1、Designation: D4640 86 (Reapproved 2009)Standard Test Method forDetermining Stroke Cure Time of Thermosetting Phenol-Formaldehyde Resins1This standard is issued under the fixed designation D4640; the number immediately following the designation indicates the year oforiginal adoption or, in the case o
2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of the curerate at any specified temperature for a t
3、hermosetting phenol-formaldehyde resin. The time at that temperature required tomake a fluid mixture change into a hard immovable massindicates speed of cure.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI uni
4、ts that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine
5、the applica-bility of regulatory limitations prior to use.2. Terminology2.1 Definitions of Terms Specific to This Standard:2.1.1 stroke cure time, nthe time required for a resin beingheld at a specified temperature on a hot plate and being strokedwith a spatula, to adhere to the hot plate and not to
6、 the spatula.3. Summary of Test Method3.1 This test method employs the use of controlled heat anda thin layer of resin to determine the time in seconds requiredto change from a fluid stage to a cured immovable stage.4. Significance and Use4.1 This method is significant as a process control forpolyme
7、rization time.4.2 When the cure times are determined at several tempera-tures and plotted as time versus temperature, different resinscan be compared for curing characteristics.5. Apparatus5.1 Electric Hot Cure Plate, with a smooth surface free ofrough spots with adjustable control to hold the tempe
8、raturewithin 3.5F (2C) (Note 1).5.2 Spatula,3by716 in. (75 by 10 mm), stainless.5.3 Stopwatch.5.4 Knife, brass, putty with straight edge.6. Procedure6.1 Adjust the hot plate to the desired test temperature.NOTE 1Usual temperatures are 300F (150C), 320F (160C), and330F (165C).6.2 Place an approximate
9、ly 0.5-g specimen on the hot plateand spread over an approximately 2-in.2(130-mm2) area witha clean spatula as quickly as possible. Start the stopwatchimmediately upon adding the specimen to the hot plate, thenstroke steadily across the specimen in alternating smoothingand patting motions.6.3 As the
10、 resin approaches the cured stage, it becomesmore viscous and stringy. Stop the stopwatch when the resin onthe hot plate and the spatula no longer adhere to each other.Record the elapsed time.6.4 Remove cured resin from hot plate immediately with thestraight edged putty knife.NOTE 2The longer on the
11、 hot plate, the harder it is to remove.NOTE 3Test results can be affected by differences in construction ofhot plates, the stroking and patting with spatula, and the starting andstopping of the stopwatch.7. Report7.1 Report the following information:7.1.1 Stroke cure time in seconds; record to the n
12、earestwhole number.7.1.2 Test temperature.1This test method is under the jurisdiction of ASTM Committee D01 on Paintand Related Coatings, Materials, and Applications and is the direct responsibility ofSubcommittee D01.33 on Polymers and Resins.Current edition approved Dec. 1, 2009. Published Decembe
13、r 2009. Originallyapproved in 1986. Last previous edition approved in 2001 as D4640 - 86 (2001).DOI: 10.1520/D4640-86R09.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.8. Precision and Bias8.1 No statement is made about either the p
14、recision or biasof this method for measuring stroke cure since the resultmerely states whether there is conformance to the criteria forsuccess specified in the procedure.9. Keywords9.1 phenol-formaldehyde resins; stroke cure timeASTM International takes no position respecting the validity of any pat
15、ent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision
16、 at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comm
17、ents will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighte
18、d by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D4640 86 (2009)2