1、Designation: D 2838 09Standard Test Method forShrink Tension and Orientation Release Stress of PlasticFilm and Thin Sheeting1This standard is issued under the fixed designation D 2838; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision
2、, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This test method covers the determination of the shrinktension and related characteristics, that is, sh
3、rink force andorientation release stress, of heat-shrinkable plastic film andsheeting of less than 1.0 mm (0.04 in.) thickness. Twoprocedures are described that permit the measurement of shrinkforces at predetermined temperatures. They are as follows:1.1.1 Procedure A is designed to measure the maxi
4、mumforce exerted by a specimen that is totally restrained fromshrinking as it is heated rapidly to a specific temperature.1.1.2 Procedure B is designed to measure the maximumforce exerted by a specimen that is permitted to shrink apredetermined amount prior to restraint while being heatedrapidly to
5、a specific temperature.1.2 Orientation release stress can be determined from thedata obtained using Procedure A.1.3 The values stated in SI units are to be regarded as thestandard. The values in parentheses are for information only.1.4 This standard does not purport to address all of thesafety conce
6、rns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.NOTE 1Film has been arbitrarily defined as sheeting having nominalthickness not gre
7、ater than 0.25 m (0.010 in.).NOTE 2There is no known ISO equivalent to this test method.2. Referenced Documents2.1 ASTM Standards:2D 618 Practice for Conditioning Plastics for TestingD 883 Terminology Relating to PlasticsD 4000 Classification System for Specifying Plastic Mate-rialsD 5947 Test Metho
8、ds for Physical Dimensions of SolidPlastics SpecimensD 6287 Practice for Cutting Film and Sheeting Test Speci-mensD 6988 Guide for Determination of Thickness of PlasticFilm Test SpecimensE 2251 Specification for Liquid-in-Glass ASTM Thermom-eters with Low-Hazard Precision Liquids3. Terminology3.1 De
9、finitions of Terms Specific to This Standard:3.1.1 orientation release stress, nthe maximum shrinktension developed by a film in a specified direction throughoutits range of shrink temperatures while totally restrained fromshrinking.3.1.2 shrink force, nthe force per original unit widthdeveloped by
10、a film in a specified direction and at a specifiedtemperature in its attempt to shrink while under restraint.3.1.3 shrink tension, nthe force per original averagecross-sectional area developed by a film in a specified directionand at a specified temperature in its attempt to shrink whileunder restra
11、int.3.2 Definitions:3.2.1 For definitions of terms used in this test method, referto Terminology D 883.4. Summary of Test Method4.1 A 25.4-mm (1-in.) wide strip of film or sheeting isclamped in the arms of a shrink tension holder (see Fig. 1), onearm of which contains a strain gage. The holder is im
12、mersed ina hot bath and the force exerted by the film is measured by thestrain gage. The data is collected by a data acquisition device.The tests may be carried out with or without free shrinkage ofthe material before restraint.5. Significance and Use5.1 As a result of the manufacturing process, int
13、ernalstresses are locked into the film and these can be released byheating. For any given type of film or sheeting, the tempera-tures at which shrinkage will begin are related to processingtechniques employed to manufacture the film and also may berelated to a phase transition in the base resin.1Thi
14、s test method is under the jurisdiction of ASTM Committee D20 on Plasticsand is the direct responsibility of Subcommittee D20.19 on Film and Sheeting.Current edition approved May 1, 2009. Published June 2009. Originallyapproved in 1969. Last previous edition approved in 2008 as D 2838 - 08.2For refe
15、renced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Cop
16、yright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2 Shrink tension affects the appearance and performanceof a film in a shrink-packaging application. It may also be usedto determine the degree and direction of orientation. Theorientation
17、 exerts a great influence upon important physicalcharacteristics such as tensile strength, stiffness, tear resis-tance, and impact strength.5.3 Data from Procedure A are most useful for determiningthe degree and direction of orientation, orientation releasestress, and the maximum force that the film
18、 can exert at a giventemperature.5.4 Since, in actual applications, film is seldom, if ever,totally restrained, data from Procedure B are useful in estimat-ing the force an item to be packaged will actually receive andin predicting the appearance of packaged items.5.5 The characterization of shrink
19、tension as a function oftemperature, and the resultant determination of orientationrelease stress and its corresponding temperature, is usuallycarried out only for a particular material of specified thicknessfor a defined fabrication process. For product developmentpurposes, quality control and dete
20、rmination of conformity tospecification limits, the measurement of shrink tension at onlyone or two specified temperatures is normally sufficient.5.6 Before proceeding with this test method, reference shallbe made to the specification of the material being tested. Anytest specimen preparation, condi
21、tioning, dimensions, or testingparameters, or combination thereof, covered in the relevantASTM material specification shall take precedence over thosementioned in this test method. If there are no relevant ASTMmaterial specifications, then the default conditions apply. Table1 of Classification Syste
22、ms D 4000 lists the ASTM materialspecifications that currently exist6. Apparatus6.1 Shrink Tension Holder3A suggested design is por-trayed in Fig. 1 and Fig. 2.6.2 Strain Gage Conditioner, four-arm bridge, preferable.6.3 Data Acquisition Device Electronic, digital or chartrecorder pen having a respo
23、nse of no more than 30 ms from 10to 90 % of full-scale deflection, chart width of at least 100 mmis preferable.6.4 Specimen Cutter For the apparatus and techniques forcutting film and sheeting used in this test method, refer toPractice D 6287.6.5 Constant-Temperature Liquid Bath, capable of control-
24、ling accurately to 60.5C and covering the range of interest,usually from 50 to 175C.3The sole source of supply of the Shrink Tension Holder known to the committeeat this time is Standard Scientific Supply Company, 105 West Butternut Road,Hellertown, PA180555, ph: 610-8387500. If you are aware of alt
25、ernative suppliers,please provide this information to ASTM International Headquarters. Your com-ments will receive careful consideration at a meeting of the responsible technicalcommittee,1which you may attend.FIG. 1 Design for Shrink Tension HolderD28380926.6 Thermometer, covering the range of inte
26、rest and con-forming to the requirement of Specification E 2251.6.7 Liquid Bath, which will not plasticize or react withspecimens. Polyethylene glycol, glycerin, and water have beenfound to have wide applicability. Silicone oils are useful forsamples requiring temperatures above 175C.6.8 ThicknessSp
27、ecimen thickness shall be determinedusing a micrometer or other suitable thickness gauge inaccordance with Test Methods D 5947 or D 6988, as appropri-ate for the specimen thickness.7. Test Specimens7.1 The test specimens shall consist of strips of uniformwidth and thickness. The width of the specime
28、ns shall be 25.46 0.2 mm (1.0 6 0.01 in.).7.2 Length of Test Specimens:7.2.1 Specimens for ProcedureAshall be at least 127 mm (5in.) in length.7.2.2 Length of specimens for Procedure B is dependentupon the amount of shrink desired prior to restraint. At least 50mm shall be allowed for clamping. The
29、remaining lengthrequired can be calculated by solving for L in the followingequation:L 5 d/100 2 s! 3 100 (1)where:L = specimen length required between clamps, mm or in.,d = distance between clamps, mm or in., ands = percent shrink desired prior to restraint.Measure a distance equivalent to L, leavi
30、ng at least 25.4 mm(1 in.) at either end of the strip for clamping and mark thebeginning and termination of the distance with a line perpen-dicular to the edge and across the width of the strip.7.3 Measure the thickness of the specimen to the nearest0.0025 mm (0.0001 in.) at a minimum of four positi
31、ons, but atleast at each 25.4 mm (1 in.) along the length of the specimenthat will be between the clamps. Record the thicknesses.Calculate and record their average.7.4 For each measurement of shrink tension at a giventemperature, test at least four specimens from each direction,machine and transvers
32、e, of the test sample.8. Preparation of Apparatus8.1 Set up constant-temperature bath and equilibrate at thetemperature chosen for the test. Shrink tension will normallybe observed near the softening temperature of polymericmaterial.8.2 Balance and set the data acquisition device at zero inaccordanc
33、e with the manufacturers instructions.9. Calibration9.1 Zero shrink holder with no load on shrink arm.9.2 Place a weight (normally 4.45 N, 454 gf, 1 lbf) equal tothe chosen full-scale value for the measurements to be made onthe shrink arm. Adjust the data acquisition device to full scalein accordanc
34、e with the manufacturers instructions.9.3 Check linearity by placing weights of less mass on thearm. If the response is non-linear, have the equipment repairedto make response linear.9.4 Re-check the zero of the shrink holder with no load onthe shrink arm.10. Conditioning10.1 ConditioningCondition t
35、he test specimens at 23 62C (73.4 6 3.6F) and 50 6 10 % relative humidity for notless than 40 h prior to test in accordance with Procedure A ofPractice D 618, unless otherwise specified by agreement or therelevant ASTM material specification. In cases of disagree-ment, the tolerances shall be 61C (6
36、1.8F) and 65%relative humidity.FIG. 2 Circuit Diagram for Shrink, Tension HolderD283809311. Procedure ATotally Restrained11.1 Clamp the first specimen in the holder under theminimum positive loading force achievable. Under no circum-stances shall it exceed the maximum force observed afterimmersion o
37、f the specimen. The holder must be at ambienttemperature.11.2 Initiate data collection before immersing holder intobath. Immerse the shrink holder and specimen into the bath,taking special care to lower it in such a manner that thespecimen remains in a horizontal position. Immerse smoothlyand quickl
38、y without bumping or jerking the holder. Keep thespecimen in the bath long enough to reach a peak or plateauand 2 to 3 s thereafter.NOTE 3Slight variations from the horizontal will generally produce anegligible error. The error, however, will increase in significance as theshrink force approaches ze
39、ro. A jig may be used to aid in maintaining theproper alignment of the holder while immersing the specimen.11.3 Stop data collection and immerse the holder in a beakerof cold water until it returns to ambient temperature. Thenremove the specimen.11.4 Repeat 11.1-11.3 for each specimen in the set.11.
40、5 Repeat 11.1-11.4 for temperature increments of nomore than 10C through the shrink temperature range of thefilm or sheeting under test. This is usually the softeningtemperature range of the material.12. Procedure BPredetermined Shrink BeforeRestraint12.1 Clamp the specimen in the holder so that the
41、 linesmarked in 7.2.2 coincide with the inside edges of the clamps.12.2 Follow the instructions given in 11.1-11.5.13. Calculation13.1 Record the maximum force (peak or plateau whicheveris greater) to the nearest 0.045 N (0.01 lbf or 4.5 gf).13.2 Shrink ForceDivide the maximum force by thespecimen w
42、idth to obtain shrink force. Express shrink force ineither newtons per metre or pounds-force per inch.13.3 Shrink TensionDivide the maximum force in new-tons (or pounds force) by the product of the average thicknessin millimetres (inches) and the specimen width in millimetres(inches) to obtain the s
43、hrink tension in pascals.14. Orientation Release Stress14.1 Prepare graphs of shrink tension as a function oftemperature for each film direction of interest, using dataobtained by Procedure A.14.2 The maximum shrink tension developed for eachdirection of interest, as determined by the graphs prepare
44、d in14.1, is the orientation release stress.15. Report15.1 Report the following information:15.1.1 Complete sample identification,15.1.2 Procedure used,15.1.3 Percent shrink prior to restraint,15.1.4 Test temperature,15.1.5 Film direction (longitudinal, transverse),15.1.6 Number of specimens tested,
45、15.1.7 Average thickness of each specimen,15.1.8 Shrink force of each specimen,15.1.9 Shrink tension of each specimen,15.1.10 Average results, standard deviation, and confidencelimits where applicable, and15.1.11 Orientation release stress, film direction, and tem-perature where it occurs, plus plot
46、s used to obtain it.16. Precision and Bias16.1 RepeatabilityThe standard deviation of measure-ments of shrink force within a laboratory is usually a functionof the magnitude of the measurement between the limits of 9.8N/m (0.056 lbf/in.) and 175 N/m (1.0 lbf/in.). The standarddeviation will increase
47、 with the magnitude of the measurement.The percent coefficient of variation (s/X3 100) will generallynot exceed 10 %.16.2 ReproducibilityThe standard deviation of averagesof shrink force obtained by different laboratories is relativelyconstant for measurements between the limits of 9.8 N/m(0.056 lbf
48、/in.) and 175 N/m (1.0 lbf/in.) and generally will notexceed 5.8 N/m (0.034 lbf/in.).16.3 BiasThe bias of this test method cannot be assessedsince applicable accepted reference materials are not available.17. Keywords17.1 film; orientation release stress; shrink force; shrinktension; thin sheetingD2
49、838094SUMMARY OF CHANGESCommittee D20 has identified the location of selected changes to this standard since the last issue(D 2838 - 08) that may impact the use of this standard. (May 1, 2009)(1) Added Note 1 to define film.(2) Revised 6.8 to clarify wording regarding thickness mea-surement.Committee D20 has identified the location of selected changes to this standard since the last issue(D 2838 - 07) that may impact the use of this standard. (November 1, 2008)(1) Revised Section 10.ASTM International takes no position respecting the validity of any