1、Designation: B 705 05Standard Specification forNickel-Alloy (UNS N06625, N06219 and N08825) WeldedPipe1This standard is issued under the fixed designation B 705; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revi
2、sion. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers welded UNS N06625,* UNSN06219* and UNS N08825* pipe in the annealed condition(temper) for general c
3、orrosion applications.1.2 This specification covers pipe sizes in schedules shownin the Permissible Variations in Outside Diameter and WallThickness for Welded Pipe table of Specification B 775.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parenthes
4、es are forinformation only.1.4 The following precautionary caveat pertains only to thetest methods portion, Section 8, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of the userof this standard to b
5、ecome familiar with all hazards includingthose identified in the appropriate Material Safety Data Sheetfor this product/material as provided by the manufacturer, toestablish appropriate safety and health practices, and deter-mine the applicability of regulatory limitations prior to use.2. Referenced
6、 Documents2.1 ASTM Standards:2B 751 Specification for General Requirements for Nickeland Nickel Alloy Welded TubeB 775 Specification for General Requirements for Nickeland Nickel Alloy Welded PipeB 880 Specification for General Requirements for ChemicalCheck Analysis Limits for Nickel, Nickel Alloys
7、, andCobalt Alloys2.2 ASME Boiler and Pressure Vessel Code3Section IX Welding and Brazing Qualifications3. General Requirement3.1 Material furnished in accordance with this specificationshall conform to the applicable requirements of the currentedition of Specification B 775 unless otherwise provide
8、dherein.4. Definition of Terms4.1 Class 1Welded, cold-worked, annealed, and nonde-structively tested in accordance with 9.1.4.2 Class 2Welded, cold-worked, annealed, and nonde-structively tested in accordance with 9.2.4.3 Grade 1Annealed condition, relevant for UNSN06625.4.4 Grade 2Solution annealed
9、 condition, relevant forUNS N06625.5. Ordering Information5.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification.Examples of such requirements include, but are not limited to,th
10、e following:5.1.1 Alloy name or UNS number,5.1.2 ASTM designation,5.1.3 Dimensions:5.1.3.1 Pipe size,5.1.3.2 Length (specific or random),5.1.4 Class (see 3),5.1.5 Grade if UNS N06625 is specified. If neither grade ofN06625 is specified, grade 1 will be supplied.5.1.6 Quantity (feet or number of piec
11、es),5.1.7 Certification State if certification is required,5.1.8 Samples for Product (Check) AnalysisState whethersamples for product (check) analysis should be furnished (7.2),and1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct res
12、ponsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved May 1, 2005. Published June 2005. Originallyapproved in 1982. Last previous edition approved in 2003 as B 705 03.* New designation established in accordance with Practice E 527 and SAEJ 1086, Pra
13、ctice for Numbering Metals and Alloys (UNS).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Available from A
14、merican Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York, NY 10016-5990.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United State
15、s.5.1.9 Purchaser InspectionIf purchaser wishes to witnesstests or inspection of material at place of manufacture, thepurchase order must so state indicating which tests or inspec-tions are to be witnesses.6. Material and Manufacture6.1 Pipe shall be made from flat-rolled alloy by an auto-matic weld
16、ing process with no addition of filler metal. Subse-quent to welding and prior to final annealing, the material shallbe cold-worked in either the weld metal only or both weld andbase metal.6.2 Pipe shall be furnished with oxide removed. Whenbright annealing is used, descaling is not necessary.7. Che
17、mical Composition7.1 The material shall conform to the composition limitsspecified in Table 1. One test per lot shall be performed.7.2 If a product (check) analysis is performed by thepurchaser, the material shall conform to the product (check)analysis variations per Specification B 880.8. Mechanica
18、l Properties and Other Requirements8.1 Mechanical PropertiesThe material shall conform tothe mechanical properties specified in Table 2. One pipe per lotshall be examined.8.2 Flattening Test A section of pipe not less than 4 in.(102 mm) in length shall be capable of withstanding, withoutcracking, fl
19、attening under a load applied gradually at roomtemperature until the distance between the platens is five timesthe wall thickness. The weld shall be positioned 90 from thedirection of the applied flattening force. One pipe per lot shallbe examined.8.2.1 Superficial ruptures resulting from surface im
20、perfec-tions shall not be a cause for rejection.8.3 Transverse Guided Bend Test:8.3.1 At the option of the pipe manufacturer, the transverseguided bend test may be substituted in lieu of the flatteningtest. Two bend specimens shall be taken transversely from pipeor the test specimens may be taken fr
21、om a test plate of the samematerial and heat as pipe, which is attached to the end of thecylinder and welded as a prolongation of the pipe longitudinalseam. Except as provided in 8.3.2, one shall be subjected to aface guided bend and a second to a root guided bend test. Onespecimen shall be bent wit
22、h the inside surface of the pipeagainst the plunger and the other with the outside surface of thepipe against the plunger. Guided bend test specimens shall beprepared and tested in accordance with Section IX, Part QW160 of theASME Boiler and Pressure Vessel Code and shall beone of the types shown in
23、 QW462.2 and QW462.3 of that code.One bend test (two bend specimens) per lot shall be examined.8.3.2 For specified wall thicknesses38 in. (9.5 mm) andover, but less than34 in. (19 mm) side bend tests may be madeinstead of the face and root bend tests. For specified wallthicknesses34 in. (19) and ove
24、r, both specimens shall besubjected to the side bend tests. Side bend specimens shall bebent so that one of the side surfaces becomes the convexsurface of the bend specimen.8.3.3 The bend test shall be acceptable if no cracks or otherdefects exceeding18 in. (3 mm) in any direction be present inthe w
25、eld metal or between the weld and the pipe or plate metalafter bending. Cracks which originate along the edges of thespecimen during testing, and are less than14 in. (6.5 mm)measured in any direction shall not be considered.9. Nondestructive Testing9.1 Class 1Each piece in each lot shall be subjecte
26、d toone of the following four tests: hydrostatic, pneumatic (airunderwater), eddy current, or ultrasonic.9.2 Class 2Each piece in each lot shall be subjected to aleak test and an electric test as follows:9.2.1 Leak TestHydrostatic or pneumatic (air underwater).9.2.2 Electric Test Eddy current or ult
27、rasonic.9.3 The manufacturer shall have the option to test to Class1 or 2 and select the nondestructive test methods, if notspecified by the purchaser.10. Product Marking10.1 In addition to the requirements of Specification B 751,UNS N06625 tubes shall be marked with grade information.11. Keywords11
28、.1 N06219; N06625; N08825; welded pipeTABLE 1 Chemical RequirementsComposition Limits, %UNSN06625UNSN06219UNSN08825Ni 58.0 minABal 38.046.0Cr 20.023.0 18.0-22.0 19.523.5Fe 5.0 max 2.0-4.0 22.0 minAMo 8.010.0 7.0-9.0 2.5 3.5Cb + Ta 3.154.15 . .C 0.10 max 0.05 max 0.05 maxMn 0.50 max 0.50 max 1.0 maxS
29、i 0.5 max 0.70-1.10 0.5 maxP 0.015 max 0.020 max .S 0.015 max 0.010 max 0.03 maxAl 0.4 max 0.50 max 0.2 maxTi 0.40 max 0.50 max 0.61.2Co (if determined) 1.0 max 1.0 max .Cu . 0.50 max 1.53.0AElement may be determined arithmetically by difference.TABLE 2 Mechanical Property RequirementsAlloy GradeTen
30、sile Strengthmin, psi (MPa)Yield Strength0.2 % Offset,min, psi (MPa)Elonga-tionin2in.or50mm, min,%UNS N06625 1 (annealed) 120 000 (827) 60 000 (414) 30UNS N06625 2 (solutionannealed)A100 00 (690) 40 000 (276) 30UNS N06219 96 000 (660) 39 000 (270) 30UNS N08825 85 000 (586) 35 000 (240) 30ASolution a
31、nnealed at 2000F (1093C) minimum, with or without subsequentstablization anneal at 1800F (982C) minimum to increase resistance to sensiti-zation.B705052SUMMARY OF CHANGESCommittee B02 has identified the location of selected changes to this standard since the last issue (B 705 03)that may impact the
32、use of this standard.(1) Added Transverse Guided Bend Test option.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any s
33、uch patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invi
34、ted either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received
35、a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).B705053