order specifies stock lengths, specificlengths, or specific lengths with ends as specified in Table 13, Table 14, and Table 15 for the product specification indicated:TABLE 2 Tolerances for Diameter or Distance Between ParallelSurfaces of Cold-Drawn Rod(Applicable to
47、 Specifications B98/B98M (Copper Alloy UNS No.C65500 and C66100), B124/B124M (Copper Alloy UNS Nos. C27450,C36500, C37000, C37700, C61900, C62300, C63000, C63200,C64200, C64210, C65500, C67500, C67600, C69300, C70620,C71520, and C77400), B138/B138M, B139/B139M, B150/B150M,B151/B151M, B196/B196M, B37
48、1/B371M, B411/B411M, and B441.)Diameter or Distance BetweenParallel Surfaces, in. mmTolerances, Plus and Minus,Ain. mmRound Hexagonal,OctagonalUp to 0.150 3.8, incl 0.002 0.050 . . .Over 0.150 to 0.500 3.8 to 12, incl 0.002 0.050 0.004 0.10Over 0.500 to 1.00 12 to 25, incl 0.003 0.08 0.005 0.13Over
49、1.00 to 2.00 25 to 50, incl 0.004 0.10 0.006 0.15Over 2.00 50 0.20B 0.20B 0.40B 0.40BTABLE 2 Tolerances for Diameter or Distance Between ParallelSurfaces of Cold-Drawn Rod(Applicable to Specifications B98/B98M (Copper Alloy UNS No.C65500 and C66100), B124/B124M (Copper Alloy UNS Nos. C27450,C36500, C37000, C37700, C61900, C62300, C63000, C63200,C64200, C64210, C65500, C67500, C67600, C69300, C70620,C71520, and C77400), B138/B138M, B139/B139M, B150/B150M,B1