1、Designation: D3434 00 (Reapproved 2018)Standard Test Method forMultiple-Cycle Accelerated Aging Test (Automatic Boil Test)for Exterior Wet Use Wood Adhesives1This standard is issued under the fixed designation D3434; the number immediately following the designation indicates the year oforiginal adop
2、tion or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers a procedure for testing thedurability of wood ad
3、hesives that may be suitable for exterior(wet use) exposure conditions. The possible use of adhesivessuitable for evaluation includes, but is not limited to those usedfor laminating large members, manufacturing plywood, orfabricating wood joints such as finger or scarf joints. Thispractice is not su
4、itable for interior type glues.2,31.2 The test does not evaluate for any biological effects.1.3 The test subjects specimens to a large number ofalternate boil/dry cycles.1.4 The values stated in SI units are to be regarded as thestandard. The inch-pound units in parentheses are provided forinformati
5、on only.1.5 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety, health, and environmental practices and deter-mine the applicability of regulatory limitations prio
6、r to use.1.6 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization TechnicalBa
7、rriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:4D906 Test Method for Strength Properties of Adhesives inPlywood Type Construction in Shear by Tension LoadingD907 Terminology of AdhesivesD2339 Test Method for Strength Properties of Adhesives inTwo-Ply Wood Construction in S
8、hear by Tension LoadingD4422 Test Method for Ash in Analysis of Petroleum CokeE122 Practice for Calculating Sample Size to Estimate, WithSpecified Precision, the Average for a Characteristic of aLot or Process3. Terminology3.1 DefinitionsDefinitions of terms in this test methodmay be found in Termin
9、ology D907.4. Summary of Test Method4.1 The lumber is selected, adhesive obtained, and testspecimens prepared.4.2 The specimens are subjected to the required number ofboil/dry cycles.4.3 The specimens are withdrawn from the test at therequired periodic intervals.4.4 The designated number of specimen
10、s are tested intensile shear at the end of the specified number of boil/drycycles.4.5 Plot shear strength, kPa (psi), or percent of wood failure,or both, versus the number of boil/dry cycles to which thespecimens have been subjected.4.6 The graph is compared for the test adhesives. Because ofthe var
11、iables occurring in wood, a known performance adhe-sive control should be run for each test set being evaluated.5. Significance and Use5.1 This test method is intended to differentiate between theexterior durability of two or more adhesives. At present, this isdone by comparing the adhesives as desc
12、ribed in 4.5 and 4.6rather than by assigning absolute numerical values for dura-bility performance.5.2 The test method as described is for comparing potentiallong-term durability rather than for use as a quality controlprocedure. This makes it suitable for research, adhesive1This test method is unde
13、r the jurisdiction of ASTM Committee D14 onAdhesives and is the direct responsibility of Subcommittee D14.30 on WoodAdhesives.Current edition approved Aug. 1, 2018. Published August 2018. Originallyapproved in 1975. Last previous edition approved in 2013 as D3434 00 (2013).DOI: 10.1520/D3434-00R18.2
14、Walser and Colbeck, “Bond-Degrade Accelerating Machine Helps PredictBond Life,” Adhesives Age, Vol 10(11), November 1967, pp. 3335.3Kreibich and Freeman, “Development and Design of an Accelerated BoilMachine,” Forest Products Journal, Vol 18, No. 12, December 1968.4For referenced ASTM standards, vis
15、it the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-29
16、59. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical
17、Barriers to Trade (TBT) Committee.1evaluation, process evaluation, and product design. A modifi-cation could be made, that is, shorten the number of cyclesused so the test method would be suitable for quality control inproduction mills. The results obtained for a particular adhesivecan be used to sh
18、ow how many cycles are required for a millquality control test of that adhesive.5.3 The test method assumes that boil/dry cycling is anadequate and useful accelerated aging technique. Evaluation oflong-term durability of adhesives in wood joints under severeservice conditions, including extended ext
19、erior exposure, is acomplex field, and no entirely reliable short-term test is knownto ensure that a new type of adhesive system will satisfactorilyresist all of the chemical, moisture, microorganism, and solventeffects that such severe service may involve. Except for effectsof microorganisms and ot
20、her similar biological influences, thistest method has proven very useful for comparison purposes todistinguish between adhesive systems of different degree ofdurability to the usual temperature, moisture, and cyclicmoisture conditions. It has proven very useful to distinguishbetween bondlines, made
21、 with adhesives of proven chemicaland biological durability, that were properly used in productionto resist the mechanical and moisture effects that such jointsmust withstand in severe service over extended periods ofexposure. It does not, in itself, assure that new types ofadhesives will always wit
22、hstand actual exterior or other severeservice.6. Apparatus6.1 Due to the large number of boil/dry cycles involved, anautomated piece of test equipment is required. A schematicdiagram of one system found suitable is shown in Fig. 1;aphotograph in Fig. 2. The equipment shown automatically boilsand dri
23、es the test specimens as required.6.2 A tensile shear tool is required such as described in TestMethod D2339.7. Test Specimens7.1 Wood Substrate:7.1.1 For Lumber Laminating AdhesivesCondition thewood at 23 6 2C (73.4 6 3.6F) and a relative humidity of 50to 70 % (preferably 65 %) until a moisture con
24、tent of 8 to 14 %(preferably 9 to 12 %) has been attained. Freshly surface bothsides of each lamination before bonding with 6.3 6 0.25-mm(0.25 6 0.01-in) thick lumber. Since adhesives join materialsby surface attachment, care must be taken to ensure a uniformreproducible surface representative of ac
25、tual construction.Typical surfaces include sawed, planed, sanded, and skived.Detailed surface preparation procedures used must be includedin the report (see 10.1).7.1.1.1 Specimen moisture content (MC) conditions calledfor in this test method should be checked in accordance withTest Methods D4422.7.
26、1.2 For Plywood AdhesivesPrepare the test specimen inaccordance with Test Method D906.7.1.3 Miscellaneous SpecimensOther wood joints, such asfinger or scarf joints, or other wood-based materials, such asparticleboard, hardboard, or insulating board, may also beevaluated.7.2 AdhesiveStore the adhesiv
27、e or its components at themanufacturers recommended conditions.7.3 Bonding Procedure:7.3.1 It has been found convenient to fabricate large two-and three-ply blocks, which are subsequently cut into a numberof test specimens. A140 by 140-mm (512 by 512-in) block willyield four specimens and one 140 by
28、 200-mm (512 by 8-in)block will yield eight specimens.FIG. 1 Automatic Boil MachineD3434 00 (2018)27.3.2 Mix and apply the adhesive(s) to the surface(s) to bebonded in accordance with the manufacturers instructions. Ifthe processes are being evaluated, prepare specimens reflectingthe limits of the t
29、ypical process conditions.7.3.3 Age the large blocks for at least 1 week at 23 6 2C(73.4 6 3.6F) and a relative humidity of 50 to 70 %(preferably 65 %) before cutting into the smaller test specimen.7.4 Test Specimen Fabrication:7.4.1 Fig. 3 shows the preferred test specimens and dimen-sions for lumb
30、er laminating adhesives. The same specimenscan be used with veneer when evaluating plywood adhesives.The two-ply specimen will be satisfactory when bondlineperformance parallel to the grain is to be evaluated; thethree-ply specimen when cross-grain bondline performance isto be evaluated.7.4.2 Cut la
31、rge blocks into test specimens as shown in Fig.3. Exercise care in grooving the specimens to ensure that thecut extends to, but not beyond, the bondline as shown in Fig.3.7.4.3 Fig. 4 shows a suitable test specimen for evaluatingfinger joints.7.4.4 Different specimen dimensions may be used for spe-c
32、ial applications but the boil/dry cycling time periods may haveto be modified to allow for complete wetting and drying.7.5 Number of Test Specimens:7.5.1 Ninety specimens are required for each adhesive,process variable, lay-up type, substrate material, etc., to beevaluated.7.5.2 Randomly divide each
33、 set of 90 specimens into ninegroups of ten each and sequentially number them for identifi-cation. (Depending upon the statistical accuracy desired, addi-tional specimens may be desired; see Practice E122).7.5.3 Include twelve additional test specimens for moisturecontent determinations during aging
34、.8. Procedure8.1 Controls:8.1.1 Dry ControlsTest ten specimens dry in tensile shear(no cycling), using the apparatus indicated in 6.2. Record theultimate shear strength and percent wood failure. The drycontrol values obtained shall be at least as high as therecommended values obtained by the adhesiv
35、e manufacturer orthe normal values for that type of adhesive, or both.8.1.2 Wet ControlsSubmerge ten specimens for 3 days in23 6 2C (73.4 6 3.6F) water. Position the specimens in sucha way that water can readily circulate around all sides of eachspecimen. Test wet in tensile shear in accordance with
36、 8.1.1.Record the results.FIG. 2 Automatic Boil MachineD3434 00 (2018)38.2 Accelerated Aging Cycles:8.2.1 Positioning of Test SpecimensPosition the test speci-mens in the automatic cycling machine in such a way that airor water can readily circulate around all sides of each speci-men.8.2.2 Cycle 1Su
37、bmerge the specimens for 10 min inboiling water.8.2.3 All Following Cycles Consist of:8.2.3.1 Dry the specimens for 4 min with 23 6 2C (73.4 63.6F) circulating air at 1.74 6 0.29 m/s (300 6 50 ft/min).8.2.3.2 Dry the specimens for 57 min with 107 6 2C (2256 6F) circulating air at 1.74 6 0.29 m/s (30
38、0 6 50 ft/min).8.2.3.3 Submerge the specimens for 10 min in boiling water.8.3 Shear Testing of Cycled Wet Specimens:8.3.1 Withdraw ten specimens from each set after exposureto 20, 40, 100, 200, 400, 800, and 1600 cycles.8.3.2 Soak the specimens to be shear tested in 23 6 2C(73.4 6 3.6F) water until
39、tested, this soak period not to exceed3 days.8.3.3 Test the wet specimens in tensile shear in accordancewith 8.1.1. Record the results.8.4 Withdraw two test specimens in the wet phase and twotest specimens in the dry phase after 20, 100, and 400 cyclesfor moisture content determinations. Weigh the t
40、est specimensimmediately or wrap them in plastic film if they cannot beweighed immediately. Moisture content may be determined byMethod A of Test Methods D4422 (see 7.1.1.1).8.5 Miscellaneous specimens described in 7.1.3 may requiremodifications in the test method and cycles used.9. Interpretation o
41、f Test Results9.1 Plot the ultimate shear strength or percent wood failure,or both, versus number of cycles including data obtained fromcontrols.9.2 Using the graphs obtained from 9.1, rank all adhesivesexamined, process variables studied, and substrates evaluated.NOTE 1All laminations made with 6.3
42、-mm (1/4 in.) lumber.FIG. 3 Test SpecimensFIG. 4 Typical Finger Joint SpecimenD3434 00 (2018)410. Report10.1 The report shall include, but not be limited to, thefollowing:10.2 Description of the materials used and preparation ofthe test specimens,10.3 Aging of bonded specimens prior to test,10.4 Ind
43、icate that tests were performed in accordance withthis test method and list deviations, and10.5 Prepare test results in graphical and tabular form.10.6 Include dry phase and wet phase moisture content dataas determined in 8.4.11. Precision and Bias11.1 Precision is made up of two parts: repeatabilit
44、y (withina laboratory) and reproducibility (between laboratories). Sinceonly one automatic boil machine exists it is not possible todetermine the reproducibility of this test method.11.1.1 The repeatability is dependent, in large part, upon theindividual test method used to determine the bond streng
45、th ofthe laminate. For example, Test Method D906 for PlywoodAdhesives, or other test methods as appropriate for the specifictest specimen or joint configuration.11.2 This test method has no measure of bias since thestrength of the laminate and wood failure are defined by thetesting methods.12. Keywo
46、rds12.1 adhesive; aging; boil test; multiple-cycle; wet; woodASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such p
47、atent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited e
48、ither for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fai
49、r hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Co