1、Designation: B 517 05Standard Specification forWelded Nickel-Chromium-Iron-Alloy (UNS N06600, UNSN06603, UNS N06025, and UNS N06045) Pipe1This standard is issued under the fixed designation B 517; the number immediately following the designation indicates the year oforiginal adoption or, in the case
2、 of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification2covers welded, cold-worked, andannealed nickel-chromium-iron alloy (UNS
3、 N06600,*N06603, N06025, and N06045) pipe for general corrosiveservice and heat-resisting applications.1.2 This specification covers outside diameter and nominalwall pipe shown in ANSI B36.19. Pipe having other dimen-sions may be furnished provided such pipe complies with allother requirements of th
4、is specification.1.3 The values stated in inch-pound units are to be regardedas the standard.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including tho
5、se identified in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 775 Spec
6、ification for General Requirements for Nickeland Nickel Alloy Welded PipeB 899 Terminology Relating to Non-ferrous Metals andAlloys2.2 ANSI Standard:B36.19 Stainless Steel Pipe43. Terminology3.1 Terms defined in Terminology B 899 shall apply unlessdefined otherwise in this standard.4. General Requir
7、ement4.1 Material furnished in accordance with this specificationshall conform to the applicable requirements of the currentedition of Specification B 775 unless otherwise providedherein.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allrequirements that are necessar
8、y for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include, but are not limited to,the following:5.1.1 Alloy name or UNS number.5.1.2 ASTM designation and year of issue.5.1.3 Condition (temper).5.1.4 Dimensions:5.1.4.1 Nominal pipe s
9、ize or outside diameter and schedulenumber or nominal wall thickness.5.1.4.2 Length (specific or random).5.1.5 Quantity (feet or metres, or number of pieces).5.1.6 CertificationState if certification or a report of testresults is required.5.1.7 Samples for Product (Check) AnalysisState whethersample
10、s for product (check) analysis should be furnished.5.1.8 Purchaser InspectionIf the purchaser wishes towitness tests or inspection of material at the place of manu-facture, the purchase order must so state indicating which testsor inspections are to be witnessed.1This specification is under the juri
11、sdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Nov. 1, 2005. Published November 2005. Originallyapproved in 1970. Last previous edition approved in 2003 as B 5
12、17 03.2For ASME Boiler and Pressure Code applications see related SpecificationSB-517 in Section II of that Code.* New designation established in accordance with ASTM E 527 and SAE J1086,Practice for Numbering Metals and Alloys (UNS).3For referenced ASTM standards, visit the ASTM website, www.astm.o
13、rg, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036.1*A Summary of Chang
14、es section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Materials and Manufacture6.1 Pipe shall be made from flat-rolled alloy by an auto-matic welding process with no addition of filler metal
15、. Subse-quent to welding and prior to final heat treatment, the materialshall be cold worked either in both weld and base metal or inweld metal only.6.2 Pipe shall be furnished with a scale-free finish. Whenbright annealing is used, descaling is not necessary.7. Chemical Composition7.1 The material
16、shall conform to the requirements as tochemical composition prescribed in Table 1.7.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations in Specification B 775.8. Mechanical and Other Requirements8.1 Mechanical PropertiesT
17、he material shall conform tothe requirements for mechanical properties prescribed in Table2.8.2 Flattening TestPipe shall be capable of withstanding,without cracking, flattening under a load applied gradually atroom temperature until the distance between the platens is fivetimes the wall thickness.
18、The weld shall be positioned 90 fromthe direction of the applied flattening force.8.3 Nondestructive Test Requirements:8.3.1 Category 1Each piece of each lot shall be subject toone of the following four tests: hydrostatic, pneumatic (airunderwater), eddy current, or ultrasonic.8.3.2 Category 2Each p
19、iece in each lot shall be subjectedto a leak test and an electric test as follows:8.3.2.1 Leak TestHydrostatic or pneumatic (air underwa-ter).8.3.2.2 Electric TestEddy current or ultrasonic.8.4 The manufacturer shall have the option to test Category1 or Category 2 and select the nondestructive test
20、methods, ifnot specified by the purchaser.8.5 Transverse Guided Bend TestAt the option of the pipemanufacturer, the transverse guided bend test may be substi-tuted in lieu of the flattening test. Two bend specimens shall betaken transversely from pipe or the test specimens may betaken from a test pl
21、ate of the same material and heat as pipe,which is attached to the end of the cylinder and welded as aprolongation of the pipe longitudinal seam. One test is requiredfor each lot as defined in Specification B 775.9. Number of Tests9.1 Chemical AnalysisOne per lot.9.2 Mechanical PropertiesOne test pe
22、r lot.9.3 Flattening or Transverse Guided Bend TestOne testper lot.9.4 NondestructiveEach piece in each lot.10. Keywords10.1 welded pipe; N06600; N06603; N06025; N06045TABLE 1 Chemical RequirementsElementCompositionLimits,%Product (Check) AnalysisVariations, under min orover max, of theSpecified Lim
23、it of ElementN06600 N06603 N06025 N06045NickelA72.0 min Bal Bal 45.0 min 0.45Chromium 14.0 min 24.026.0 24.026.0 26.029.0 0.1517.0 max 0.25Iron 6.0 min 8.011.0 8.011.0 21.025.0 0.1010.0 max 0.10Manganese 1.0 0.15 max 0.15 max 1.0 max 0.03Carbon 0.15 max 20.0-40.0 0.150.25 0.050.12 0.01Copper 0.5 max
24、 0.50 max 0.10 max 0.3 max 0.03Silicon 0.5 max 0.50 max 0.5 max 2.53.0 0.03Sulfur 0.015 max 0.010 max 0.010 max 0.010 max 0.003Aluminum . 2.4-3.0 1.82.4 .Titanium . 0.010.25 0.10.2 .Phosphorus . 0.020 max 0.02 max 0.02 maxZirconium . 0.010.40 0.010.10 .Yttrium . 0.010.15 0.050.12 .Cerium . . . 0.030
25、.09ANickel shall be determined arithmetically by difference.TABLE 2 Mechanical Property RequirementsAlloyTensile Strength,min,psi (MPa)Yield Strength,0.2 % Offset,min, psi (MPa)Elongation in 2 in.or 50 mm,min, %N06600 80 000 (550) 35 000 (240) 30N06603 94 000 (650) 43 000 (300) 25N06025 98 000 (680)
26、 39 000 (270) 30N06045 90 000 (620) 35 000 (240) 30B517052SUMMARY OF CHANGESCommittee B02 has identified the location of selected changes to this standard since the last issue (B 517 03)that may impact the use of this standard.(1) Added Transverse Guided Bend Test.ASTM International takes no positio
27、n respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.
28、This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM I
29、nternational Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address sho
30、wn below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).B517053