1、Designation: D517 98 (Reapproved 2015)Standard Specification forAsphalt Plank1This standard is issued under the fixed designation D517; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parenthe
2、ses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope1.1 This specification covers asphalt plank used for bridgedecks as wel
3、l as for industrial floors.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of thi
4、s standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Classification2.1 Type I, aPlain, butt-edge asphalt plank for use as anindustrial flooring.2.2 Type I, bPlain, butt-edge asphalt plank for use on arailroad brid
5、ge as a waterproofing system protection layer.2.3 Type IIShip-lap edge asphalt plank for use on arailroad bridge as a waterproofing system protection layer.3. Ordering Information3.1 The user should state the type and dimensions in thepurchase order. If no type is specified, Type I shall befurnished
6、.4. Materials and Manufacture4.1 Asphalt plank shall be formed from a mixture of asphalt,fibers, modifiers, or a combination thereof, and mineral filler insuch a manner as to produce a uniformly dense mass.4.2 In the case of Type II asphalt plank, the edges of theplanks shall be of a lap joint confi
7、guration.5. Requirements5.1 AsphaltThe asphalt cement shall have such character-istics that when combined with the other ingredients, a plankmeeting the requirements of this specification will result.5.2 FiberThe fibrous material shall consist of finely di-vided threads or any natural or synthetic f
8、iber (except asbestos)from free lumps, and when used, shall be in a flocculentcondition. The fabric and fibrous material shall be free from allforeign materials.5.3 Mineral FillerThe mineral filler shall consist of finelycrushed slate, limestone, silica, or other aggregate that hasproven suitable fo
9、r use with asphalt cement in constructingpavement wearing surfaces.5.4 AbsorptionThe absorption of asphalt plank shall notexceed 1.0 % by weight when tested in accordance with 9.2.5.5 BrittlenessAt least 80 % of the specimens tested ofeach thickness of plank shall not show any detrimentalcracking wh
10、en tested in accordance with the method describedin 9.3.5.6 HardnessThe hardness of the plank, when tested inaccordance with the method prescribed in 9.5, shall meet thefollowing requirements:Temperature, Load, Penetration,C (F) kg (lb.) mm (mils)Type I, a 25 (77) 66 (30) 0.889 (35)Type I, b 25 (77)
11、 66 (30) 1.651 (65)Type II 25 (77) 66 (30) 1.651 (65)6. Dimensions, Mass, and Permissible Variations6.1 Asphalt plank shall have the dimensions specified orshown on the plans and determined in accordance with 9.4.Tolerances of 61.6 mm (116 in.) in thickness, 63.2 mm (18 in.)in width and 66.4 mm (14
12、in.) in length will be permitted.Plank sizes shall be 12 in. in width by either 24 in. or 48 in. inlength. Thickness shall be12 in.,34 in., 1 in., or 1.5 in.6.2 The asphalt plank shall conform to the following massrequirements.Specimen Thickness, Min Mass,mm (in.) kg/m2(lbs/ft2)12.7 (0.5) 0.2 (5)19
13、(0.75) 0.3 (7.5)1This specification is under the jurisdiction of ASTM Committee D04 on Roadand Paving Materials and is the direct responsibility of Subcommittee D04.34 onPreformed Joint Fillers, Sealers and Sealing Systems.Current edition approved July 1, 2015. Published October 2015. Originallyappr
14、oved in 1938. Last previous edition approved in 2008 as D517 98 (2008).DOI: 10.1520/D0517-98R15.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States125.4 (1.0) 0.4 (10)37.5 (1.5) 0.6 (15)Specimen Thickness, Min. Mass,mm (in.) kg/m2(lbs/ft2
15、)12.7 (0.5) 0.2 (5)19 (0.75) 0.3 (7.5)25.4 (1.0) 0.4 (10)37.5 (1.5) 0.6 (15)7. Workmanship, Finish, and Appearance7.1 The asphalt plank shall be free from defects affecting itsserviceability and appearance; it shall have straight edges andsquare corners.8. Sampling8.1 For the purpose of testing, thr
16、ee planks shall be selectedat random by the purchaser or his representative for each 1000planks or fraction thereof for each thickness included in theshipment.9. Test Methods9.1 ScopeThe four test methods listed in this section areintended to measure those attributes necessary to measure theability
17、of asphalt plank to provide a reasonably long andsatisfactory service. They are listed as follows:Test Method SectionAbsorption 9.2Brittleness 9.3Dimensions 9.4Hardness 9.59.2 Absorption:9.2.1 ScopeThis test method covers the determination ofwater absorption of asphalt plank.9.2.2 Significance and U
18、seThe ability of the plank towithstand significant water absorption is a measure of itsporosity and therefore its ability to withstand freezing andthawing conditions. It is a measure of its density.9.2.3 ProcedureAspecimen 50.8 by 152.4 mm (2 by 6 in.)shall be cut from the asphalt plank in such a ma
19、nner that alledges are freshly cut. The mass of the specimen shall beaccurately determined to the nearest 0.10 g, immersed in waterfor 24 h, removed, and the surface water wiped off with aslightly dampened cloth. The mass of the specimen shall thenbe determined to the nearest 0.10 g and the percent
20、absorptiondetermined. The time elapsing between the removal of thespecimen from the bath and its weighing shall not exceed 1min.9.3 Brittleness:9.3.1 ScopeThis test method covers the determination ofbrittleness of asphalt plank.9.3.2 Significance and UseThis test measures the abilityof the plank to
21、function in cold temperatures without detrimen-tal cracking.9.3.3 ProcedureTwo 152.4 by 152.4 mm (6 by 6 in.)specimens shall be cut from each of the three sample planksselected in accordance with Section 8. Five of those specimensshall be tested as follows: The specimens shall be conditionedand main
22、tained at a temperature of 0C (32F) for not less than3 h, and then tested immediately. A 0.9-kg (2-lb) weightdropped from a height of 508 mm (20 in.) onto a 5.7 mm(0.225 in.) diameter cylindrical pin shall not cause a crack toextend more than 37.5 mm (1.5 in.) from the point of impact.The point of i
23、mpact shall be as close to the center of the sampleas possible.9.4 Dimensions:9.4.1 ScopeThis test method covers the measurement ofdimensions to determine if the sample complies with the planor specification requirements.9.4.2 Significance and UseThis test method will ensurethat the finished product
24、 in place will afford an even, uniformbearing surface for subsequent construction.9.4.3 ProcedurePlank from each lot shall be examined forappearance, straightness of edges, and squareness of corners,and measured for width and length to an accuracy required inSection 6. They shall also be calipered a
25、t four scattered pointseach, with a micrometer having flat bearing surfaces at bothcontact points of not less than 6.4 mm (14 in.) in diameter. Theaverage of the readings shall be considered the thickness of theplank.9.5 Hardness:9.5.1 ScopeThis test method covers the determination ofhardness of asp
26、halt plank.9.5.2 Significance and UseThis test method measures theability of the asphalt plank to withstand serviceable loads andto ensure that the grade of asphalt used is proper to serve underwarm temperature without excessive deformation.9.5.3 ProcedureThe hardness of the plank shall be deter-min
27、ed by means of a McBurney penetrometer in which the pinin contact with the plank during the test is a hemispherical pin5.7 mm (0.225 in.) in diameter. The specimen shall be keptsubmerged in water maintained at the temperature specified fora time sufficient to ensure that the specimen has attained th
28、istemperature throughout. The test shall be made with thespecimen supported on a smooth, solid support. The tests shallbe performed upon samples at least 152.4 mm (6 in.) in lengthand of the full width of the plank. In each case the requiredload shall be applied for a period of 60 s, and the contact
29、 pinof the penetrometer shall be applied to the specimen at points37.5 mm (1.5 in.) or more from the edge of the specimen.9.6 Precision and Bias:9.6.1 PrecisionAttempts are being made to determine theprecision of the two tests in this standard that result in anumerical value.NOTE 1Since a precision
30、estimate for this standard has not beendeveloped, this test method should be used for research and informationalpurposes only. Therefore, this standard should not be used for theacceptance or rejection of a material for purchasing purposes.9.6.2 BiasNo statement can be made on the bias of thetests i
31、n this standard because no material having an acceptedreference value is available.10. Keywords10.1 asphalt plank; bridge deck waterproofing; protectioncourse; industrial flooringD517 98 (2015)2ASTM International takes no position respecting the validity of any patent rights asserted in connection w
32、ith any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible tec
33、hnical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful considera
34、tion at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr H
35、arbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 98 (2015)3