ASTM C1136-2009 Standard Specification for Flexible Low Permeance Vapor Retarders for Thermal Insulation《隔热用柔性、低渗透蒸气阻化剂的标准规范》.pdf

上传人:inwarn120 文档编号:463498 上传时间:2018-11-27 格式:PDF 页数:4 大小:84.21KB
下载 相关 举报
ASTM C1136-2009 Standard Specification for Flexible Low Permeance Vapor Retarders for Thermal Insulation《隔热用柔性、低渗透蒸气阻化剂的标准规范》.pdf_第1页
第1页 / 共4页
ASTM C1136-2009 Standard Specification for Flexible Low Permeance Vapor Retarders for Thermal Insulation《隔热用柔性、低渗透蒸气阻化剂的标准规范》.pdf_第2页
第2页 / 共4页
ASTM C1136-2009 Standard Specification for Flexible Low Permeance Vapor Retarders for Thermal Insulation《隔热用柔性、低渗透蒸气阻化剂的标准规范》.pdf_第3页
第3页 / 共4页
ASTM C1136-2009 Standard Specification for Flexible Low Permeance Vapor Retarders for Thermal Insulation《隔热用柔性、低渗透蒸气阻化剂的标准规范》.pdf_第4页
第4页 / 共4页
亲,该文档总共4页,全部预览完了,如果喜欢就下载吧!
资源描述

1、Designation: C1136 09Standard Specification forFlexible, Low Permeance Vapor Retarders for ThermalInsulation1This standard is issued under the fixed designation C1136; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of las

2、t revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers vapor retarder

3、s for thermalinsulation, specifically, flexible materials with permeance of0.10 perm or lower and surface burning characteristics of 25flame spread/50 smoke or lower. These materials are intendedfor use at surface temperatures of 20 to 150F (29 to 66C).It does not cover mastics or barrier coatings a

4、pplied in liquidform, nor materials intended for use as weather barriers.1.2 This is a material specification and does not imply thatan installed system using these materials will provide thephysical properties specified in Section 6.1.3 This specification provides physical requirements forvapor ret

5、arders. Practice C755 provides assistance in solvingproblems related to moisture vapor transmission through ther-mal insulation materials.1.4 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI units that are provided

6、 for information onlyand are not considered standard.1.5 The following precautionary caveat pertains to the testmethods portion only, Section 10, of this specification: Thisstandard does not purport to address all of the safety concerns,if any, associated with its use. It is the responsibility of th

7、e userof this standard to establish appropriate safety and healthpractices and determine the applicability of regulatory limita-tions prior to use.2. Referenced Documents2.1 ASTM Standards:2C168 Terminology Relating to Thermal InsulationC755 Practice for Selection of Water Vapor Retarders forThermal

8、 InsulationD774/D774M Test Method for Bursting Strength of PaperC1258 Test Method for Elevated Temperature and Humid-ity Resistance of Vapor Retarders for InsulationC1263 Test Method for Thermal Integrity of Flexible WaterVapor RetardersC1338 Test Method for Determining Fungi Resistance ofInsulation

9、 Materials and FacingsD828 Test Method for Tensile Properties of Paper andPaperboard Using Constant-Rate-of-Elongation Appara-tus3D882 Test Method for Tensile Properties of Thin PlasticSheetingD1204 Test Method for Linear Dimensional Changes ofNonrigid Thermoplastic Sheeting or Film at ElevatedTempe

10、ratureE84 Test Method for Surface Burning Characteristics ofBuilding MaterialsE96/E96M Test Methods for Water Vapor Transmission ofMaterials2.2 TAPPI Standards:T461 Flame Resistance of Treated Paper and Paperboard3. Terminology3.1 DefinitionsDefinitions in Terminology C168 apply toterms used in this

11、 specification.4. Classification4.1 Classification of vapor retarders is based on vaporretardance and strength properties, as listed in Table 1.5. Materials and Manufacture5.1 It is possible to construct vapor retarders from anynumber of various films, foils, cloths, papers, and reinforce-ments, alo

12、ne or in combination, to achieve required perfor-mance.1This specification is under the jurisdiction of ASTM Committee C16 onThermal Insulation and is the direct responsibility of Subcommittee C16.33 onInsulation Finishes and Moisture.Current edition approved Nov. 1, 2009. Published December 2009. O

13、riginallyapproved in 1990. Last previous edition approved in 2008 as C113608. DOI:10.1520/C1136-09.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Doc

14、ument Summary page onthe ASTM website.3Withdrawn. The last approved version of this historical standard is referencedon www.astm.org.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.6. Physical Properties6.1 Maximum permeance for a sp

15、ecific type vapor retardershall be as shown in Table 1 when tested in accordance with10.1.6.2 All vapor retarders shall demonstrate a flame spread of25 or less and smoke developed of 50 or less when testing thefinish side (the side opposite that contacting the insulation) inaccordance with 10.2.6.3

16、Minimum tensile strength for a specific type vaporretarder shall be as shown in Table 1 when tested in accordancewith 10.3.6.4 Maximum dimensional change for a specific type vaporretarder shall be as shown in Table 1, when tested in accor-dance with 10.4.6.5 All type vapor retarders shall not sustai

17、n growth of fungiwhen tested in accordance with 10.5.6.6 All type vapor retarders shall not crack or delaminate attemperatures from 20 to 150F (29 to 66C) when tested inaccordance with 10.6.6.7 Minimum burst strength for a specific type vaporretarder shall be as shown in Table 1 when tested in accor

18、dancewith 10.7.6.8 Vapor retarders containing paper or paper products shallnot demonstrate an increase in char length of more than 20 %when tested in accordance with 10.8.6.9 All type vapor retarders shall not corrode or delaminate,nor demonstrate, after exposure, a permeance greater than themaximum

19、 allowable for the type being tested, when tested inaccordance with 10.9.7. Dimensions, Mass, and Permissible Variations7.1 Dimensions for roll or sheeted materials shall be asspecified by the purchaser.7.2 Tolerance for roll materials shall be 618 in. (63 mm) onwidth and +5, 0 % on length.7.3 Toler

20、ance for sheeted materials shall be 618 in. (63mm) on length and width.8. Workmanship, Finish and Appearance8.1 There shall be no defects in materials or workmanshipthat will affect the required performance of the vapor retarder.8.2 There shall be no defects that adversely affect theappearance of th

21、e vapor retarder.8.3 There shall be no defects that would affect ability of userto process material.9. Significance and Use9.1 Entrapment of water in thermal insulation caused bycondensation of water vapor that has penetrated into theinsulation is detrimental to the thermal resistance of theinsulati

22、on. For this reason, in certain installations wheretemperature and moisture conditions have the potential tocreate a vapor driving force toward the insulation, a deterrentto the passage of such vapor into the installed insulation needsto be provided. This is the primary function of the vaporretarder

23、.9.2 In addition to the function stated in 9.1, a vapor retarderhas the potential to provide physical protection and addedstrength to the insulation system.9.3 This specification is used to specify material by physicalproperty requirements that address the above prerequisites. Thedesigner of an insu

24、lation system, after determining the degreeof protection needed for the insulation, can use this specifica-tion to specify the appropriate type of vapor retarder when oneis required.10. Test Methods10.1 Water Vapor PermeanceTest water vapor permeancein accordance with Test Methods E96/E96M, Procedur

25、e A.10.2 Surface Burning CharacteristicsTest in accordancewith Test Method E84.10.3 Tensile Strength:10.3.1 Test the tensile strength of plastic sheet vapor retard-ers in accordance with Test Method D882, with results reportedin pounds per inch width of specimen (Newtons per millimetrewidth).10.3.2

26、Test the tensile strength of all other vapor retarders inaccordance with Test Method D828, with results reported inpounds per inch of specimen width (Newtons per millimetrewidth).10.3.3 Tested specimens shall be 2 in. (51 mm) wide with 1in. (25 mm) between jaws.10.3.4 Since the criterion for jaw bre

27、aks of Test MethodD828 (a break within 1 in. of jaw) cannot be used with theabove specimen configuration, employ visual inspection andappropriate care to ensure that the clamping action is notinitiating breakage.10.4 Dimensional Stability:10.4.1 Test dimensional stability in accordance with TestMeth

28、od D1204.10.4.2 Expose the specimens to a temperature of 150 6 4F(66 6 2C) for 24 h.TABLE 1 Physical Property RequirementsPhysical Properties Type I Type II Type III Type IV Type V Type VI Type VII Type VIIIPermeance, maxPerms (ngPa1s1m2)0.02 (1.15) 0.02 (1.15) 0.10 (5.75) 0.10 (5.75) 0.02 (1.15) 0.

29、03 (1.72) 0.01 (0.58) 0.02 (1.15)Burst Strength, minpsi (kPa)55 (380) 35 (240) 55 (380) 35 (240) 100 (690) 100 (690) 70 (483) 60 (414)Tensile, Machine Directionlb/in. width, min (N/mm width, min)45 (7.9) 30 (5.3) 45 (7.9) 30 (5.3) 40 (7.0) 20 (3.5) 11 (1.9) 8 (1.4)Tensile, Cross Directionlb/in. widt

30、h, min (N/mm width, min)30 (5.3) 20 (3.5) 30 (5.3) 20 (3.5) 60 (10.6) 30 (5.3) 10 (1.7) 7 (1.2)Dimensional Change, maxpercent0.50 0.50 0.50 0.50 4.5 2.6 1 1C1136 09210.5 Fungi Resistance:10.5.1 Test fungi resistance in accordance with Test MethodC1338.10.5.2 For all tests, inoculate three specimens

31、of the subjectsample. Growth on any of the three specimens constitutesfailure of the sample.10.5.3 Test both sides of laminated products that use dis-similar materials, with the exception of a metallic foil side,which need not be tested.10.5.4 Test either side of single layer products such aspolymer

32、ic films.10.6 Thermal Integrity of Flexible Water Vapor RetardersTest in accordance with Test Method C1263.10.7 Burst Strength of Vapor RetardersTest in accordancewith D774/D774MTest Method for Bursting Strength of Paper.10.7.1 Since only one side of the vapor retarder materialwill be exposed in ser

33、vice, only that side need be evaluated forburst strength.10.8 Permanence of Flame RetardancyTest in accordancewith TAPPI Test T461, Flame Resistance of Treated Paper andPaperboard.10.9 Elevated Temperature and Humidity Resistance ofVapor Retarders for InsulationTest in accordance with TestMethod C12

34、58.11. Sampling, Inspection, and Rejection of DefectiveMaterial11.1 A lot of material shall be considered to be the largestquantity of a specific vapor retarder received by the purchaserunder one order, or, it so designated by the manufacturer, thatquantity of products identified as the particular l

35、ot.11.2 Aunit of material shall be considered to be the smallestpackaged quantity of vapor retarder within a lot, that is, oneroll in a lot of rolls or one bundle of sheets in a lot of sheetedmaterial.11.3 Inspection shall consist of any tests for specificationconformance the user deems necessary. D

36、ue to the impracti-cality of performing some tests on an inspection basis, the useris entitled to request certification to specific test requirements.11.4 Incoming lots shall be sampled at a minimum rate of5 % of units received for inspection.11.5 If any nonconformance to specification is detectedwi

37、thin the 5 % sample, increase sampling to 10 % of the lot.11.6 If 50 % or more of the 10 % sampled units is deter-mined to be defective, the lot shall be considered unacceptable.11.7 It shall be left to the discretion of the user whether tocontinue sampling for acceptable material. In any case, unit

38、sfound defective shall be considered unacceptable and rejected.12. Certification12.1 When specified in the purchaser order or contract, thepurchaser shall be furnished certification that samples repre-senting each lot have been either tested or inspected as directedin this specification and the requ

39、irements have been met. Whenspecified in the purchaser order or contract, a report of theresults shall be furnished.12.2 Qualification RequirementsThe following require-ments are generally designated for initial product qualification:12.2.1 Permeance,12.2.2 Surface burning characteristics,12.2.3 Ten

40、sile strength,12.2.4 Dimensional stability,12.2.5 Fungi resistance,12.2.6 Thermal integrity,12.2.7 Burst Strength,12.2.8 Flame retardance permanence, and12.2.9 Elevated temperature and humidity resistance.12.3 Inspection RequirementsThe following requirementsare generally designated for acceptance s

41、ampling of lots ofqualified products:12.3.1 Dimensions, and12.3.2 Workmanship and appearance.13. Product Marking13.1 The packaged vapor retarder material shall bear iden-tification including the following information:13.1.1 Manufacturer,13.1.2 Product designation,13.1.3 Roll or sheet dimensions, and

42、13.1.4 Lot number.13.2 If required by the user, the packaged material shall beara marking of conformance to this specification, such as:ASTMC1136, Type _.13.3 If required by the user, material which has beenclassified as to surface burning characteristics in accordancewith Test Method E84 by an inde

43、pendent testing laboratoryagreed upon by both parties, shall bear the authorized label ormarking of that institution.14. Packaging14.1 Unless otherwise specified, the material shall be sup-plied in the manufacturers standard commercial package.15. Keywords15.1 flexible; low permeance; thermal insula

44、tion; vaporretardersC1136 093APPENDIX(Nonmandatory Information)X1. PERMEANCE UNDER OTHER THAN STANDARD TEST CONDITIONSX1.1 Transmission of water vapor through a vapor retarderis induced by a vapor pressure differential between sides of thevapor retarder, caused by different conditions of relativehum

45、idity from side to side.X1.2 The resistance of materials to the passage of watermay change under varying vapor driving conditions, such ashigher or lower temperatures, higher or lower relative humiditydifferentials, or like differentials at different ranges (that is,50/0 % RH as opposed to 75/25 %RH

46、).X1.3 For purposes of this specification, a standard testcondition is used, that of 73F (23C) with 50 % relativehumidity on one side and 0 % relative humidity on the other.X1.4 It is conceivable that a material that meets a require-ment for permeance under the test conditions of the specifica-tion

47、may not be adequate under actual conditions of use.X1.5 Since varying test conditions or conditions of use mayaffect performance (in this or any physical testing), a user maydeem it necessary to evaluate a vapor retarder for permeanceunder conditions more closely approximating actual serviceconditio

48、ns.X1.6 Considerations of such aspects as performance underconditions other than standard test conditions must be agreedupon between user and supplier and do not constitute a part ofthis specification.ASTM International takes no position respecting the validity of any patent rights asserted in conne

49、ction with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headqu

展开阅读全文
相关资源
猜你喜欢
相关搜索

当前位置:首页 > 标准规范 > 国际标准 > ASTM

copyright@ 2008-2019 麦多课文库(www.mydoc123.com)网站版权所有
备案/许可证编号:苏ICP备17064731号-1