1、Designation: B 435 06Standard Specification forUNS N06002, UNS N06230, UNS N12160, and UNS R30556Plate, Sheet, and Strip1This standard is issued under the fixed designation B 435; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the
2、 year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification2covers alloys UNS N06002, UNSN06230, UNS N12160, and UNS R30556* in the form ofrolled pla
3、te, sheet, and strip for heat-resisting and generalcorrosive service.1.2 The following products are covered under this specifi-cation:1.2.1 Sheet and StripHot- or cold-rolled, annealed, anddescaled unless solution annealing is performed in an atmo-sphere yielding a bright finish.1.2.2 PlateHot-rolle
4、d, solution-annealed, and descaled.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of
5、 the user of this standard to become familiarwith all hazards including those identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory lim
6、itations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 906 Specification for General Requirements for Flat-Rolled Nickel and Nickel Alloys Plate, Sheet, and StripE 527 Practice for Numbering Metals and Alloys (UNS)3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 pla
7、te, nmaterial316 in. (4.76 mm) and over inthickness.3.1.2 sheet and strip, nmaterial under316 in. (4.76 mm) inthickness.4. General Requirements4.1 Material furnished under this specification shall con-form to the applicable requirements of Specification B 906unless otherwise provided herein.5. Order
8、ing Information5.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Examples of such requirements include, but arenot limited to the following:5.1.1 Alloy,5.1.2 DimensionsThickness (in decimals of an inch),width, an
9、d length (inch or fraction of an inch),5.1.3 CertificationState if certification or a report of testresults is required (Specification B 906, section on MaterialTest Report an Certification),5.1.4 Optional RequirementPlate; state how plate is to becut (Specification B 906, Table titled Permissible V
10、ariations inwidth and Length of Sheared, Torch-Cut, or Abrasive-CutRectangular Plate),5.1.5 Purchase InspectionState which tests or inspectionsare to be witnessed (Specification B 906, section on Inspec-tion), and5.1.6 Samples for Product (Check) AnalysisState whethersamples should be furnished (Spe
11、cification B 906, section onSampling).6. Chemical Composition6.1 The material shall conform to the requirements as tochemical composition prescribed in Table 1.6.2 If a product (check) analysis is made by the purchaser,the material shall conform to the requirements specified inTable 1 and Specificat
12、ion B 906.1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved June 1, 2006. Published June 2006. Originallyapproved in 1966. La
13、st previous edition approved in 2003 as B 435 - 03.2For ASME Boiler and Pressure Vessel Code applications, see related Specifi-cation SB-435 in Section II of that Code.* New designation established in accordance with Practice E 527 and SAEJ1086, Practice for Numbering Metals and Alloys (UNS).3For re
14、ferenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, W
15、est Conshohocken, PA 19428-2959, United States.7. Mechanical Properties and Other Requirements7.1 Tensile PropertiesThe material shall conform to theroom temperature tensile properties prescribed in Table 2.7.2 Grain Size for Sheet and Strip:7.2.1 Annealed alloys UNS N06002, UNS N06230, andUNS R3055
16、6 sheet and strip shall conform to the grain sizerequirements given in Table 3.7.2.2 Annealed alloy UNS N12160 shall conform to anaverage grain size of ASTM No. 5 or coarser.8. Dimensions, Mass, and Permissible Variations8.1 WeightFor calculations of mass or weight, the follow-ing densities shall be
17、 used:Alloy Densitylb/in.3(g/cm3)N06002 0.297 (8.23)N06230 0.324 (8.97)R30556 0.297 (8.23)N12160 0.292 (8.08)8.2 Thickness:8.2.1 Sheet and StripThe thickness shall be measuredwith the micrometer spindle38 in. (9.525 mm) or more fromany edge for material 1 in. (25.4 mm) or over in width and atany pla
18、ce on material under 1 in. in width.8.3 Length:8.3.1 Sheet and StripSheet and strip may be ordered to cutlengths, in which case a variation of18 in. (3.175 mm) over thespecified length shall be permitted, with a 0 minus tolerance.8.4 Straightness:8.4.1 The edgewise curvature (depth of chord) of flat
19、 sheet,strip, and plate shall not exceed the product of 0.05 in.multiplied by the length in feet (0.04 mm multiplied by thelength in centimetres).8.4.2 Straightness for coiled strip is subject to agreementbetween the manufacturer and the purchaser.8.5 Squareness (Sheet)For sheets of all thicknesses
20、andwidths of 6 in. (152.4 mm) or more, the angle between adjacentsides shall be 90 6 0.15 (116 in. in 24 in. or 2.6 mm/m).8.6 FlatnessPlate, sheet, and strip shall be commerciallyflat.8.7 Edges:8.7.1 Plates shall have sheared, abrasive-cut or plasma-torch-cut edges as specified.8.7.2 Sheet and strip
21、 shall have sheared or slit edges.9. Product Marking9.1 Each plate, sheet, or strip shall be marked on one facewith the specification number, alloy, heat number, manufactur-ers identification, and size. The markings shall have nodeleterious effect on the material or its performance and shallbe suffi
22、ciently stable to withstand normal handling.9.2 Each bundle or shipping container shall be marked withthe name of the material; this specification number; alloy; thesize; gross, tare, and net weight; consignor and consigneeaddress; contract or order number; and such other informationas may be define
23、d in the contract or order.10. Keywords10.1 plate; sheet; strip; UNS N06002; UNS N06230; UNSN12160; UNS R30556TABLE 1 Chemical RequirementsElementComposition Limits, %UNS N06002 UNS N06230 UNS R30556 UNS N12160Nickel remainder remainder 19.022.5 remainderIron 17.020.0 3.0 max remainder 3.5 maxChromi
24、um 20.523.0 20.024.0 21.023.0 26.030.0Cobalt 0.52.5 5.0 max 16.021.0 27.033.0Molybdenum 8.010.0 1.03.00 2.54.0 1.0 maxTungsten 0.21.0 13.015.0 2.03.5 1.0 maxCarbon 0.050.15 0.050.15 0.050.15 0.15 maxSilicon 1.00 max 0.250.75 0.200.80 2.43.0Manganese 1.00 max 0.301.00 0.502.00 1.5 maxPhosphorus 0.04
25、max 0.030 max 0.04 max 0.030 maxSulfur 0.03 max 0.015 max 0.015 max 0.015 maxColumbium (N6) . . 0.30 max 1.0 maxTantalum . . 0.301.25 .Aluminum . 0.50 max 0.100.50 .Zirconium . . 0.0010.10 .Lanthanum . 0.0050.050 0.0050.10 .Nitrogen . . 0.100.30 .Boron . 0.015 max 0.02 max .Titanium . . . 0.200.80TA
26、BLE 2 Mechanical Property RequirementsUNSTensile Strength,min, ksi (MPa)Yield Strength(0.2 % Offset),min, ksi (MPa)Elongation in 2 in.(50.8 mm) or 4D,Amin, %N06002 95 (655) 35 (240) 35N06230B110 (760) 45 (310) 40R30556C100 (690) 45 (310) 40N12160D90 (670) 35 (240) 40AD refers to the diameter of the
27、tension specimen.BSolution annealed at a temperature between 2200 and 2275F (1204 and1246C) followed by a water quench or rapidly cooled by other means.CSolution annealed at 2100F (1150C) minimum.DSolution annealed at 1950F (1065C) minimum.TABLE 3 Grain Size for Annealed SheetThickness, in. (mm)ASTM
28、 Micrograin SizeNumber, maxAverage Grain,Diameter, max, in.(mm)0.125 (3.175) and under 3.0 0.0050 (0.127)Over 0.125 (3.175) 1.5 0.0084 (0.214)B435062APPENDIX(Nonmandatory Information)X1. HEAT TREATMENTX1.1 Proper heat treatment during or subsequent to fabri-cation is necessary for optimum performanc
29、e, and themanufacturer shall be consulted for details.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent r
30、ights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either f
31、or revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair heari
32、ng you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).B435063